Insulation sound-absorbing decorative plate and preparation method thereof

A decorative board and substrate technology, applied in the field of thermal insulation and sound-absorbing decorative boards and their preparation, can solve problems such as lack of thermal insulation and sound absorption, cement sand is not environmentally friendly, and unfavorable to human health, and achieve good thermal insulation effects, eliminate light pollution, and easily The effect of cleaning and maintenance

Active Publication Date: 2014-05-28
LIAOYANG YIMENG CARPET MFG
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, materials such as white paint, latex paint, and paint are mostly used for the exterior and interior walls of buildings, all of which contain formaldehyde, which is not conducive to human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Insulation sound-absorbing decorative plate and preparation method thereof
  • Insulation sound-absorbing decorative plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0041] Example 1

[0042] The PP fiber and glass fiber are mixed, and the mixing ratio is 30% according to the weight percentage of the PP fiber, and the rest is glass fiber; the air-laid method is used to make the PP fiber and glass fiber into a sheet under the condition of 150~180℃. Form the original substrate, the thickness is 10mm; the production speed when airlaid is 3m / min;

[0043] Using PET non-woven fabric as the bottom layer, one side of the original substrate and the bottom layer are pressed together with a pressing machine at a temperature of 180~220℃ to form a double-layer board composed of the substrate and the bottom layer; the pressing pressure is 8 Bar;

[0044] Perform corona treatment on the substrate surface of the double-layer board until the surface tension of the substrate surface of the double-layer board is 38 dyne, then preheat to 40°C, and then coat a layer of PUR glue on the surface of the double-layer board;

[0045] Using PVC film as the surface layer, th...

Example Embodiment

[0049] Example 2

[0050] The method is the same as in Example 1, the difference is:

[0051] (1) The mixing ratio of PP fiber and glass fiber is 40% by weight of PP fiber, and the rest is glass fiber; the original substrate is a 9mm thick coil; the production speed when airlaid is 2m / min;

[0052] (2) Use PP non-woven fabric as the bottom layer; the pressing pressure of the plate press is 5Bar;

[0053] (3) Perform corona treatment on the substrate surface of the double-layer board until the surface tension of the substrate surface of the double-layer board is 39 dyne, and then preheat to 50°C;

[0054] The weight of the bottom layer of the prepared thermal insulation sound-absorbing decorative board is 60g / ㎡ and the thickness is 0.28mm; the weight of the substrate is 1000g / ㎡ and the thickness is 3.5mm; the weight of the PP surface layer is 170g / ㎡ and the thickness is 0.18mm;

[0055] The thermal conductivity of the thermal insulation and sound-absorbing decorative board is 0.052W / (m·k)...

Example Embodiment

[0056] Example 3

[0057] The method is the same as in Example 1, the difference is:

[0058] (1) The mixing ratio of PP fiber and glass fiber is 50% according to the weight percentage of PP fiber, and the rest is glass fiber; the original substrate is 8mm thick; the production speed during airlaid is 3m / min;

[0059] (2) The pressing pressure of the plate press is 1Bar;

[0060] (3) Perform corona treatment on the substrate surface of the double-layer board until the surface tension of the substrate surface of the double-layer board is 40 dyne, and then preheat to 20~60℃;

[0061] The weight of the bottom layer of the prepared thermal insulation and sound-absorbing decorative board is 70g / ㎡ and the thickness is 0.31mm; the weight of the substrate is 1500g / ㎡ and the thickness is 5mm; the weight of the surface layer is 120g / ㎡ and the thickness is 0.13mm;

[0062] The thermal conductivity of the thermal insulation and sound-absorbing decorative board is 0.057W / (m·k); the sound-absorbing an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to an insulation sound-absorbing decorative plate and a preparation method, which belongs to the technical field of building material. The insulation sound-absorbing decorative plate comprises a substrate, a superficial layer and a bottom layer; the substrate is spliced with the superficial layer through PUR glue, the other surface of the substrate is spliced to the bottom layer; the materials of the substrate are PP fiber and glass fiber; the material of the superficial layer is a PP membrane, or a PVC membrane, or a PETG membrane; and the material of the bottom layer is non-woven fabrics. The preparation method comprises the following steps: 1)mixing the PP fiber and glass fiber, using an air laying method to prepare an original substrate; 2)taking the non-woven fabrics as the bottom layer, compacting one side of the original substrate and the bottom layer by a veneer press under the temperature of 180-220 DEG C to prepare a double-layer plate; 3)performing corona treatment and preheating the substrate surface of the double-layer plate, then coating the PUR glue; and 4)applying the superficial layer and the substrate of the double-layer plate together. The insulation sound-absorbing decorative plate does not contain asbestos, benzene and formaldehyde which are harmful to human body, light pollution of a matte series product can be avoided, and the production technology enables environmental protection.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a thermal insulation and sound-absorbing decorative board and a preparation method thereof. Background technique [0002] At present, materials such as white paint, latex paint, and paint are mostly used for the exterior and interior walls of buildings, all of which contain formaldehyde, which is not conducive to human health; the cement sand required for tile bonding is not environmentally friendly, and bricklayers are required for construction, which is expensive and not available. The function of heat preservation and sound absorption. Contents of the invention [0003] Aiming at the above-mentioned technical problems of existing architectural decorative panels, the present invention provides a thermal insulation and sound-absorbing decorative panel and its preparation method, which is made of formaldehyde-free materials through air-laid, composite pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/12B32B7/12B32B37/02B32B37/12B32B37/10
Inventor 褚乃博赵惠宏寇骞陈齐栾凤昌赵明
Owner LIAOYANG YIMENG CARPET MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap