A metal antirust oil containing sorbitan monooleate

A sorbitan monooleate and metal anti-rust technology, applied in the field of metal anti-rust oil, can solve the problem that the anti-rust effect is not good enough, and achieve excellent contact anti-rust performance, good gas-phase anti-rust effect, and good contact anti-rust effect of effect

CN103215595BActive Publication Date: 2016-03-02ANHUI FANCHANG COUNTY WANNAN VALVE CASTING
4 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Patents(China)
Current Assignee / Owner
Publication Date
2016-03-02

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
Patent Text Reader

Abstract

The invention discloses a metal antirust oil containing sorbitan monooleate, which is prepared from the following raw materials: No. 120 solvent oil, hydroxyethyl methacrylate, silane coupling agent KH 792, sorbitan monooleate Oleate, ethanol, polypropylene glycol, modified nano kaolinite powder, antioxidant, composite film-forming material, magnesium stearate, polyethylene glycol, triethanolamine oleate, barium petroleum sulfonate, antioxidant BHT, Alcohol ether glycoside, phenylethanolamine A, benzotriazole, 2-aminoethyl heptadecenyl imidazoline, phytic acid. The invention has excellent contact antirust performance and good gas phase antirust effect, and the invention has good gas phase antirust effect and contact antirust effect on steel and brass.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to the field of metal surface treatment agents, in particular to a metal antirust oil containing sorbitan monooleate. Background technique

[0002] Metal surface treatment agent refers to the general term for various chemical agents for metal surface treatment. Metal surface treatment includes degreasing, rust removal, phosphating, antirust and other substrate pretreatments, which are prepared for metal coating technology and metal protection technology. The quality of substrate pretreatment has a great influence on subsequent coating preparation and metal use. big impact.

[0003] Oil-soluble rust inhibitors are also called oil-soluble corrosion inhibitors. Most are long carbon chain organic compounds with polar groups. The polar groups in the molecule are tightly adsorbed on the metal surface by the action of charge; the non-polar group long carbon chain hydrocarbons are facing the outside of the metal surface, and can be mis...

Examples

Embodiment Construction

[0015] A metal antirust oil containing sorbitan monooleate, it is made by the raw material of following parts by weight (kg):

[0016] No. 120 solvent oil 110, hydroxyethyl methacrylate 1.3, silane coupling agent KH7921.7, sorbitan monooleate 1.8, ethanol 0.7, polypropylene glycol 0.2, modified nano kaolinite powder 0.4, antioxidant 6260.2, Composite film-forming material 7, magnesium stearate 0.4, polyethylene glycol 0.5, triethanolamine oleate 2.5, barium petroleum sulfonate 0.7, antioxidant BHT0.6, alcohol ether glycoside 0.8, phenylethanolamine A0.3, benzo Triazole 0.9, 2-aminoethyl heptadecenyl imidazoline 1.9, phytic acid 0.4;

[0017] The composite film-forming material is prepared from the following raw materials in parts by weight: 138 rosin resin 40, triisopropanolamine 0.4, octylphenol polyoxyethylene ether 5, chlorobutanol 2, ethyl acetate 2, No. 120 solvent oil 72, butyl acrylate 3, dimethyl silicone oil 2;

[0018] The preparation method of the modified nano-ka...