Carbonyl compound M(CO)6 modified high-performance aluminum alloy material and preparation method thereof

A technology of aluminum alloy material and carbonyl, which is applied in the field of high-performance aluminum alloy material and its preparation, can solve the problems of mixing harmful elements, affecting product quality, and large fluctuation range of modificator ratio, so as to improve strength and elongation performance , reduce the overall cost, improve the effect of metamorphism

Inactive Publication Date: 2015-01-21
GUIZHOU HUAKE ALUMINUM MATERIAL ENG TECH RES
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] In actual production, the frequent problems are that the modifying ability of the modifying agent is unstable, the ratio of the modifying agent added fluctuates widely, it is not easy to accurately control the amount added, and at the same time, it is very easy to mix harmful elements in the process of manufacturing aluminum master alloys of high-temperature elements , has a great influence on the final product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbonyl compound M(CO)6 modified high-performance aluminum alloy material and preparation method thereof
  • Carbonyl compound M(CO)6 modified high-performance aluminum alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0053] Step 1: Select the formula of each element and substance according to the table below, and calculate the weight of each substance required based on the total amount of the prepared alloy of 1000kg.

[0054]

[0055]

[0056] Step 2: First add aluminum ingots or molten aluminum into the melting furnace, heat it to melt it completely and keep it warm at 700-800°C; the melting process is completed in a closed environment;

[0057] Step 3: Add the alloy elements selected in Step 1 according to the proportion of the formula to completely dissolve and melt them, and stir the mixed melt evenly;

[0058] Step 4: Refining the above alloy melt in a furnace; adding a refining agent to the alloy melt and stirring evenly, and the melt refining is operated in a closed environment;

[0059] Step 5: After refining and removing slag, degas the melt with protective gas nitrogen, and at the same time make the carbonyl compound M(CO) 6 The molecular crystal modifier (30 mesh) is add...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a carbonyl compound M(CO)6 modified high-performance aluminum alloy material and a preparation method thereof. The alloy comprises the following components in percentage by weight: less than or equal to 8ppm of Be, 0.005-0.2 percent of Cu, less than or equal to 0.05 percent of Mn, less than or equal to 0.05 percent of Mg, less than or equal to 0.01 percent of Cr, less than or equal to 0.01 percent of Ni, less than or equal to 0.1 percent of Zn, less than or equal to 0.06 percent of Ti, less than or equal to 0.03 percent of Ca, less than or equal to 0.05 percent of V, less than or equal to 0.05 percent of B, 0.003-0.005 percent of Si, 0.003-0.65 percent of Fe and the balance of Al and inevitable trace impurities, wherein the content of a single impurity element is less than or equal to 0.03 percent, the content of the total impurity elements is less than or equal to 0.15 percent, and the carbonyl compound M(CO)6 molecular crystal modifying agent is 1ppm to 1.0 percent of the total furnace burden amount. The aluminum alloy material has a crystalline grain structure which is smaller than that of general aluminum and aluminum alloy and has high purity.

Description

technical field [0001] The invention relates to an aluminum alloy material and a preparation method thereof, in particular to a carbonyl compound M(CO) 6 A metamorphic high-performance aluminum alloy material and a preparation method thereof. Background technique [0002] Modification can greatly improve the comprehensive mechanical properties and chemical stability indicators of aluminum alloys, sometimes even subversively. Substances capable of altering are called modificators. [0003] At present, almost all modificators are concentrated on one technical means: to produce master alloys containing modifiable elements with aluminum as the matrix, and then add the master alloys to the melt when the aluminum alloy is smelted. [0004] This process produces two unfavorable links for energy saving: ①The melting and casting of master alloys containing high concentrations of metamorphic elements often require very high temperatures (>1000°C, such as Al-Ti-B, Al-RE, Al- Si, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/00C22C21/04C22C1/06C22C1/02
Inventor 门三泉车云张中可
Owner GUIZHOU HUAKE ALUMINUM MATERIAL ENG TECH RES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products