Portland cement refractory mortar and construction technology thereof

A technology of Portland cement and refractory mortar, which is applied in the processing of building materials, construction, building structure, etc., can solve problems such as hidden dangers of quality and safety, and achieve the effect of optimizing material performance, ensuring strength and low cost

Active Publication Date: 2013-02-13
CHINA NAT PETROLEUM CORP CHUANQING DRILLING ENG CO LTD
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] In summary, directly using refractory mud to install refractory bricks for load-bearing structures will cause serious quality and safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Portland cement refractory mortar and construction technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A Portland cement refractory mortar, comprising the following components in mass percentage: Portland cement 16%, powdery refractory mud 15%, silica micropowder 5%, quartz sand 30%, river sand 50%, and the balance is water .

[0039] The present invention also includes an early-strength water reducer with a mass percentage of 2%. The early strength water reducer is sodium tripolyphosphate water reducer. The maximum particle size of the quartz sand is less than 4mm. The river sand is continuously graded fine sand with a specification of 0.5 mm.

[0040] A construction technique for Portland cement refractory mortar, comprising the steps of:

[0041] (1) Batching: batching raw materials according to mass percentage;

[0042] (2), mix the raw materials in step (1) according to the proportion and stir evenly;

[0043] (3) Use the refractory mortar obtained in step (2) to build refractory bricks within 4 hours after the mixing is completed;

[0044] (4) After masonry, it...

Embodiment 2

[0046] A Portland cement refractory mortar, comprising the following components in mass percentage: Portland cement 12%, powdery refractory mud 10%, silica micropowder 5%, quartz sand 20%, river sand 30%, and the balance is water.

[0047] The present invention also includes an early-strength water reducer with a mass percentage of 0.5%. The early-strength water-reducer is an early-strength water-reducer calcium chloride, and the early-strength water-reducer is not limited to the two described ones, and other early-strength water-reducers in the prior art can also be used. The maximum particle size of the quartz sand is less than 4mm. The river sand is continuously graded fine sand with a specification of 1 mm.

[0048] A construction technique for Portland cement refractory mortar, comprising the steps of:

[0049] (1) Batching: batching raw materials according to mass percentage;

[0050] (2), mix the raw materials in step (1) according to the proportion and stir evenly; ...

Embodiment 3

[0054] A Portland cement refractory mortar, comprising the following components in mass percentage: Portland cement 14%, powdery refractory mud 12%, silica micropowder 5%, quartz sand 25%, river sand 40%, and the balance is water .

[0055] The present invention also includes an early-strength water reducer with a mass percentage of 1.5%. The early strength water reducer is sodium tripolyphosphate. The maximum particle size of the quartz sand is less than 4mm. The river sand is continuously graded fine sand with a specification of 0.8 mm.

[0056] A construction technique for Portland cement refractory mortar, comprising the steps of:

[0057] (1) Batching: batching raw materials according to mass percentage;

[0058] (2), mix the raw materials in step (1) according to the proportion and stir evenly;

[0059] (3) Use the refractory mortar obtained in step (2) to build refractory bricks within 4 hours after the mixing is completed;

[0060] (4) After masonry, it is natura...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a portland cement refractory mortar and a construction technology thereof. The portland cement refractory mortar comprises the following components in percentage by weight: 12-16% of portland cement, 10-15% of powdery refractory mortar, 5% of silica powder, 20-30% of quartz sand, 30-50% of river sand and the balance of water. The refractory mortar has high early strength, can resist high calcination temperature, has high adhesive property and strength after the calcination and is used for solving the safety problem during the current construction process; and moreover, the cost is lower than that of the conventional refractory castable.

Description

technical field [0001] The invention relates to a refractory mortar and a construction process thereof, in particular to a Portland cement refractory mortar and a construction process thereof, which are used for building refractory bricks. Background technique [0002] The refractory technology of the existing technology is relatively mature, and the micro-powder technology and low-cement technology have been successfully applied to refractory castables, so that the cast refractory structures can work in very harsh high-temperature environments. However, the cost of using refractory castables is often very high. In some working environments that do not have strict requirements on high-temperature environments, using refractory castables for structures will undoubtedly cause waste of functions and increase costs. [0003] At present, some structures that work in the environment of 500 ° C to 1200 ° C, such as the fire wall of the blowout pit in the petroleum industry, indepen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66E04G21/14
Inventor 付文涛高兴宝谌登刚周洲刘颖
Owner CHINA NAT PETROLEUM CORP CHUANQING DRILLING ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap