12Cr2Mo1R steel plate for ultra-thick hydrogen-contacting equipment and production method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A hydrogen-facing equipment and production method technology, applied in the field of steel, can solve the problems of long production cycle, difficult production, waste of production cost, etc., and achieve the effect of large margin and uniform impact performance
Active Publication Date: 2013-03-06
NANYANG HANYE SPECIAL STEEL CO LTD
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] In the production of Cr-Mo steel, due to its high strength and hardness, special requirements for process equipment, etc., the production is difficult. Especially, when the production thickness is more than 100mm, the blanking method is often used to form the material, the production cycle is long, and the production Serious waste of cost
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0017] The extra-thickness of the present invention is 100mm-150mm and the performance and flaw detection hydrogen steel 12Cr2Mo1R steel plate contains the following chemical composition in weight percentage (unit, wt%): C: 0.08-0.15, Si: 0.20-0.50, Mn: 0.30 ~0.60, P: ≤0.018, S: ≤0.005, Als: ≤0.020~0.050, Cr: 2.0~2.5, Mo: 0.90~1.10, others are Fe and residual elements.
[0018] The production method adopted in the present invention includes: converter smelting, LF refining, vacuum refining, pouring, heating, rolling, controlled cooling, slow cooling and heat treatment. In the converter smelting, ensure that the tapping carbon is ≥ 0.05%, the tapping P is ≤ 0.015%, and the tapping temperature is ≥ 1650°C; the number of spot blowing should not exceed 2 times to avoid slag during the tapping process; in the LF refining , use a large amount of slag to make slag, and ensure that the white slag retention time is controlled at more than 15min; in the vacuum refining, the holding time...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
elongation
aaaaa
aaaaa
elongation
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a 12Cr2Mo1R steel plate for ultra-thick hydrogen-contacting equipment and a production method thereof. The 12Cr2Mo1R steel plate comprises the following chemical components, by mass, 0.08-0.15% of C, 0.20-0.50% of Si, 0.30-0.60% of Mn, equal to or less than 0.018% of P, equal to or less than 0.005% of S, equal to or less than 0.020-0.050% of AlS, 2.0-2.5% of Cr, 0.90-1.10% of Mo, and the balance Fe and residual elements. The production method comprises steps of converter smelting, LF refining, vacuum refining, casting, heating, rolling, controlled cooling, slow cooling, and heat processing. A whole production process from molten iron pretreatment to steel plate heat treatment is executed in strict accordance with above technology, so the object quality performance margin of products is large, wherein the yield margin is 40-80Mpa, the tensile margin is 55-70Mpa, and the elongation margin is 6-9%, thereby the impact performance is uniform and the margin is large.
Description
technical field [0001] The invention relates to steel materials, in particular to an extra-thick 12Cr2Mo1R steel plate for hydrogen-facing equipment and a production method. technical background [0002] In the production of Cr-Mo steel, due to its high strength and hardness, special requirements for process equipment, etc., the production is difficult. In particular, when the production thickness is more than 100mm, the blanking method is often used to form the material, the production cycle is long, and the production The waste of cost is serious. Contents of the invention [0003] The object of the present invention is to provide a 12Cr2Mo1R steel plate for hydrogen equipment with a thickness of 100 mm to 150 m in thickness of 100 mm to 150 m to ensure performance and flaw detection, and a production method thereof. [0004] A hydrogen-facing steel plate 12Cr2Mo1R steel plate, the chemical composition and mass percentage (unit, wt%) are as follows: C: 0.08-0.15, Si: 0....
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.