Novel 6063 aluminum alloy material and its production technology

A technology of aluminum alloy material and production process, which is applied in the field of new 6063 aluminum alloy material, can solve problems such as gaps in product quality and process technology, difficulty in producing profiles, and narrow application range, so as to broaden the application range, improve production efficiency, and improve The effect of machinability

Active Publication Date: 2013-07-17
CHENGDU SUNSHINE ALUMINUM
View PDF0 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the high production cost of my country's construction 6063 aluminum profile products and the great gap between product quality and process technology, most of the profiles in my country are concentrated in low-end products. It is difficult to produce profiles with complex cross-sections for 6063 aluminum profiles, which makes the scope of application of the products narrow.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Example 1 : A new type of 6063 aluminum alloy material. Rare earth elements are added to the original 6063 aluminum alloy. The composition and weight percentage of the new 6063 aluminum alloy are: Si: 0.36%, Mg: 0.48%, Fe: 0.3%, Cu: 0.025%, Mn : 0.025%, Cr: 0.05%, Zn: 0.05%, Ti: 0.05%, rare earth elements: 0.2%, other impurities: 0.1%, Al: balance, the sum of the percentages of each component is 100%.

[0027] The rare earth elements include La and Ce, and their weight percentages are: 41.5% for La and 58.5% for Ce.

[0028] A kind of production technological process of novel 6063 aluminum alloy material comprises the following steps:

[0029] S1: Ingredients: select 99.7% industrial pure aluminum, Al-rare earth master alloy, industrial magnesium ingot and aluminum-silicon master alloy ingot as the raw material of furnace charge, and select covering agent, refining agent and paint as auxiliary materials;

[0030] The components and weight percentages of each charge ra...

Embodiment 2

[0040] Example 2 : A new type of 6063 aluminum alloy material. Rare earth elements are added to the original 6063 aluminum alloy. The composition and weight percentage of the new 6063 aluminum alloy are: Si: 0.52%, Mg: 0.4%, Fe: 0.35%, Mn: 0.05%, Zn : 0.05%, rare earth elements: 0.18%, Al: balance, the sum of the percentages of each component is 100%.

[0041] The rare earth elements include La and Ce, and their weight percentages are: 41.5% for La and 58.5% for Ce.

[0042] The production process flow of a novel 6063 aluminum alloy material is the same as that of Example 1.

Embodiment 3

[0043] Example 3 : A new type of 6063 aluminum alloy material. Rare earth elements are added to the original 6063 aluminum alloy. The composition and weight percentage of the new 6063 aluminum alloy are: Si: 0.5%, Mg: 0.38%, Cu: 0.1%, Cr: 0.05%, Ti : 0.05%, rare earth elements: 0.22%, other impurities: 0.1%, Al: the balance, and the sum of the percentages of each component is 100%.

[0044] The rare earth elements include La and Ce, and their weight percentages are: 41.5% for La and 58.5% for Ce.

[0045] The production process flow of a novel 6063 aluminum alloy material is the same as that of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel 6063 aluminum alloy material. Rare earth elements are added into the original 6063 aluminum alloy. The novel 6063 aluminum alloy material comprises, based on the weight percentage,0.36%- 0.4% of Si, 0.48% - 0.52% of Mg, 0 -0.35% of Fe, 0 -0.1% of Cu, 0 - 0.05% of Mn, 0 - 0.05% of Cr, 0 - 0.05% of Zn, 0 - 0.05% of Ti, 0.18%-0.22% rare earth elements, 0-0.1% of the remaining impurities and the balance of Al. According to the invention, the content of Mg and Si is controlled within a narrow range. At the same time, cerium-based mixed rare earth elements and alloying element boron are added, which keeps alloy material high strength and high electrical and thermal conductivity; improves machining property and plastic extrusion; and improves production efficiency.

Description

technical field [0001] The invention relates to a novel 6063 aluminum alloy material, which belongs to the technical field of nonferrous metal processing. Background technique [0002] The widening application of 6063 aluminum alloy in construction, decoration, automobile, aviation, electronics and other fields has higher requirements for the strength performance, corrosion resistance and oxidation coloring performance of the new modified deformed aluminum alloy. Due to the existence of a large number of hard phases in some aluminum alloys, the machining performance is poor, the extrusion force is large, the die wear is large, the life is low, the extrusion speed is slow, the production efficiency is low, and the energy consumption is high. For some thin-walled and complex profiles, especially extruded profiles with a width-to-thickness ratio greater than 100 and a large degree of asymmetry and anisotropy, ordinary 6063 alloys cannot be formed well at all. In order to meet m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/08C22C1/03
Inventor 廖健
Owner CHENGDU SUNSHINE ALUMINUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap