Cored wire, its application, vanadium and nitrogen alloyed molten steel, preparation method of vanadium and nitrogen alloyed molten steel, and vanadium and nitrogen micro-alloyed steel

A vanadium-nitrogen alloy and cored wire technology is applied in the fields of cored wire and its application, vanadium-nitrogen alloyed molten steel and its preparation, and vanadium-nitrogen microalloyed steel, achieving stable recovery rate, high yield strength and tensile strength , the effect of high recovery rate

Active Publication Date: 2014-09-17
SICHUAN PAN YAN TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method has certain limitations in the application of some varieties with higher nitrogen content requirements, because the nitrogen content of this kind of vanadium nitride cored wire is subject to the ratio of nitrogen and vanadium in the vanadium nitrogen alloy, and the vanadium in the existing products Nitrogen alloys usually have three grades of VN12, VN14 and VN16. Generally, the ratios of nitrogen and vanadium of the three grades are 12:78(N:V); 14:78(N:V); 16:78(N: V)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cored wire, its application, vanadium and nitrogen alloyed molten steel, preparation method of vanadium and nitrogen alloyed molten steel, and vanadium and nitrogen micro-alloyed steel
  • Cored wire, its application, vanadium and nitrogen alloyed molten steel, preparation method of vanadium and nitrogen alloyed molten steel, and vanadium and nitrogen micro-alloyed steel

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The invention provides a method for preparing vanadium-nitrogen alloyed molten steel. The method comprises: feeding the cored wire of the invention into molten steel to be vanadium-nitrogen alloyed for vanadium-nitrogen alloying.

[0033] According to the preparation method of vanadium-nitrogen alloyed molten steel of the present invention, in order to facilitate the rapid feeding of the cored wire into the molten steel, and at the same time in order to improve the yield strength and tensile strength of the vanadium-nitrogen micro-alloyed steel, it is preferable to carry out the vanadium-nitrogen alloying process , Carry out vanadium nitrogen alloying under dynamic conditions, dynamic conditions can be achieved by shaking or rotating the ladle, for example, the ladle can be shaken while the cored wire is fed into the molten steel in the ladle through the wire feeding device.

[0034] According to the preparation method of vanadium-nitrogen alloyed molten steel of the pre...

Embodiment 1

[0049] A cored wire A1 (with an outer diameter of 12mm), including a core layer and an outer layer wrapping the core layer. The core layer is made of vanadium nitrogen alloy, ferrosilicon nitride, titanium iron alloy and iron calcium alloy The diameter is less than 2mm), and the outer layer is a skin made of cold-rolled steel strip (brand St12), wherein, the powder contains vanadium-nitrogen alloy (VN16, vanadium content 78% by weight, N content 16% by weight): 94 % by weight, ferrosilicon nitride (36% by weight of N content, 52% by weight of Si content): 4% by weight, ferro-titanium alloy: 1% by weight, iron-calcium alloy (30% by weight of Ca content, the rest is Fe and not Other impurity elements to avoid): 1% by weight, ferro-titanium alloy is FeTi40 (Ti content is 40% by weight, the rest is Fe and other impurity elements that are unavoidable).

Embodiment 2

[0051] A cored wire A2 (with an outer diameter of 12 mm), including a core layer and an outer layer wrapping the core layer, the core layer is made of powder (granule grains) of vanadium nitrogen alloy, ferrosilicon nitride, ferrotitanium alloy and iron calcium alloy The diameter is less than 3mm), and the outer layer is a skin made of cold-rolled strip steel (brand St12), wherein, the powder contains vanadium-nitrogen alloy (VN16, vanadium content 78% by weight, N content 16% by weight): 51 % by weight, ferrosilicon nitride (N content is 36% by weight, Si content is 52% by weight): 9% by weight, ferro-titanium alloy: 25% by weight, calcium iron alloy (the content of Ca is 30% by weight, the rest is Fe and not Avoided other impurity elements): 15% by weight, ferro-titanium alloy is FeTi40 (Ti content is 40% by weight, the rest is Fe and other unavoidable impurity elements).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a cored wire and its application. The cored wire comprises a core layer and an external layer wrapping the core layer, wherein the core layer is a mixture containing a vanadium-nitrogen alloy, iron silicon nitride, a titanium-iron alloy and an iron-calcium alloy. The invention also provides a vanadium and nitrogen alloyed molten steel, and a preparation method thereof. The method comprises the steps of feeding the cored wire into molten steel to be vanadium and nitrogen alloyed, and carrying out vanadium and nitrogen alloying. The invention further provides a vanadium and nitrogen micro-alloyed steel. The vanadium and nitrogen micro-alloyed steel is obtained by casting the vanadium and nitrogen alloyed molten steel. The cored wire can be used for realizing the alloying of molten steel vanadium and nitrogen, can effectively increase the oxygen content as needed without influencing the vanadium content, enables vanadium-containing steel with a higher content of nitrogen to be produced as needed, and can realize high and stable nitrogen recovery rate.

Description

technical field [0001] The invention relates to a cored wire and its application in vanadium-nitrogen alloying of molten steel, a vanadium-nitrogen alloyed molten steel and a preparation method thereof, and a vanadium-nitrogen microalloy steel. Background technique [0002] Vanadium-nitrogen alloy is a new alloy additive that can replace ferrovanadium for the production of microalloyed steel. The addition of vanadium nitrogen alloy to steel can improve the comprehensive mechanical properties of steel such as strength, toughness, ductility and thermal fatigue resistance, and make the steel have good weldability. When the same strength is achieved, the addition of vanadium nitride saves 30-40% of the amount of vanadium added, thereby reducing the cost. Vanadium nitrogen alloys can be used in structural steel, tool steel, pipe steel, steel bars and cast iron. The application of vanadium-nitrogen alloys in high-strength low-alloy steels can effectively micro-alloy vanadium and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C33/06C22C35/00
Inventor 刘明张国才王建程兴德王义成罗开金
Owner SICHUAN PAN YAN TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com