Gas-phase antirust agent containing modified nanometer bentonite

A technology of nano-bentonite and gas phase rust inhibitor, applied in the field of metal rust prevention, can solve the problem of inability to form rust protection and the like, and achieve the effects of good gas phase rust prevention effect, good gas phase rust prevention effect and good contact rust prevention effect.

Active Publication Date: 2013-05-15
湖南三创富泰环保材料股份有限公司
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing anti-rust agents are all composed of base oil and oil-soluble corrosion inhibitors, which can only play the functi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gas-phase antirust agent containing modified nanometer bentonite
  • Gas-phase antirust agent containing modified nanometer bentonite
  • Gas-phase antirust agent containing modified nanometer bentonite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] A kind of gas-phase antirust agent containing modified nano-bentonite, it is made by the raw material of following parts by weight (kg):

[0020] Castor oil 93, ferrocene 1.2, polyisobutene 1.8, 2-aminoethylheptadecenyl imidazoline 1.2, N-phenyl-2-naphthylamine 0.8, 1-hydroxybenzotriazole 1.4, hexamethoxene Product 1.1, zinc dialkyldithiophosphate 2, sodium dodecylbenzenesulfonate 0.8, film-forming resin 4.8, modified nano-bentonite 1.1;

[0021] The film-forming resin is prepared from the following raw materials in parts by weight: rosin 4.7, urea 3.1, zinc powder 1.7, dimethyl silicone oil 2.3, liquefied paraffin 10.6, 3-aminopropyltrimethoxysilane 2.7, acetylcitric acid Tris (2-ethylhexyl) ester 6, epoxy linseed oil 11, xylene 9.7, polyvinyl alcohol 7.9;

[0022] The preparation method of the modified nano-bentonite is as follows: the bentonite is soaked in 15% sodium hydroxide solution for 9 hours, washed with deionized water, dried, and 2.4.6-tri(dimethylbenzene) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a gas-phase antirust agent containing modified nanometer bentonite. The antirust agent is prepared from the following raw materials in parts by weight: 90-95 parts of castor oil, 0.9-1.2 parts of ferrocene, 0.9-1.8 parts of polyisobutene, 1-2 parts of 2-aminoethyl heptadecenyl imidazoline, 0.8-1.3 parts of N-phenyl-2-naphthylamine, 1.1-1.7 parts of 1-hydroxybenzotriazole, 0.9-1.1 parts of urotropine, 1-2 parts of zinc dialkyl dithiophosphate, 0.4-0.8 part of sodium dodecyl benzene sulfonate, 4.4-4.8 parts of film-forming resins and 0.8-1.4 parts of modified nanometer bentonite. The gas-phase antirust agent has excellent contact antirusting performance and good gas-phase antirusting effect and has good gas-phase antirusting effect and contact antirusting effect on steels and brasses.

Description

technical field [0001] The invention relates to the technical field of metal antirust, in particular to a gas phase antirust agent containing modified nano-bentonite. Background technique [0002] Corrosion is one of the main forms of damage to metal products. According to statistics, the annual direct economic loss caused by metal corrosion accounts for about 2%-4% of the total output value of the national economy. [0003] In order to avoid corrosion and reduce losses, people have adopted various methods, and using antirust agents to protect metal products is one of the most common protection methods at present. Antirust agent grease is composed of one or more antirust additives (also known as oil-soluble corrosion inhibitors) and auxiliary additives added to the basic components of petroleum. It is easy to use, low in cost, good in effect, and simple in operation. Metalwork industries are heavily used. However, the existing anti-rust agents are all composed of base oil ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23F11/02
Inventor 何益庆
Owner 湖南三创富泰环保材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap