A technology of nail polish and light curing, which is applied in manicure, cosmetics, pedicure, etc. It can solve the problems of poor flexibility and brittle nails, achieve moderate adhesion, prevent damage, and avoid auxiliary peeling effects

Inactive Publication Date: 2014-09-10
ZHANGJIAGANG MAOAN TRADING
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention overcomes the problem that there are many UV light-cured nail polish products currently on the market in the prior art, but their flexibility is poor, which easily leads to the brittleness of the nail plate, and the adhesion is too strong to be easily peeled off from the nail. Provides a UV light-curable blue nail polish with moderate adhesion, which can meet the adhesion effect on the nail, and can be easily peeled off from the nail, avoiding the use of organic solvents for auxiliary peeling, and effectively preventing the peeling solvent from affecting the skin. nail injury

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of UV photocurable blue nail polish, in each component and each component weight percent content is:

[0022] Urethane Acrylate 55%

[0023] Trimethylolpropane Triacrylate 20%

[0024] Epoxy Acrylate 15

[0025] The initiator is 11734%

[0026] Blue Pigment 5%

[0027] Polyether modified silicone 1%.

[0028] The preparation method of UV photocurable blue nail polish, comprises the steps:

[0029] Step 1) take by weighing each component of UV photocurable blue nail polish in proportion,

[0030] Step 2) Stir the components in step 1) evenly, and the speed of the mixer is 1000 rpm to obtain UV light-curable blue nail polish;

[0031] Step 3) packaging and labeling.

Embodiment 2

[0033] A kind of UV photocurable blue nail polish, in each component and each component weight percent content is:

[0034] Urethane Acrylate 35%

[0035] Trimethylolpropane Triacrylate 35%

[0036] Epoxy Acrylate 20

[0037] 9075%

[0038] Blue Pigment 4%

[0039] Polyester modified silicone 1%.

[0040] The preparation method of UV photocurable blue nail polish, comprises the steps:

[0041] Step 1) take by weighing each component of UV photocurable blue nail polish in proportion,

[0042] Step 2) Stir the components in step 1) evenly, and the speed of the mixer is 1800 rpm to obtain UV light-curable blue nail polish;

[0043] Step 3) packaging and labeling.

Embodiment 3

[0045] A kind of UV photocurable blue nail polish, in each component and each component weight percent content is:

[0046] Urethane Acrylate 55%

[0047] Trimethylolpropane Triacrylate 20%

[0048] Epoxy Acrylate 20

[0049] 1173 and 9073%

[0050] Blue Pigment 1%

[0051] Polyacrylate 1%.

[0052] The preparation method of UV photocurable blue nail polish, comprises the steps:

[0053] Step 1) take by weighing each component of UV photocurable blue nail polish in proportion,

[0054] Step 2) Stir the components in step 1) evenly, and the speed of the mixer is 1200 rpm to obtain UV light-curable blue nail polish;

[0055] Step 3) packaging and labeling.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of printing ink and particularly relates to UV photocuring blue nail polish. The UV photocuring blue nail polish comprises the following components in percentage by weight: 35-55% of polyurethane acrylate, 20-35% of trimethylolpropane triacrylate, 15-20% of epoxy acrylate, 3-5% of a photoinitiator, 1-5% of an indigo dye and 0.5-1% of a flatting agent. The UV photocuring blue nail polish provided by the invention is moderate in adhesive force, can satisfy the adhering effect on nails and can be easily stripped from the nails, and assistant stripping due to addition of an organic solvent is avoided, so that the damage of a stripping solution on the nails is effectively prevented.

Description

technical field [0001] The invention relates to the technical field of inks, in particular to a UV photocurable blue nail polish. Background technique [0002] Nail polish is a large category of products in the make-up series, which has the function of beautifying and modifying nails. Ordinary nail polish is a nail film-forming agent in which ester-soluble nitrocellulose is dissolved in a certain high-activity ester-based solvent system. % of nitrocellulose, a small amount of oily solvents, camphor, titanium dioxide, and oil-soluble pigments. The film formed after the nail polish is applied to the nails is firm and has a moderately colored luster, which can protect the nails and give them a sense of beauty. [0003] There are many UV light-curable nail polish products on the market, but their flexibility is poor, which easily leads to brittle cracks of the nail plate, and the adhesion is too strong, so it is not easy to peel off from the nail. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/891A61K8/89A61K8/87A61Q3/02
Inventor 徐靖
Owner ZHANGJIAGANG MAOAN TRADING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap