Waterproof printing oil base and preparation method
An oil-based, raw material technology, applied in the field of printing oil, can solve problems such as affecting the appearance and quality of printed matter, poor wear resistance, printing oil falling off, etc., and achieve the effect of shortening drying time, high firmness and strong adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] A waterproof printing oil base, which is composed of the following raw materials according to the following parts by weight: 25 parts of lignin-modified ethyl acetate, 5 parts of rosin-modified maleic acid resin, 2 parts of organic bentonite, 3 parts of titanium dioxide, and 3 parts of tin oxide 6 parts of mussel mucin, 5 parts of calcium acetate, 15 parts of environmental protection pigment, 2 parts of vegetable oil, 10 parts of graphite, 2 parts of nano rubber powder, 3 parts of activated clay, 1 part of zirconium dioxide, 2 parts of conductive components, 0.5 parts of beeswax, 5 parts of glyceride, 1 part of printing oil-based reinforcing agent, 1 part of polymerization inhibitor, 0.5 parts of stabilizer, 2 parts of wear-resistant additive, 2 parts of waterproofing agent, 1 part of wetting agent, and 1 part of thickener 1 part, 3 parts of curing agent, 1 part of curing accelerator, 1 part of defoamer, 60 parts of water.
[0023] A preparation method of waterproof pri...
Embodiment 2
[0029] A waterproof printing oil base, which is composed of the following raw materials according to the following parts by weight: 45 parts of lignin-modified ethyl acetate, 10 parts of rosin-modified maleic acid resin, 5 parts of organic bentonite, 6 parts of titanium dioxide, and 6 parts of tin oxide 10 parts of mussel mucin, 8 parts of calcium acetate, 20 parts of environmentally friendly pigments, 4 parts of vegetable oil, 15 parts of graphite, 4 parts of nano rubber powder, 5 parts of activated clay, 2 parts of zirconium dioxide, 5 parts of conductive components, 1 part of beeswax, 10 parts of glyceride, 3 parts of printing oil-based strengthening agent, 3 parts of polymerization inhibitor, 1 part of stabilizer, 4 parts of wear-resistant additive, 4 parts of waterproofing agent, 3 parts of wetting agent, 5 parts of thickener 6 parts, curing agent 6 parts, curing accelerator 3 parts, defoamer 5 parts, water 80 parts.
[0030] A preparation method of waterproof printing oi...
Embodiment 3
[0036] A waterproof printing oil base, which is composed of the following raw materials according to the following parts by weight: 35 parts of lignin-modified ethyl acetate, 8 parts of rosin-modified maleic acid resin, 3 parts of organic bentonite, 5 parts of titanium dioxide, and 5 parts of tin oxide 8 parts of mussel mucin, 6 parts of calcium acetate, 18 parts of environmental pigments, 3 parts of vegetable oil, 12 parts of graphite, 3 parts of nano rubber powder, 4 parts of activated clay, 1.5 parts of zirconia, 3 parts of conductive components, 0.8 parts of beeswax, 8 parts of glyceride, 2 parts of printing oil-based strengthening agent, 2 parts of polymerization inhibitor, 0.8 parts of stabilizer, 3 parts of wear-resistant additive, 3 parts of waterproofing agent, 2 parts of wetting agent, 3 parts of thickener 4 parts, curing agent 4 parts, curing accelerator 2 parts, defoamer 3 parts, water 70 parts.
[0037] A preparation method of waterproof printing oil base, compris...
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com