A kind of pickling solution containing compound passivating agent and preparation method thereof

A technology of passivating agent and pickling solution, which is applied in the field of cleaning stainless steel castings, can solve the problems of no specific implementation plan, etc., and achieve the effect of small acid mist, low acid treatment cost, bright and beautiful surface

Active Publication Date: 2016-06-15
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Point out the merits of commonly used treatment methods for acid mist and adding corrosion inhibitors, and roughly compare them. The lack is that there is no specific implementation plan

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1: sample preparation

[0020] The pickling solution containing passivating agent used in the following examples is prepared by the following method: 1000kg concentration is 50% industrial nitric acid mixed with 200kg40% hydrofluoric acid, after stirring evenly, add corrosion inhibitor (by Uro Tropin 40kg, sulfamic acid 40kg, sodium sulfamate 100kg one or a combination of several) and brightener (composed of triethylene glycol 20kg, coumarin, saccharin, glycerin 10kg each and alkane surfactant 40kg) or several mixed compositions), and finally add 410kg of water into the solution and stir evenly. Placed at 25°C, reacted for 24 hours. The final solution was light yellow-green and clear. The preparation is complete and ready for use.

Embodiment 2

[0021] Embodiment 2: sample preparation

[0022] The pickling solution containing passivating agent used in the following examples is prepared by the following method: the industrial nitric acid of 1000kg50% is mixed with the hydrofluoric acid of 150kg40%, after stirring, add corrosion inhibitor successively (by urotropine 2.0 kg, sulfamic acid 2.0kg, sodium sulfamate 1.0kg, one or several mixtures) and brightener (composed of triethylene glycol 1.0kg, coumarin 1.0, saccharin 0.4kg, glycerin 0.4g and alkanes surface active 1.0kg of one or several mixtures), and finally add 840kg of water into the solution and stir evenly. Placed at 25°C, reacted for 24 hours. The final solution was light yellow-green and clear. The preparation is complete and ready for use.

Embodiment 3

[0023] Example 3: Sample Preparation

[0024] The pickling solution containing passivating agent used in the following examples is prepared by the following method: 1000kg concentration is 50% industrial nitric acid and 300kg40% hydrofluoric acid are mixed, after stirring, add corrosion inhibitor (by Uro Tropin 10kg, sulfamic acid 3kg, sodium sulfamate 2kg (one or several mixtures) and brightener (1.2kg of triethylene glycol, 0.5kg of coumarin, 0.5kg of saccharin, 1kg of glycerin and alkanes surface active 1.5kg of one or several mixtures), and finally add 680kg of water into the solution and stir evenly. Placed at 25°C, reacted for 24 hours. The final solution was light yellow-green and clear. The preparation is complete and ready for use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of cleaning stainless steel castings, and relates to a pickling solution with passivation effect obtained by adding organic substances to HNO3 and HF basic acid solution. It is composed of nitric acid and hydrofluoric acid, compound passivating agent and water, and its mass content is respectively: 3.3%~37.5% for nitric acid, 0.7%~7.5% for hydrofluoric acid, and 1.3~13.5% for compound passivating agent , Water is the balance. Clean the polluted stainless steel castings to restore the metallic luster of the castings. And a dense passivation film is formed on the surface of the casting, so that the casting can still keep silver bright and beautiful without rust spots after long-term storage. Another feature of the present invention is that the acid mist is very small, which is beneficial to environmental protection and the health of operators, the pickling amount is large, and the acid treatment cost is low.

Description

technical field [0001] The invention belongs to the technical field of cleaning stainless steel castings, and relates to a compound pickling solution passivator for cleaning various steel materials. Background technique [0002] At present, the cleaning process of steel is mainly pickling, and the main components are sulfuric acid, hydrochloric acid, nitric acid, hydrofluoric acid, etc., which are prepared by adding different additives according to different proportions. But in reality, the existing pickling process has the disadvantages of large acid consumption, large acid mist, and short waste acid discharge cycle. The current pickling solution tends to add different substances to the acid to stabilize the acid solution, promote cleaning, and slow-release the steel, thereby corroding the steel and prolonging the service life. [0003] There are few reports on such pickling liquid additives. Huazhong University of Science and Technology; Wuhan Yongxing Chemical Co., Ltd....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23G1/06C23G1/08
Inventor 李艳荣朱立忠李忠建陆建国侯红美
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com