Titanium-containing cored wire and its application, titanium alloyed molten steel and its preparation method, and a titanium-containing alloy steel

A technology of titanium alloy steel and cored wire, which is applied in the field of titanium alloyed molten steel and its preparation, and titanium-containing alloy steel, can solve the problem of little research on titanium cored wire, etc., and achieves high yield strength and tensile strength. The effect of stable recovery and high recovery

Active Publication Date: 2015-09-30
SICHUAN PAN YAN TECH
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] It can be seen that the core material of the cored wire studied in the prior art is mainly calcium, niobium, vanadium, boron and other elements, but there is little research on the cored wire containing titanium

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Titanium-containing cored wire and its application, titanium alloyed molten steel and its preparation method, and a titanium-containing alloy steel

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] The invention provides a method for preparing titanium alloyed molten steel, which comprises: feeding the titanium-containing cored wire described in the invention into molten steel to be titanium alloyed for titanium alloying.

[0043] According to the preparation method of the present invention, preferably, the molten steel to be alloyed with titanium is molten steel that has been alloyed with carbon, silicon and manganese, and the temperature of the molten steel to be alloyed with titanium is 1550-1600°C.

[0044] According to the preparation method of the present invention, in order to facilitate the rapid feeding of the cored wire into molten steel, and at the same time in order to improve the yield strength and tensile strength of the titanium alloy steel, titanium alloying is preferably carried out under dynamic conditions. Shaking or turning can be realized, for example, the steel ladle can be shaken while the cored wire is fed into the molten steel in the ladle ...

Embodiment 1

[0057] A cored wire A1 (with an outer diameter of 12mm), including an inner sheath, an outer sheath, and aluminum powder (brand FLG3, particle size ≤ 2mm, Al content of 98.2% by weight, the balance <0.5% by weight of Si, <0.5% by weight of Si Fe, <0.05% by weight of S, etc.) and ferrotitanium powder (grade FeTi70, particle size ≤ 1.5mm, containing 67% by weight of Ti, <0.5% by weight of C, <0.05% by weight of S, and the balance being Fe), Both the outer skin (thickness 1.75mm) and the inner skin (thickness 1mm) are made of cold-rolled strip steel (brand St12), the inner skin is wrapped with the titanium-iron powder, and the aluminum powder is filled between the inner skin and the outer skin. The weight ratio of titanium iron powder and aluminum powder is 10:1.

Embodiment 2

[0059] A cored wire A2 (outer diameter 12mm), including inner sheath, outer sheath, aluminum powder (brand FLG3, particle size ≤ 1.3mm, Al content 98.2% by weight, Si less than 0.5% by weight, < 0.5% by weight Fe, <0.05% by weight of S, etc.) and ferrotitanium powder (grade FeTi60, particle size ≤ 1.5mm, containing 58% by weight of Ti, <0.5% by weight of C, <0.05% by weight of S, the balance is Fe) , the outer skin (thickness 2mm) and inner skin (thickness 1.2mm) are made of cold-rolled strip steel (brand St12), the inner skin is wrapped with the titanium iron powder, and the aluminum powder is filled between the inner skin and the outer skin, The weight ratio of the ferrotitanium powder to the aluminum powder is 6:1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a titanium-containing core-spun yarn which comprises an inner sheath, an outer sheath, aluminum powder and titanium-iron powder, wherein the inner sheath is wrapped outside the titanium-iron powder, and the aluminum powder is filled between the inner sheath and the outer sheath. The invention provides application of the titanium-containing core-spun yarn in preparing titanium alloying molten steel. The invention provides a preparation method of the titanium alloying molten steel, which comprises the following steps: feeding the titanium-containing core-spun yarn into molten steel to be subjected to titanium alloying, and carrying out titanium alloying. The invention provides a titanium alloying molten steel prepared by the method. The invention provides a titanium-containing alloy steel which is prepared by casting the titanium alloying molten steel. In the preferable embodiment, the core-spun yarn is used for implementing titanium alloying of molten steel, and the titanium recovery rate is high and stable (80-85%), thereby effectively enhancing the quality of the molten steel.

Description

technical field [0001] The invention relates to a titanium-containing cored wire and its application in molten steel titanium alloying, a titanium-alloyed molten steel and a preparation method thereof, and a titanium-containing alloy steel. Background technique [0002] In order to ensure the various physical and chemical properties of steel, it is necessary to add alloy additives to the steel to adjust its composition to the specified range. Elements (C, Si, Mn, S or P) that are not present in ordinary steel or have a small content are all alloying elements. Alloy additives can be pure materials (nickel, copper, aluminum, graphite powder, etc.), ferroalloys (ferromanganese, ferrosilicon, ferrovanadium, ferrotitanium, etc.), or compounds of alloying elements (oxides, carbides, etc.) substances, nitrides, etc.). [0003] Ni, Mo, Cu, Co and other elements have low affinity with oxygen, so they can be added together with the charge or during the smelting process; while Ti, V,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C21C7/00C22C33/04
Inventor 陈炼王建戈文荪常军徐权李龙曾建华蒋龙奎张开华
Owner SICHUAN PAN YAN TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap