Water-resistant magnesium oxysulfate fire-proof plate and manufacturing method thereof

A technology of fireproof board and magnesium oxysulfide, which is applied in the field of fireproof board production, can solve problems such as the inability to meet the application requirements of construction projects, achieve high strength and safety, and expand the scope of application.

Inactive Publication Date: 2014-08-13
SHANDONG PROVINCIAL ACAD OF BUILDING RES
View PDF3 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are big problems in the strength and waterproof performance of traditional magnesium oxysulfide cement, which cannot meet the application requirements of construction projects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-resistant magnesium oxysulfate fire-proof plate and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Mix the raw materials in the following mass percentages evenly to obtain the modifier (magnesium oxysulfate water resistance enhancer) of the present invention:

[0027] Silica fume 10%

[0028] Silicone water repellent powder 20%

[0029] Sucrose 38%

[0030] Humic Acid 32%.

Embodiment 2

[0032] Slurry formula:

[0033] Lightly burned magnesia powder 100kg Magnesium sulfate solution (density is 1.22g / cm 3 ) 111kg

[0034] Magnesium oxysulfide anti-water enhancer 1kg Talc powder (325 mesh) 30kg

[0035] Closed-cell perlite (30 mesh size) 5kg

[0036] Reinforcement material: medium alkali glass fiber cloth (close to the slurry) and non-woven fabric (close to the surface)

[0037] The decorative veneer is wood veneer, and the bonding material is white latex.

[0038] Production steps:

[0039] a. Preparation of modified magnesium oxysulfide cement slurry

[0040] Add light-burned magnesium oxide powder into the magnesium sulfate solution, mix and stir evenly, and add magnesium oxysulfate water-resistant enhancer to obtain a clean slurry; mix the clean slurry with talcum powder and closed-cell perlite at a stirring speed of 70 rpm, and stir Obtain the modified magnesium oxysulfide cement slurry after uniformity;

[0041] b. Spread the slurry obtained in step...

Embodiment 3

[0046] Slurry formula:

[0047] Lightly burned powder 100kg Magnesium sulfate solution (density 1.22g / cm 3 ) 114kg

[0048] Magnesium oxysulfate anti-water enhancer 1kg fly ash (200 mesh) 30kg

[0049] Closed-cell perlite (30 mesh size) 5kg

[0050] Reinforcement material: medium alkali fiberglass cloth (close to the slurry) and non-woven fabric (close to the surface).

[0051] The decorative veneer is PVC veneer, and the bonding material is one-component polyurethane glue.

[0052] Except that the active packing used is different, the manufacturing steps are the same as in Example 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a water-resistant magnesium oxysulfate fire-proof plate and a manufacturing method thereof and belongs to the field of fire-proof plate production. The fire-proof plate is prepared by adding active filler into slurry, mixing, hardening under a certain condition and demoulding, wherein modified magnesium oxysulfate is taken as a base material and medium-alkali glass fiber and non-woven fabrics and other materials are taken as a skeleton. Compared with the prior art, the fire-proof door core plate disclosed by the invention has no moisture absorption, higher durability than a conventional glass magnesium plate and smooth and beautiful appearance. The fire-proof plate can be applied to the field of building fire protection, especially fire protection engineering under a humid environment and has a good popularization and application value.

Description

[0001] technical field [0002] The invention relates to the field of fireproof board production, in particular to a water-resistant magnesium oxysulfide fireproof board and a manufacturing method thereof. Background technique [0003] Glass magnesium fireproof board is one of the most widely used fireproof boards at present. It is a new type of non-combustible building compounded with magnesite cementitious material as base material, medium alkali glass fiber cloth as reinforcement material and light material as filler. sheet. It can be used as thermal insulation building wall panels, door core panels, ceiling panels, packing boxes, etc., and can replace wooden plywood to make dado, door and window frames, furniture, etc. The surface can also be painted with blending paint and clear water paint according to needs, and can be processed into various types of board surfaces. It can also be used in simple fire prevention projects in damp environments such as basements and min...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/30C04B111/28
Inventor 王自福崔洪涛陈俊薇刘亚丽王翔靳路通
Owner SHANDONG PROVINCIAL ACAD OF BUILDING RES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap