Polypropylene fiber dry-mixed mortar for construction of outer wall
A technology of polypropylene fiber and dry powder mortar, which is applied in the field of building materials for exterior wall construction, to achieve the effects of reducing window seam leakage, easy dusting, and easy operation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0025] Example 1. Polypropylene fiber dry powder mortar for exterior wall construction. Mix 1 part of ordinary Portland cement with strength grade of 32.5, 5.31 parts of fine sand, 0.61 parts of secondary fly ash, 0.21 parts of thickening powder and 1.33 parts of water. Dry powder mortar: Add 0.9Kg of polypropylene fiber per cubic meter of dry powder mortar, and stir for 3 minutes with a mixer to form the polypropylene fiber dry powder mortar for exterior wall construction of the present invention.
Example Embodiment
[0026] Example 2. Polypropylene fiber dry mortar for exterior wall construction. Mix 0.8 parts of ordinary Portland cement with strength grade of 32.5, 5 parts of fine sand, 0.4 parts of secondary fly ash, 0.1 part of thickening powder and 1 part of water. Dry powder mortar: 0.8Kg of polypropylene fiber is mixed into each cubic meter of dry powder mortar, and stirred with a mixer for 2 minutes to form the polypropylene fiber dry powder mortar for exterior wall construction of the present invention.
Example Embodiment
[0027] Example 3. Polypropylene fiber dry powder mortar for exterior wall construction. Mix 1.2 parts of ordinary Portland cement with a strength grade of 32.5, 6 parts of fine sand, 0.8 parts of secondary fly ash, 0.3 parts of thickening powder and 1 part of water. Dry powder mortar: 1Kg polypropylene fiber is mixed into each cubic meter of dry powder mortar and stirred with a mixer for 4 minutes to form the polypropylene fiber dry powder mortar for exterior wall construction of the present invention.
[0028] The polypropylene fiber in the above embodiment is a high-strength polypropylene bundled monofilament fiber processed with 100% PP raw glue.
[0029] The physical parameters of the polypropylene fiber used in the present invention are shown in Table 1.
[0030] Table 1:
[0031] Material Polypropylene fibers proportion 0.91kg / m3 Exterior White monofilament Melting point160-175℃ Burning point ≥580℃ Acid and alkali resistance Extremely strong tensile strength ≥633Mpa...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap