Metal complexing material and preparation method thereof, and application of metal complexing material to cigarettes

A metal complexing, cigarette technology, applied in the application, tobacco, smoke oil filter and other directions, can solve problems such as discomfort, achieve the effects of high safety, improve selective adsorption performance, and simple preparation process

Active Publication Date: 2011-04-13
ZHENGZHOU TOBACCO RES INST OF CNTC
View PDF6 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, activated carbon is used as an additive for cigarette tip rods. While effectively filtering the gas phase components of the smoke, the carbon smell it brings to the smoke makes smokers feel uncomfortable.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal complexing material and preparation method thereof, and application of metal complexing material to cigarettes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The strongly acidic cation exchange resin 001*7 is packed in absolute ethanol first, soaked for 2 hours and then rinsed with absolute ethanol to remove impurities. Double the bed volume of water, 2 times the bed volume of 4% hydrochloric acid solution, 10-12 bed volumes of water treatment resin, wash with water until neutral, and then use 5-10 times the bed volume of 0.8M CuSO 4 , Fe 2 (SO 4 ) 3 , Ni(NO 3 ) 2 The resin was treated with an aqueous solution, washed with water until no metal ions flowed out, filtered, and vacuum-dried at 50°C for 30 minutes to obtain a series of metal complex materials exchanged with 001*7.

[0021] The above materials are applied to cigarettes in the form of binary composite filter rods, with an additive amount of 30mg / cig (sticks), marked as cigarette sample 2, and cigarettes without any filter modification materials added as control samples, the cigarettes used before the test Equilibrate for 48 hours under the conditions of temper...

Embodiment 2

[0026] The macroporous strongly acidic macroporous adsorption resin D072 is first packed with ethanol, soaked for 2 hours and then rinsed with ethanol to remove impurities, and then washed with 2 times the bed volume of 4% sodium hydroxide solution, 5-6 times the bed volume water, 2 times the bed volume of 4% hydrochloric acid solution, 10-12 bed volumes of water treatment resin, washed with water to neutrality, and then used 5-10 times the bed volume of 0.1M CuSO 4 , ZnSO 4 , MnSO 4、 Treat the resin with an aqueous solution, wash it with water until no metal ions flow out, and dry it in vacuum at 50°C for 30 minutes to obtain a series of metal complex materials exchanged with D072.

[0027] Apply the above-mentioned materials to cigarettes in the form of binary composite filter rods, the addition amount is 30 mg / cig (sticks), and the cigarettes without any filter modification materials are used as control samples. )°C and relative humidity (60±2)% for 48 hours, and then sor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a metal complexing material and a preparation method thereof, and application of the metal complexing material to cigarettes. The invention is characterized in that: the complexing material is obtained by complexing a porous carrier with large specific surface area, such as ion exchange resin, ion exchange fibers, macroporous adsorption resin and the like, and different metal ions, and is applied to the cigarettes in a form of a binary composite filter stick; 10 to 40mg of complexing material is added into each cigarette, so that hydrogen cyanide (HCN) in mainstream smoke can be selectively reduced by over 25 percent; meanwhile, the complexing material does not have negative effects on the sensory quality of the cigarettes. The porous carrier in the material has large specific surface area, so smoke can be effectively contacted with the functional group of the material when passing through the material; meanwhile, the metal ions on the surface can be subjectedto complexing reaction with the HCN, so that the HCN in the smoke of the cigarettes is selectively removed.

Description

technical field [0001] The invention relates to a metal complex material for selectively reducing HCN in mainstream smoke of cigarettes, a preparation method thereof and application in cigarettes. Applying the material to cigarette filter rods can effectively reduce the release of hydrocyanic acid in mainstream smoke without negatively affecting the sensory quality of cigarettes. Background technique [0002] Hydrocyanic acid (HCN) is a highly volatile and highly toxic substance, and the poisoning effect is mainly through CN - occur. Hydrocyanic acid in cigarettes mainly comes from the oxidative decomposition of nitrates and nitrogen-containing compounds in tobacco during the burning and smoking process, and its release amount is about 30-300??g / cig. Quickly enter the body and cause harm to human health. Therefore, the development of materials that can effectively reduce the release of hydrocyanic acid in mainstream cigarette smoke is of great significance for improving t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A24D3/12
Inventor 聂聪孙学辉王宜鹏杨松赵乐彭斌刘惠民谢剑平
Owner ZHENGZHOU TOBACCO RES INST OF CNTC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com