Polypropylene panel allowing writing and production technology thereof

A technology of polypropylene and writing board, which is applied in the field of stationery, can solve the problem of non-writable polypropylene boards, and achieve natural and smooth handwriting, good weather resistance, and good adhesion

Inactive Publication Date: 2015-07-22
义乌市祥胜文化用品有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a polypropylene writable plate, by coating a layer of coating with an ink composition on the surface of the polypropylene sheet to solve the problem of non-writable on the polypropylene plate, using the polypropylene sheet of the present invention Acrylic writable board can achieve the same writing effect as paper, and the coating has a good combination with polypropylene, which has a good use effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of polypropylene writable plate, comprising a polypropylene sheet and a coating with a thickness of 10 μm formed by coating the ink composition, the preparation process of this polypropylene writable plate comprises the following steps:

[0032] (1) Ink composition configuration: According to the ratio in Table 1, mix the components of the ink composition with PP ink, matting agent, diluent (cyclohexanone, isophorone or ethyl acetate), curing agent, coupling agent (N-(β-aminoethyl)-γ-aminopropyltriethoxysilane), polydimethylsiloxane, mica powder and antioxidant were mixed uniformly, left for 18 hours to obtain an ink composition, and set aside;

[0033] (2) Polypropylene sheet treatment: take a polypropylene sheet with a thickness of 0.16mm, and frost the printing surface of the polypropylene sheet;

[0034] (3) Printing: Print the ink composition obtained in step (2) on the printing surface of the polypropylene sheet by screen printing process, the screen size i...

Embodiment 2

[0036] A kind of polypropylene writable plate, comprising a polypropylene sheet and a coating with a thickness of 20 μm formed by ink composition coating, the preparation process of this polypropylene writable plate comprises the following steps:

[0037] (1) Ink composition configuration: According to the ratio in Table 1, mix the components of the ink composition with PP ink, matting agent, diluent (cyclohexanone, isophorone or ethyl acetate), curing agent, coupling agent (N-(β-aminoethyl)-γ-aminopropyltriethoxysilane), polydimethylsiloxane, mica powder and antioxidant were mixed uniformly, left for 15 hours to obtain an ink composition, and set aside;

[0038] (2) Polypropylene sheet treatment: take a polypropylene sheet with a thickness of 0.3mm, and frost the printing surface of the polypropylene sheet;

[0039] (3) Printing: Print the ink composition obtained in step (2) on the printing surface of the polypropylene sheet by screen printing process, the screen size is 250...

Embodiment 3

[0041] A kind of polypropylene writable plate, comprising a polypropylene sheet and a coating with a thickness of 16 μm formed by ink composition coating, the preparation process of this polypropylene writable plate comprises the following steps:

[0042] (1) Ink composition configuration: According to the ratio in Table 1, mix the components of the ink composition with PP ink, matting agent, diluent (cyclohexanone, isophorone or ethyl acetate), curing agent, coupling agent (N-(β-aminoethyl)-γ-aminopropyltriethoxysilane), polydimethylsiloxane, mica powder and antioxidant were mixed uniformly, left for 12 hours to obtain an ink composition, and set aside;

[0043] (2) Polypropylene sheet treatment: take a polypropylene sheet with a thickness of 0.8mm, and frost the printing surface of the polypropylene sheet;

[0044] (3) Printing: Print the ink composition obtained in step (2) on the printing surface of the polypropylene sheet by screen printing process, the screen size is 350...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a polypropylene writable plate and its preparation process. The polypropylene writable plate comprises a polypropylene sheet and a coating formed by coating an ink composition. The ink composition consists of the following parts by weight: Component composition: 100 parts of PP ink, 10-20 parts of matting agent, 40-60 parts of thinner, 1-5 parts of curing agent, 1-3 parts of coupling agent, 3-5 parts of polydimethylsiloxane, mica Powder 3~5 parts, antioxidant 2~5 parts. The coating on the surface of polypropylene writable board is prepared by screen printing process. After coating a layer of coating on the surface of polypropylene, the purpose of changing the smoothness of the surface of polypropylene can be achieved, so that it can be processed on the surface of polypropylene. Writing, and the handwriting after writing is not easy to be erased.

Description

technical field [0001] The invention relates to the field of stationery, in particular to a polypropylene writable board and a preparation process thereof. Background technique [0002] Polypropylene is a very common plastic at present. It has been used in all aspects of life. Polypropylene is cheap, non-toxic, odorless, low density, and has excellent strength, stiffness, hardness and heat resistance. , but the surface of the polypropylene sheet is smooth, so it is difficult to write on the surface of the polypropylene sheet. wipe. In order to change the non-writable shortcomings of polypropylene, it is necessary to coat a layer of coating on the surface of polypropylene, thereby changing the inherent characteristics of polypropylene, so that writing can be performed on this layer, but the combination of coating and polypropylene is not strong It will cause the coating to fall off when writing, affecting the use effect. [0003] A publication number is CN 1101653A, and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B43L1/00
Inventor 黄胜伟
Owner 义乌市祥胜文化用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com