Environment-friendly textile printing pearlescent adhesive cement and preparation method and application thereof

An environmentally friendly printing technology, applied in the field of printing, to achieve the effect of broadening the printing range and inhibiting bacteria

Inactive Publication Date: 2011-09-07
SUZHOU UNIV
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the coloring principle and particle size of pearlescent powder are completely different from those of pigments, dyes, and titanium dioxide used as fillers for conventional mortars, so far pure pearlescent powders are used without adding any fillers and are compatible with environmentally friendly adhesives. The prepared environmentally friendly pearlescent glue for textile printing has never been seen in the printing industry at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly textile printing pearlescent adhesive cement and preparation method and application thereof
  • Environment-friendly textile printing pearlescent adhesive cement and preparation method and application thereof
  • Environment-friendly textile printing pearlescent adhesive cement and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1 Manual platen pearlescent glue printing process:

[0030]The formula of the environment-friendly type textile printing pearlescent glue that the present embodiment adopts:

[0031]

[0032] After adjusting the pH value of the environment-friendly adhesive, pour anatase silver-white pearl powder, rutile silver-white pearl powder, ethylene glycol, dispersant, leveling agent, anti-mold and antibacterial additives, and nano-anion far-infrared powder into the adjusted In the adhesive with a good pH value, first stir at a low speed of 1400 rpm for 5 minutes, with a gap of 5 minutes, then add the thickener while stirring at a high speed of 2850 rpm, stop adding the thickener when the required consistency is reached, and continue to high speed After stirring at 2850 rpm for 8 / min, it was confirmed that the surface of the slurry was bright and delicate, and the finished glue of this embodiment was obtained.

[0033] The printed fabric based on 14656 plain crepe ...

Embodiment 2

[0034] Embodiment 2 Synchronous printing process of hand-made plate pearlescent glue and acid dyes

[0035] The formula of the environment-friendly type textile printing pearlescent glue that the present embodiment adopts:

[0036]

[0037] After adjusting the pH value of the environment-friendly adhesive, pour anatase silver-white pearl powder, rutile silver-white pearl powder, ethylene glycol, dispersant, leveling agent, anti-mold and antibacterial additives, and nano-anion far-infrared powder into the adjusted In the adhesive with a good pH value, first stir at a low speed of 1400 rpm for 5 minutes, with a gap of 5 minutes, then add the thickener while stirring at a high speed of 2850 rpm, stop adding the thickener when the required consistency is reached, and continue to high speed After stirring at 2850 rpm for 8 / min, it was confirmed that the surface of the slurry was bright and delicate, and the finished glue of this embodiment was obtained.

[0038] Printing fabric...

Embodiment 3

[0039] Example 3 Machine printing flat screen pearl glue and disperse dye synchronous printing process circuit

[0040] The formula of the environment-friendly type textile printing pearlescent glue that the present embodiment adopts:

[0041]

[0042] After adjusting the pH value of the environment-friendly adhesive, pour anatase silver-white pearl powder, rutile silver-white pearl powder, ethylene glycol, dispersant, leveling agent, anti-mold and antibacterial additives, and nano-anion far-infrared powder into the adjusted In the adhesive with a good pH value, first stir at a low speed of 1400 rpm for 5 minutes, with a gap of 5 minutes, then add the thickener while stirring at a high speed of 2850 rpm, stop adding the thickener when the required consistency is reached, and continue to high speed After stirring at 2850 rpm for 8 / min, it was confirmed that the surface of the slurry was bright and delicate, and the finished glue of this embodiment was obtained.

[0043] The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly textile printing pearlescent adhesive cement and a preparation method and application thereof. The adhesive cement comprises the following components in percentage by weight: 49 to 39 percent of environment-friendly ultra-soft adhesive, 15 to 25 percent of rutile silvery white pearlescent powder in the particle size range of between 5 and 25 microns, 15 to 25 percent of anatase silvery white pearlescent powder in the particle size range of between 10 and 60 microns, 4 to 6 percent of glycol, 1 to 2 percent of dispersing agent, 1 to 3 percent of leveling agent, 1 to 2 percent of mould-proof antibacterial auxiliary agent, 2 to 4 percent of nano negative ion far-infrared powder and 2 to 4 percent of thickening agent. The adhesive cement cannot block a screen during screen printing, has high weather resistance and has the obvious advantages of environment friendliness, no toxic hazard, high-temperature resistance, acid-base resistance, incapability of spontaneous combustion and combustion supporting, high oxidation resistance, high covering power and the like which are obviously distinguished from those of the common dye and pigment.

Description

technical field [0001] The invention belongs to the technical field of printing, and in particular relates to an environment-friendly pearlescent glue for textile printing and its preparation method and application. Background technique [0002] Mucilage can be divided into ordinary mucilage and special mucilage according to the application. Ordinary glue is only used for general printing, and does not require special effects. It itself can generally be divided into transparent paste, white glue, color printing paste and varnish paste. The transparent paste printed on the fabric itself is transparent and has no covering power. It is only suitable for printing on light-colored fabrics. The advantage is that due to its high resin content, its firmness is better than that of white glue. It can be mixed with white glue. Improving the firmness can also increase the gloss and elasticity, but the hiding power is poor; while the white glue itself is white and can be used for white...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/44D06P1/52D06P1/673
Inventor 丁志平苗海青
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com