Rubber sealing material

A rubber seal and rubber technology, applied in the field of materials, can solve the problems of vicious accidents, losses and troubles, poor quality of seals, etc., and achieve the effect of low friction coefficient and strong wear resistance

Inactive Publication Date: 2014-02-19
WUXI WEIHAIDA MACHINERY MFG
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the quality of the seal is poor, it will cause loss and trouble if it is light, and it will cause serious accidents if it is serious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The formula of the rubber sealing material of the present invention is as follows:

[0012] 85kg of hydrogenated nitrile rubber, 30kg of acrylate rubber, 4kg of oleyl alcohol, 11kg of diacetyl peroxide, 4kg of alumina, 6kg of zinc oxide, 7kg of high wear-resistant carbon black, 1kg of antioxidant, 4kg of sulfur.

[0013] The acrylonitrile content in hydrogenated nitrile rubber is 24%, the Mooney viscosity is 75, and the iodine absorption value is 13.

[0014] The preparation method of the rubber sealing material of the present invention is as follows:

[0015] First add the formulated amount of hydrogenated nitrile rubber, acrylic rubber, oleyl alcohol, and diacetyl peroxide into the mixer. After mixing at 135°C for 6 minutes, add the formulated amount of antioxidant, alumina, and zinc oxide in sequence , High wear-resistant carbon black, sulfur, kneading, press molding; finally, the molded rubber material is added to the mold in the vulcanization equipment for vulcanization, t...

Embodiment 2

[0017] The formula of the rubber sealing material of the present invention is as follows:

[0018] Hydrogenated nitrile rubber 80kg, acrylate rubber 35kg, oleyl alcohol 5kg, diacetyl peroxide 10kg, alumina 5kg, zinc oxide 5kg, high wear-resistant carbon black 8kg, antioxidant 2kg, sulfur 5kg.

[0019] The acrylonitrile content of hydrogenated nitrile rubber is 23%, the Mooney viscosity is 70, and the iodine absorption value is 11.

[0020] The preparation method of the rubber sealing material of the present invention is as follows:

[0021] First add the formulated amount of hydrogenated nitrile rubber, acrylic rubber, oleyl alcohol, and diacetyl peroxide into the mixer, mix at 130°C for 8 minutes, and then add the formulated amount of antioxidant, alumina, and zinc oxide in sequence , High wear-resistant carbon black, sulfur, kneading, pressing molding; finally, the molded rubber material is added to the mold in the vulcanization equipment for vulcanization treatment, the temperature...

Embodiment 3

[0023] The formula of the rubber sealing material of the present invention is as follows:

[0024] 90kg of hydrogenated nitrile rubber, 25kg of acrylate rubber, 3kg of oleyl alcohol, 12kg of diacetyl peroxide, 3kg of alumina, 8kg of zinc oxide, 6kg of high wear-resistant carbon black, 0.3kg of antioxidant, and 3kg of sulfur.

[0025] The acrylonitrile content in hydrogenated nitrile rubber is 26%, the Mooney viscosity is 80, and the iodine absorption value is 15.

[0026] The preparation method of the rubber sealing material of the present invention is as follows:

[0027] First add the formulated amount of hydrogenated nitrile rubber, acrylate rubber, oleyl alcohol, and diacetyl peroxide into the mixer. After mixing for 5 minutes at 140°C, add the formulated amount of antioxidant, alumina, and zinc oxide in sequence , High wear-resistant carbon black, sulfur, kneading, press molding; finally, the molded rubber material is added to the mold in the vulcanization equipment for vulcaniza...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
friction coefficientaaaaaaaaaa
Login to view more

Abstract

The invention provides a rubber sealing material. The rubber sealing material consists of the following components in parts by mass: 80-90 parts of hydrogenated butadiene-acrylonitrile rubber, 25-35 parts of acrylate rubber, 3-5 parts of oleyl alcohol, 10-12 parts of diacetyl peroxide, 3-5 parts of aluminum oxide, 5-8 parts of zinc oxide, 6-8 parts of high wear resistant carbon black, 0.3-2 parts of an anti-aging agent, and 3-5 parts of sulfur. The rubber sealing material provided by the invention can bear the pressure of 410 Mpa, and has the advantages of low friction coefficient (0.20-0.22) and strong wear resistance.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a rubber sealing material. Background technique [0002] Sealing products are important basic components of all kinds of machinery, and almost all industrial sectors cannot do without it. The quality of the sealing element is directly related to the service life and operational reliability of the machine. If the quality of the seals is poor, it will cause loss and trouble if it is light, and it will cause serious accidents if it is serious. In an environment with high working pressure, the sealing ring bears a large load, which requires the sealing product not only to have good sealing performance, but also to have good high-pressure resistance. Contents of the invention [0003] The invention provides a high-pressure-resistant rubber sealing material capable of withstanding a pressure of 410MPa. [0004] The invention provides a rubber sealing material, which...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L15/00C08L33/04C08K13/02C08K5/14C08K3/22C08K5/05C08K3/06C08K3/04B29C35/02
Inventor 黄铁军
Owner WUXI WEIHAIDA MACHINERY MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka