Ceramic paint and coating having stereoscopic effect

A technology of ceramic coating and three-dimensional effect, applied in the field of ceramic coating and coatings prepared by adopting the ceramic coating, can solve the problems of reduced work efficiency, cumbersome steps, etc., and achieves good decorative effect, good hot and cold hardness and wear resistance Effect

Inactive Publication Date: 2013-04-10
INNOTEK TECH CHINA
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN102212302A discloses a three-dimensional effect paint, which is composed of hydroxyacrylic resin as the main component, which can provide a vivid three-dimensional effect on the decorative surface, enhance the appearance of the surface, and improve the decoration, but it is only suitable for indoor and outdoor decoration, furniture, handicrafts, etc. Surface decoration, other than cooking utensils
CN101104778A discloses a three-dimensional anti-stick coating that can produce stereoscopic effects on the surface of cookware. It is formed by mixing magnetic particle dispersion and anti-stick coating, including fluorocarbons, organic silicon resins and water-based fluororesin three-dimensional anti-stick coatings , but this process needs to disperse the magnetic micro-powder first, which cannot be directly added to the paint for use, the steps are cumbersome, and the work efficiency is reduced; and the technical solution does not involve the ceramic paint system

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic paint and coating having stereoscopic effect
  • Ceramic paint and coating having stereoscopic effect
  • Ceramic paint and coating having stereoscopic effect

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The preparation method of the ceramic paint with three-dimensional effect:

[0027] The invention provides a method for manufacturing a ceramic coating with a three-dimensional effect. First, fully disperse the silica sol and magnetic powder until the precipitate completely disappears as liquid A; then mix organosilane and catalyst uniformly as liquid B; then liquid B Add it into the dispersed liquid A, mature for 1.5-12 hours, and finally filter with a 100-150 mesh filter to obtain the ceramic coating of the present invention.

[0028] When adding silicone oil to the ceramic coating, first fully disperse the silica sol and magnetic powder until the sediment disappears completely as liquid A; then mix organosilane, silicone oil and catalyst evenly as liquid B; then add liquid B to the In the dispersed liquid A, ripen for 1.5 to 12 hours, and finally filter with a 100-150 mesh filter screen to obtain the ceramic coating of the present invention.

[0029] Preparation met...

Embodiment 1

[0051] First, fully disperse 100 parts by weight of silica sol and 1 part by weight of magnetic powder Black Mica until the precipitate completely disappears as liquid A; then add 60 parts by weight of methyltrimethoxysilane, 5 parts by weight of phenyl trimethyl Oxysilane and 0.6 parts by weight of acetic acid are mixed uniformly as liquid B; then liquid B is added to liquid A that has been dispersed, aged for 2 hours, and finally filtered with a 100-150 mesh filter to obtain the present invention. Ceramic coatings.

Embodiment 2

[0053] First, 100 parts by weight of silica sol and 12 parts by weight of magnetic powder Blackstar Green are fully dispersed until the precipitate completely disappears as liquid A; then 50 parts by weight of methyltrimethoxysilane, 5 parts by weight of silicone oil PMX- 0156 and 0.3 parts by weight of formic acid are uniformly mixed as liquid B; then liquid B is added to liquid A that has been dispersed, aged for 1.5 hours, and finally filtered with a 100-150 mesh filter to obtain the ceramic coating of the present invention .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to ceramic paint having a stereoscopic effect, which is characterized by comprising the following components in parts by weight: 100 parts of silica sol, 50-100 parts of organosilane, 0.3-1 part of catalyst, and 1-20 parts of magnetic powder, wherein the organosilane is methyltrimethoxy silane and/or methyltriethoxy silane; and the catalyst is one or a combination of formic acid, acetic acid, hydrochloric acid, citric acid, methyl formate, ethyl acetoacetate and maleic anhydride. The ceramic paint further comprises 1-5 parts by weight of silicone oil and 5-10 parts by weight of additional organosilane, wherein the additional organosilane is one or a combination of tetramethoxyl silane, tetraethoxy silane, dimethyldimethoxy silane, dimethyldiethoxy silane and phenyltrimethoxy silane. The ceramic paint provided by the invention has favorable cold/hot hardness and wear resistance; and the magnetic powder in the paint can form a coating having multiple stereoscopic patterns, thereby achieving good decorative effect.

Description

technical field [0001] The invention relates to a ceramic coating and a coating prepared by using the ceramic coating, in particular to a ceramic coating and a coating with a three-dimensional effect. Background technique [0002] Nowadays, people's living standards are improving day by day, pursuing a fashionable and beautiful living room environment, and they are increasingly particular about the appearance of kitchen utensils. At present, the appearance of cooking utensils is dominated by traditional flat designs, using different colors and patterns, and achieving decorative effects through coatings. With the rise of the 3D concept, it is also a development trend to realize 3D stereoscopic effects on cooking utensils. CN102212302A discloses a three-dimensional effect paint, which is composed of hydroxyacrylic resin as the main component, which can provide a vivid three-dimensional effect on the decorative surface, enhance the appearance of the surface, and improve the de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/24
Inventor 林学佐钟迪克
Owner INNOTEK TECH CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap