Manufacture method for flexible large-area high-heat-power electrothermal film

A production method and large-area technology, applied in the direction of electric heating devices, electrical components, heating by discharge, etc., can solve the problems of large initial investment, limited heating power, troubles, etc., and achieve large contact area, fast heat generation and heat dissipation, and heat transfer effect Good results

Inactive Publication Date: 2014-11-19
ZHEJIANG GONGSHANG UNIVERSITY
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Cable heating technology and electrothermal film technology are also gradually used in the heating field. Compared with the current electric heating film technology, the initial investment of cable heating technology is also large, and the construction is troublesome; while the electric heating film technology takes too long to warm up and heats up. The power is limited, and there are certain restrictions on the application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacture method for flexible large-area high-heat-power electrothermal film
  • Manufacture method for flexible large-area high-heat-power electrothermal film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Such as figure 1 and figure 2 As shown, the flexible large-area high-heating power electric heating film of the present invention is a rectangle, and it comprises an electric heating film 1, a copper electrode 2 and a sealing insulator 3; firstly, the conductive film is prepared, and 10g of carbon black particles are added to 100g of naphtha In the solvent, after ultrasonic dispersion is uniform, add 100g of silicone rubber and stir evenly, then add 4g of curing agent; inject the mixed solution into the mold at room temperature for 48 hours to cure and form an electric heating film; finally, conductively bond the conductive film to the copper electrode and use insulating polymer Ester film sealing treatment, the electric heating film is first pasted on a polyester film, and then another polyester film is pasted on the upper surface. After the adhesive is cured, a complete flexible large-area high-heating power electric heating is obtained. film. When using, just conn...

Embodiment 2

[0018] Such as figure 1 and figure 2 As shown, the flexible large-area high-heating power electric heating film of the present invention is a rectangle, and it includes an electric heating film 1, a copper electrode 2 and a sealing insulator 3; firstly, the conductive film is prepared, and 15g of carbon black particles are added to 150g of naphtha In the solvent, after ultrasonic dispersion is uniform, add 100g of silicone rubber and stir evenly, then add 4g of curing agent; inject the mixed solution into the mold at room temperature for 48 hours to cure and form an electric heating film; finally, conductively bond the conductive film to the copper electrode and use insulating polymer Ester film sealing treatment, first paste the electric heating film on a polyester film, and then paste another polyester film on the upper surface. After the adhesive is cured, a complete flexible large-area high-heating power electric heating is obtained. film. When using, just connect the c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Disclosed is a manufacture method for a flexible large-area high-heat-power electrothermal film. The electrothermal film comprises a conductive film, a copper electrode and an insulation film protective layer. The electrothermal film is prepared by use of a carbon black/silicone rubber conductive composite material. The film has the advantages of flexibility and large area; the electrothermal film has the advantages of uniform heating and high heat power after being energized; and the electrothermal film is in the shape of a large-area film, has the advantages of large heat dissipation area and good heat-transfer property and can be fully contacted with a heated body for heat transfer. The electrotehrmal film provided by the invention can be used for indoor heating in a building and has the advantages of simple installation, relatively low initial investment, rapid heating and the like, thereby having a certain application value.

Description

technical field [0001] The invention relates to the field of electric heating, in particular to a large-area electric heating film heating technology. Background technique [0002] At present, there are many materials and methods that can be used for electric heating. According to the different ways of electric energy conversion, electric heating is usually divided into resistance heating, induction heating, arc heating, electron beam heating, infrared heating and medium heating. At present, the electric heating methods used for building indoor heating mainly include the use of heating cables arranged in the concrete under the floor or carbon fiber mixed into the cement mortar to make it conductive to obtain electric heating performance. This technology is still mainly in the research stage; At present, the electrothermal film appearing on the market is made of conductive special ink and metal current-carrying strips, which are processed and hot-pressed between insulating po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H05B7/02
Inventor 廖波韦影吴娟陈学光
Owner ZHEJIANG GONGSHANG UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap