A production method, stainless steel technology, applied in decorative art, embossed decorative parts, etc., can solve the problems of low production efficiency, complex and cumbersome production process, high production cost, etc., and achieve the effect of reducing the rollable thickness

Inactive Publication Date: 2011-12-21
杨元恒
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The production process of the above method is complex and cumbersome, the production environment is relatively harsh, the production cost is high, and the production efficiency is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of production method of stainless steel pattern welded pipe
  • A kind of production method of stainless steel pattern welded pipe
  • A kind of production method of stainless steel pattern welded pipe

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] ginseng is figure 1 , figure 2 , image 3 As shown, a kind of production method step of stainless steel pattern welded pipe is like this:

[0026] (1) heating the stainless steel strip 3 with a rectangular intermediate frequency induction heating coil 2, the heating temperature is 1000-1200°C;

[0027] (2) The heated stainless steel strip 3 is continuously produced intermittently by a three-roll asynchronous hot-rolling mill 1, and the upper roll 1-3 of the three-roll asynchronous hot-rolling mill 1 is an active carving roll. The middle roll 1-5 is a passive smooth working roll, the lower roll 1-6 is an active smooth support roll, and the outer diameter ratio of the upper roll 1-3, middle roll 1-5, and lower roll 1-6 is 1:0.2- 0.4∶0.8-1, the speed ratio of upper roller 1-3 and lower roller 1-6 is 1∶0.9-0.6, the depth of engraving is 0.2-2.7mm, and the width left on both sides of the stainless steel belt 3 is 0.8-1.2mm the welding area;

[0028] (3) The rectangular...

Embodiment 2

[0034] see Figure 4 , Figure 5 As shown, this example is a stainless steel welded pipe with zigzag embossing on the inner surface 3-2, the cross section of the inner wall of the pipe is zigzag grooved 3-2-1, the outer diameter of the engraving roller 1-3 is φ170mm, and the middle roller 1-5 The outer diameter of the lower roller 1-6 is φ42mm, the outer diameter of the lower roller 1-6 is φ170mm, the width is 21.2mm, the thickness of the stainless steel belt 3 is 0.7mm, the depth of the groove 3-2-1 is 0.3mm, the distance between adjacent grooves is 0.36mm, and the tooth top is wide is 0.22mm, tooth bottom width is 0.268mm, tooth tip angle is 9°, the included angle between flute 3-2-1 and steel strip longitudinal angle is 25°, zigzag flute 3-2-1 is in addition to stainless steel welded pipe Outside the weld area, all are filled. Leave 1 mm on both sides of the weld without rolling, and the outer wall of the welded pipe is smooth. The speed ratio of upper and lower rolls 1-...

Embodiment 3

[0036] see Figure 6 As shown, this example is a T-shaped embossed stainless steel welded pipe 3-3 on the outer surface, the surface of the welded pipe is covered with T-shaped embossed lines 3-3-1, and multiple rows of T-shaped embossed lines 3-3-1 are arranged one by one along one direction. The height of the outer embossment is 0.4mm, the thickness of the stainless steel strip is 0.8mm, the outer diameter of the upper roll 1-3 is φ170mm, the outer diameter of the middle roll 1-5 is φ34mm, the outer diameter of the lower roll 1-6 is φ152mm, both sides of the weld Leave 1.2mm unrolled on each edge, and roll T-shaped reliefs 3-3-1 on the rest. The inner wall of the welded pipe is smooth. The rotational speed ratio of upper roll 1-3 and lower roll 1-6 is 1: 0.8. Its groove rolling method is as described in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production method of a stainless steel patterned welded pipe, which can roll out patterns with clear lines on the surface of the stainless steel welded pipe, and has high production efficiency. The production method steps of the stainless steel pattern welded pipe are as follows: Under the protection of hydrogen and nitrogen mixed gas, the stainless steel strip is heated by a medium frequency heating coil, and the continuous production is carried out by a three-roll asynchronous engraved hot rolling mill; the upper roll of the rolling mill is the active one. Engraving roller. The middle roll is a passive smooth work roll, and the bottom roll is an active smooth support roll. The depth of the engraving is 0.2-2.7mm. The rotation speed ratio of the lower roll is 1:0.6-0.9; the single-sided engraved stainless steel strip coming out of the rolling mill is rolled into a cylinder by cooling and roughly forming horizontal rolls, and then welded into a round pipe by a stainless steel welded pipe machine. The horizontal rollers of the horizontal roller set are made of MC nylon or rubber materials.

Description

technical field [0001] The invention relates to the technical field of production of stainless steel welded pipes, in particular to a production method of stainless steel patterned welded pipes. technical background [0002] At present, the stainless steel patterned pipes sold on the market are printed on the outer surface of the welded stainless steel pipe by screen printing, after drying, immersed in a chemical corrosion solution, and through a chemical reaction, the surface metal part protected by the paint-free protective layer is corroded. Thereby forming various preset three-dimensional patterns on the surface of the stainless steel pipe. The corrosion depth is about 0.1-0.4mm. The production process of the above method is complex and cumbersome, the production environment is relatively harsh, the production cost is high, and the production efficiency is low. Contents of the invention [0003] The purpose of the present invention is to provide a production method o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21C37/08B44B5/00
Inventor 杨元恒
Owner 杨元恒
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap