High strength thin steel sheet excelling in weldability and process for producing the same

一种薄钢板、高强度的技术，应用在高强度薄钢板及其制造领域，能够解决加工性降低、高强度冷轧特性降低等问题，达到高抗拉强度、优良镀覆特性的效果

Inactive Publication Date: 2015-06-24
POHANG IRON & STEEL CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the case of manufacturing a steel sheet having a high strength of 800 MPa or more in an actual process, the cold rolling characteristics are significantly lowered due to the high strength of the hot strip as an intermediate material
In addition, since the heat treatment conditions of rapid cooling should be used in the annealing process, the workability is also significantly reduced
Japanese Patent Laid-Open No. 2005105367 does not fully consider these issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High strength thin steel sheet excelling in weldability and process for producing the same
  • High strength thin steel sheet excelling in weldability and process for producing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A steel plate comprising: 0.02%-0.20% C; 1.5% or less Si; 1.5%-3.0% Mn; 0.001%-0.10% P; 0.010% or less S; %-0.40% of acid-soluble aluminum (Sol.Al); 0.020% or less of N; 0.3%-1.5% of Cr; 0.0010%-0.0060% of B; 0.001%-0.10% of Sb; At least one material selected from the group consisting of 0.003%-0.08% of Ti, 0.003%-0.08% of Nb, and 0.003%-0.08% of Mo; including iron and other unavoidable impurities as a balance, and Si, Mn, B, Sb, P and S satisfy the conditions of 5<(Si / Mn+150B) / Sb<20 and C+Mn / 20+Si / 30+2P+4S<0.27.

[0016] In addition, a method for manufacturing the steel plate includes: heating a slab of the steel plate, and 3 Rolling and coiling a slab at a temperature between the transition point and the finish rolling exit side of 950° C., the slab of the steel plate comprising 0.02% to 0.20% of C, 1.5% or less of Si, 1.5% by weight percentage %-3.0% Mn, 0.001%-0.10% P, 0.010% or less S, 0.01%-0.40% acid-soluble aluminum (Sol.Al), 0.020% or less N, 0.3%-1.5 % Cr, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
Login to View More

Abstract

Provided are a high strength thin steel sheet having tensile strength of about 800 MPa or more, and a manufacturing method thereof. The thin steel sheet is mainly used for construction materials, home appliances, and automobiles. The thin steel sheet has excellent plating characteristic, welding characteristic, bending workability, and hole expansion ratio. The thin steel sheet includes, in weight %, C: 0.02-0.20%, Si: 1.5% or less, Mn: 1.5-3.0%, P: 0.001-0.10%, S: 0.010% or less, SoLAl: 0.01-0.40%, N: 0.020% or less, Cr: 0.3-1.5%, B: 0.0010-0.0060%, Sb: 0.001-0.10%, and including at least one material selected from the group consisting of Ti: 0.003-0.08%, Nb: 0.003-0.08%, and Mo: 0.003-0.08%, and includes Fe and other inevitable impurities as a remainder. Here, Si, Mn, B, Sb, P, and S meet conditions of 5<(Si / Mn+150B) / Sb<20 and C+Mn / 20+Si / 30+2P+4S<0.27. Also, the manufacturing method can secure workability of the thin steel sheet.

Description

[0001] This application is a branch of a PCT patent application with a priority date of December 28, 2007 and an application number of 200880123092.5 filed on August 8, 2008, entitled "High-strength thin steel plate with excellent weldability and its production process". case application. technical field [0002] The present invention relates to a high-strength thin steel sheet having a tensile strength of about 800 MPa or more, which is mainly used for building materials, home appliances, and automobiles, and a manufacturing method thereof, and more particularly, to a steel sheet having excellent plating characteristics. , weldability, bending workability, hole expansion ratio (HER), and high tensile strength high-strength thin steel plate and a manufacturing method thereof. Background technique [0003] Recently, steel sheets for automobiles are required to have higher strength in order to improve fuel economy or durability. In consideration of collision safety and passen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/60C21D8/02
CPCC22C38/06C22C38/32C22C38/38C22C38/60C21D8/0226C21D8/0236C22C38/24C22C38/26C22C38/28C21D2211/002C21D2211/005
Inventor 康熙宰吴振根陈光根金钟常
Owner POHANG IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com