Positive pole and paste of long-service-life power lead-acid storage battery

A lead-acid battery, long-life technology, applied in battery electrodes, circuits, electrical components, etc., can solve problems such as shortening curing time, and achieve the effect of improving plate consistency, improving battery life, and solving unevenness

Active Publication Date: 2013-11-06
HENAN CHAOWEI POWER SUPPLY
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The positive electrode and paste of the lead-acid storage battery of the present invention can effectively solve the matching relationship between the existing battery capacity and life, improve the capacity and life of the battery, and at the same time greatly improve the consistency of the plate, and use high temperature curing to shorten the curing time, thereby effectively Solve problems such as inhomogeneity of formation and improve production efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The positive electrode and paste of the long-life power lead-acid storage battery of the present invention are expressed in weight percent, and the raw material ratio composition of the positive electrode of the lead-acid storage battery and the paste is as follows:

[0019] Lead powder 83%, sulfuric acid 8%, stannous sulfate 0.15%, conductive fiber (using polyacetylene) 0.06%, colloidal graphite 0.25%, cerium oxide 0.07%, 4BS seed (using 4PbO·PbSO 4 Crystals) 0.9%, the balance is deionized water.

[0020] The mass percent concentration of the raw material sulfuric acid used is 45%; 4PbO·PbSO 4 The mass percentage of crystals is ≥98%, the grain size is 1.2-1.5 μm, and the mass percentage of impurity iron is ≤0.0008%.

Embodiment 2

[0021] Embodiment 2: basically the same as Embodiment 1, the difference is:

[0022] The positive electrode and paste of the long-life power lead-acid storage battery of the present invention are expressed in weight percent, and the raw material ratio composition of the positive electrode of the lead-acid storage battery and the paste is as follows:

[0023] Lead powder 80%, sulfuric acid 6%, stannous sulfate 0.10%, conductive fiber (using polypyrrole) 0.05%, colloidal graphite 0.20%, cerium oxide 0.05%, 4BS seed crystal (using 4PbO·PbSO 4 crystals) 0.8%, and the balance is deionized water.

Embodiment 3

[0024] Embodiment 3: basically the same as Embodiment 1, the difference is:

[0025] The positive electrode and paste of the long-life power lead-acid storage battery of the present invention are expressed in weight percent, and the raw material ratio composition of the positive electrode of the lead-acid storage battery and the paste is as follows:

[0026] Lead powder 85%, sulfuric acid 9%, stannous sulfate 0.20%, conductive fiber (using polypyrrole) 0.07%, colloidal graphite 0.30%, cerium oxide 0.09%, 4BS seed crystal (using 4PbO·PbSO 4 crystals) 1.0%, and the balance is deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a positive pole and paste of a long-service-life power lead-acid storage battery. Raw materials of the positive pole and the paste of the long-service-life power lead-acid storage battery consist of, by weight, lead powder 80-85%, sulfuric acid 6-9%, stannous mono-sulphate 0.1-0.2%, conductive fiber 0.05-0.07%, colloidal graphite 0.2-0.3%, cerium oxide 0.05-0.09%, 4BS seed crystal 0.8-1.0% and the balance deionized water. By adopting the positive pole and paste of the long-service-life power lead-acid storage battery, the matching relationship of the existing battery capacity and the service life can be effectively solved, the battery capacity is improved, and the service life is prolonged. In addition, the consistency of a pole plate is improved remarkably, and accordingly the problems including uneven formation and the like are effectively solved.

Description

technical field [0001] The invention relates to the technical field of lead-acid batteries, in particular to a positive electrode and paste of long-life power lead-acid batteries. Background technique [0002] Ordinary batteries are also called lead-acid batteries. Its electrodes are composed of lead and lead oxides, and the electrolyte is an aqueous solution of sulfuric acid. The main advantages are stable voltage and low price; the disadvantages are low specific energy (that is, the electric energy stored per kilogram of battery), short service life and frequent daily maintenance. Old-fashioned ordinary batteries generally have a lifespan of about 2 years, and it is necessary to regularly check the height of the electrolyte and add distilled water. However, with the development of technology, the life of ordinary batteries has become longer and easier to maintain. [0003] Lead-acid batteries have been widely used in various low-speed vehicle markets, and a lot of resear...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/62
CPCY02E60/12Y02E60/10
Inventor 张雷程志明李松林
Owner HENAN CHAOWEI POWER SUPPLY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com