Preparation method of solvent type tert-butyl peroxyneo-caprate (BNP)

A new technology of tert-butyl caprate and peroxide, which is applied in the preparation of peroxy compounds, the preparation of organic compounds, chemical instruments and methods, etc. Low problems, to achieve stable product quality and high activity, improve product content and yield, and overcome the effects of low activity

Active Publication Date: 2012-05-09
LINZIZHENGHUA ACCESSORY INGREDIENT ZIBO
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, azo initiators have insurmountable disadvantages such as low activity and high toxicity, which affect the quality of high polymers such as polyvinyl chloride products, and the toxic substances in the production process are seriously harmful to the human body.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment one: the preparation steps of solvent type tert-butyl peroxyneodecanoate (BNP) are as follows:

[0013] (1) In a 500ml flask, add 22.5 grams of sodium hydroxide with a mass content of 90%, 40 grams of water, stir and cool to 5°C, and make a sodium hydroxide alkaline solution with a concentration of about 32%;

[0014] (2) 28 grams of tert-butyl hydroperoxide with a purity of 70.5% were added dropwise to the solution prepared in step (1), reacted for 30 minutes, and the temperature was controlled at 25° C.;

[0015] (3) Slowly add 50 grams of 80% octadecanoyl chloride solution in the flask after stirring evenly, the reaction temperature is controlled at 25°C to 30°C, and the addition is completed within 1.5 hours to 2 hours. Stir the reaction for 60 minutes;

[0016] (4) Stop stirring after the reaction is over, let it stand, separate the reaction mother liquor, and wash the reaction product with water until the pH value is 5 to 7;

[0017] (5) The obtained ...

Embodiment 2

[0019] Embodiment two: the preparation steps of solvent type tert-butyl peroxyneodecanoate (BNP) are as follows:

[0020] (1) In a 500ml flask, add 22.5 grams of sodium hydroxide with a mass content of 90%, 40 grams of water, stir and cool to 5°C, and make a sodium hydroxide alkaline solution with a concentration of about 32%;

[0021] (2) 28 grams of tert-butyl hydroperoxide with a purity of 70.5% were added dropwise to the solution prepared in step (1), reacted for 30 minutes, and the temperature was controlled at 25° C.;

[0022] (3) Slowly add 50 grams of 80% octadecanoyl chloride solution in the flask after stirring evenly, the reaction temperature is controlled at 25°C to 35°C, and the addition is completed within 1.5 hours to 2 hours. After adding the octadecanoyl chloride solution Stir the reaction for 60 minutes;

[0023] (4) Stop stirring after the reaction is over, let it stand, separate the reaction mother liquor, and wash the reaction product with water until the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of an initiator for synthesizing a high polymer, in particular to a preparation method of solvent type tert-butyl peroxyneo-caprate (BNP). According to the technical scheme of the invention, the preparation method of the solvent type BNP comprises the following steps of: mixing octyl decanoyl chloride with an alkaline solution and tert-butyl hydrogen peroxide, stirring and reacting at the temperature of 10-40 DEG C; separating a mother liquor; and washing a reaction product to the neutral state and adding an alkane solvent to obtain the solvent type BNP. Due to the adoption of the method for preparing the solvent type BNP provided by the invention, the process flow is simplified, the complex requirements on reaction equipment are eliminated, a reaction is undergone in the mild and safe environment, the product content and yield are increased greatly, and the yield can be over 95 percent.

Description

technical field [0001] The invention relates to a preparation method of an initiator for high polymer synthesis, in particular to a preparation method of solvent-based tert-butyl peroxyneodecanoate (BNP). Background technique [0002] With the rapid development of the domestic polymer synthesis industry, the quality and demand of initiators for polymer synthesis have increased rapidly. As we all know, azo initiators, such as azobisisobutyronitrile and azobisisoheptanonitrile (ABVN), have long been used as initiators for the synthesis of high polymers such as polyvinyl chloride. However, azo initiators have insurmountable shortcomings such as low activity and high toxicity, which affect the quality of high polymers such as polyvinyl chloride products, and the toxic substances in the production process are seriously poisonous to the human body. [0003] Solvent-type tert-butyl peroxyneodecanoate (BNP), as a high-efficiency initiator for polymer synthesis, compared with common...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C07C409/38C07C407/00
Inventor 侯永正翟少华倪啟化许淑女
Owner LINZIZHENGHUA ACCESSORY INGREDIENT ZIBO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap