Preparation technology of camouflage cover cloth
A preparation process and tent cloth technology are applied in the field of camouflage tent cloth preparation technology, which can solve the problems of destroying dyes, reducing strength, destroying the fabric itself, etc., and achieving the effects of low economic cost, high water repellency and reasonable process.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0045] Example one:
[0046] A preparation process of camouflage tent cloth includes the following steps: the first step is to pre-treat the base cloth for dyeing, printing, coating, and setting; the second step is to use disperse dyes including dyeing with near-infrared shielding function The base fabric is dyed with the dye liquor of ultraviolet absorber; the third step is to select the printing paste including the disperse dye for printing with near-infrared shielding function to print the dyed base fabric; the fourth step is to use polyamide resin glue Base the printed base fabric; the fifth step, use PVC coating paste to whiten the base fabric after the base; the sixth step, use polyurethane silver paste to PU white the base fabric after the PVC Silver surface coating; The seventh step, the base fabric after PU silver surface coating is dipped and rolled in a water-repellent finishing solution, then dried and baked. The amount of disperse dye for dyeing in the dye liquor is...
Example Embodiment
[0047] Embodiment two:
[0048] The difference from the first embodiment is that the amount of disperse dye for dyeing in the dye liquor is 0.5% (owf), and the amount of ultraviolet absorber is 0.5% (owf). The amount of dispersant per liter of dye liquor is 1g, the amount of high-temperature levelling agent per liter of dye liquor is 1g, and the amount of penetrant per liter of dye liquor is 2g. In the second step, when dyeing, first put the dye solution and base cloth at room temperature, adjust the pH of the dye solution to 4.5, then heat up to 50°C in 15 minutes, and then heat up to 125°C in 50 minutes, then After being kept for 80 minutes, the temperature is lowered and the base cloth is restored, and the liquor ratio is 1:30. The weight ratio of the disperse dye for printing, synthetic thickener, and binder is 0.5:60:4. The weight ratio of the polyamide resin coating glue, crosslinking agent, and solvent is 100:1:8. Adjust the viscosity to 8000mPa·S when preparing polyami...
Example Embodiment
[0049] Example three:
[0050] The difference from the first embodiment is that the amount of disperse dye for dyeing in the dye liquor is 2.5% (owf), and the amount of ultraviolet absorber is 2.5% (owf). The amount of dispersant per liter of dye liquor is 2g, the amount of high-temperature levelling agent per liter of dye liquor is 2g, and the amount of penetrant per liter of dye liquor is 0.5g. In the second step, the dye liquor has a liquor ratio of 1:50. The weight ratio of the disperse dye for printing, synthetic thickener and binder is 2.5:90:15. The weight ratio of the polyamide resin coating glue, crosslinking agent and solvent is 90:1.5:4. Adjust the viscosity to 10000mPa·S when preparing polyamide resin glue. In the fourth step, the process parameters when using polyamide resin glue for bottoming are: select an acute angle scraper, adjust the angle of the scraper to 115 degrees, adjust the magnetic force of the magnet roller to 90%, control the temperature of the fro...
PUM
Property | Measurement | Unit |
---|---|---|
Breaking strength | aaaaa | aaaaa |
Breaking strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap