A protective coating, polyvinyl chloride technology, applied in the field of polymers, can solve the problems of volatile substrate compatibility, low light stabilization efficiency, poor extraction resistance, etc., to achieve easier control of the copolymerization reaction, excellent UV The effect of photoprotective properties, high UV resistance

Active Publication Date: 2012-07-18
SICHUAN UNIV +2
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a photoprotective coating material and preparation method with strong operability, low preparation cost, non-toxic environmental protection, and excellent comprehensive performance. The material has high toxicity, easy migration, poor extraction resistance, easy volatilization, poor compatibility with the substrate, weak adhesion, low light stability efficiency, and high production cost, which greatly improves the anti-ultraviolet aging performance of the product. Reduce use cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Single-component water-based UV protection coating material for polyvinyl chloride and preparation method thereof
  • Single-component water-based UV protection coating material for polyvinyl chloride and preparation method thereof
  • Single-component water-based UV protection coating material for polyvinyl chloride and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] (1) The raw material composition formula of one-component environmental protection water-based UV protective coating material is as follows: special functional additive: 0.3 parts, ethyl acrylate: 16 parts, butyl acrylate: 11 parts, methyl methacrylate: 53 parts parts, acrylonitrile: 20 parts, acrylic acid: 1 part, emulsifier OP-10: 3 parts, initiator ammonium persulfate: 0.5 parts, deionized water: 100 parts. Put the above-mentioned other formula raw material components except the initiator ammonium persulfate and 50 parts of deionized water into the emulsification tank, and emulsify at a speed of 800 rpm for about 2 hours to obtain the emulsified monomer, and the remaining 50 parts Add one part of deionized water into the reactor and heat up to about 60°C, then add emulsified monomer and initiator in parallel flow, react at a temperature of about 80°C for about 4 hours, keep warm for about 1 hour after fully reacting, and cool to the room At room temperature, after mo...

Embodiment 2

[0041] (1) The raw material composition formula of one-component environmental protection water-based UV protective coating material is as follows: special functional additive: 0.8 parts, ethyl acrylate: 27 parts, butyl acrylate: 28 parts, methyl methacrylate: 25 parts Parts, acrylonitrile: 30 parts, acrylic acid: 1 part, sodium lauryl sulfate 60% and OS 40% mixture emulsifier: 3 parts, potassium persulfate initiator: 0.5 parts, deionized water: 100 parts. Put the above-mentioned other formula raw material components except the initiator potassium persulfate and 40 parts of deionized water into the emulsification tank, emulsify at a high speed of 2000 rpm for about 0.5 hour to obtain the emulsified monomer, and the remaining 60 parts Add a portion of deionized water to the reactor and heat it up to about 100°C, then add emulsified monomer and initiator in a parallel flow, react at a temperature of about 85°C for about 0.6 hours, and keep warm for about 0.6 hours after fully rea...

Embodiment 3

[0044] (1) The raw material composition formula of one-component environmental protection water-based UV protective coating material is: special functional additive: 0.5 parts, ethyl acrylate: 34 parts, butyl acrylate: 13 parts, methyl methacrylate: 35 parts Parts, acrylonitrile: 10 parts, acrylic acid: 3 parts, dioctyl sulfosuccinate sodium salt and OP mixed emulsifier: 4 parts, azobisisobutyronitrile initiator: 1 part, deionized water: 100 parts. Put the above-mentioned other formula raw material components except the initiator azobisisobutyronitrile and 60 parts of deionized water into the emulsification tank, and emulsify at a speed of 1000 rpm for about 1.5 hours to obtain the emulsified monomer, and the remaining Part of 40 parts of deionized water is added to the reactor and the temperature is raised to about 80°C, then the emulsifying monomer and initiator are added in a parallel flow, and the reaction is carried out at a temperature of about 80°C for about 0.8 hours, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a single-component water-based UV protection coating material for polyvinyl chloride and a preparation method thereof. The single-component water-based UV protection coating material is special functional assistant-containing aqueous emulsion of an acrylic ester copolymer. When used, the aqueous emulsion is sprayed on the surface of a polyvinyl chloride product; and after the aqueous emulsion is solidified, the uniform photoprotection coating material is formed. Results of experiments show that the polyvinyl chloride product of the single-component environmental-friendly water-based UV protection coating material provided by the invention has obviously improved UV stability, greatly improved mechanical property long-term conservation rate and obviously improved appearance color stability.

Description

technical field [0001] The invention relates to the technical field of polymers, more specifically to an ultraviolet light protective coating material for polyvinyl chloride, and a preparation method for the ultraviolet light protective coating material. technical background [0002] In the field of chemical building materials in my country, the amount of polyvinyl chloride has always ranked first. However, when used outdoors, under the influence of ultraviolet light as the main cause, PVC molecules will undergo a series of physical and chemical changes, which will lead to performance degradation such as hardening, brittleness, discoloration, and pulverization of the product. eventually loses its use value. Therefore, the poor UV resistance of polyvinyl chloride has become one of the main obstacles restricting its healthy development. [0003] The most commonly used method to improve the light resistance of polyvinyl chloride is to add a certain amount of organic ultraviol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C09D133/12C09D133/20C09D133/08C09D7/12
Inventor皮红叶先科郭少云张军蒋文君王廷举
OwnerSICHUAN UNIV