Multifunctional rare earth metal-organic framework and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A rare earth metal, organic framework technology, applied in organic chemistry, non-metallic elements, chemical instruments and methods, etc., to achieve the effect of high adsorption enthalpy
Inactive Publication Date: 2012-10-31
NANKAI UNIV
View PDF1 Cites 50 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, MOFs materials that can recognize harmful solvents su
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0020] A method for preparing a multifunctional rare earth metal-organic framework, using europium nitrate hexahydrate as the metal salt, and using H 2 FDA is used as a ligand, and DMF is used as a solvent. The synthesis steps are as follows:
[0021] 1) 44.6mg of Eu(NO 3 ) 3 ·6H 2 O and 31.2 mg of H 2 Put FDA's into the polytetrafluoroethylene liner of the hydrothermal reactor and mix, then add 2mL of DMF solvent, and stir for 2min at room temperature;
[0022] 2) Put the reaction kettle with the above mixed solution in an oven, bake at 120°C for 21 hours, and separate the solid after taking out the product;
[0023] 3) The above solid was washed 3 to 5 times with DMF to obtain light yellow strip crystals of the metal framework material of europium or terbium ions, and the yield calculated based on metal Eu was 63%.
Embodiment 2
[0025] A method for preparing a multifunctional rare earth metal-organic framework, using terbium nitrate hexahydrate as the metal salt, and using H 2 FDA is used as a ligand, and DMF is used as a solvent. The synthesis steps are as follows:
[0026] 1) Add 45.3mg of Tb(NO 3 ) 3 ·6H 2 O and 31.2 mg of H 2 Put FDA's into the polytetrafluoroethylene liner of the hydrothermal reactor and mix, then add 2mL of DMF solvent, and stir for 2min at room temperature;
[0027] 2) Put the reaction kettle with the above mixed solution in an oven, bake at 120°C for 21 hours, and separate the solid after taking out the product;
[0028] 3) The above solid was washed 3 to 5 times with DMF to obtain light yellow strip crystals of the metal framework material of europium or terbium ions, and the yield calculated based on metal Tb was 66%.
[0029] Characterization of the multifunctional metal-organic framework material structure:
[0030] 1) Structural determination of the metal-organic fram...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a multifunctional rare earth metal-organic framework of which the chemical formula is {[Ln(FDA)1.5(DMF)].DMF}n, wherein Ln is Eu or Tb, the FDA is furyl-2,5-dicarboxylic acid, and the DMF is N,N-dimethylformamide; and the rare earth metal framework structure has an Eu<3+>/Tb<3+> ion in a coordination environment, and forms a three-dimensional framework structure containing one-dimensional honeycomb channels. The preparation method comprises the following steps: by using europium nitrate hexahydrate or terbium nitrate hexahydrate as a metal salt, H2FDA as a ligand and DMF as a solvent, stirring the mixed solution, baking, separating and washing the solid to obtain the multifunctional rare earth metal-organic framework. The multifunctional rare earth metal-organic framework provided by the invention has an fluorescent identification function on cancerigenic organic solvents, such as methylbenzene, benzene and acetone, has excellent selective adsorptivity for gas and high acting force with H2, contains high adsorptive enthalpy, and thus, is a multifunctional novel-structure microporous MOF (metal-organic framework) material.
Description
【Technical field】 [0001] The invention relates to a fluorescent probe, a gas adsorption and separation dual-functional material, in particular to a multifunctional rare earth metal-organic framework and a preparation method thereof. 【Background technique】 [0002] Metal-Organic Frameworks (MOFs) are porous crystalline materials formed by coordination bonds between metal ions or clusters and organic ligands. Aspects such as gas adsorption and separation, catalysis, photoelectric and magnetic materials, and sensors have attractive application potentials, and are rapidly developing into research hotspots in the interdisciplinary fields of energy, materials, and life sciences. (See: Yaghi OM et al., Nature, 1995, 378, 703; Zhou HC et al., Chem. Soc. Rev., 2009, 38, 1477). [0003] For a long time, compared with the main group metal and transition metal MOFs, the research on rare earth MOFs is still relatively small. This may be due to the high coordination numbers and flexible...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more