Absorbable suture line and method for preparing the same

A technology of suture and collagen, which is applied in medical science, surgery, surgical instruments, etc., can solve the problems of high cost and slow absorption, and achieve the effect of low cost, stable and reliable absorption, and good biocompatibility

Inactive Publication Date: 2015-09-30
SUZHOU JONATHAN NEW MATERIALS TECH
View PDF11 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Technical problem to be solved: the present invention provides an absorbable suture and its preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0025] Example 1:

[0026] An absorbable suture thread, which is mainly made of the following raw materials according to the mass ratio: 24 parts of collagen, 23 parts of silk protein, 12 parts of silk fibroin, 13 parts of sericin, 12 parts of glycolic acid, 11 parts of lactic acid, and poly 2 parts of glycolide, 6 parts of polylactide, 4 parts of polyglycolide lactide, 1 part of sodium carbonate, 40 parts of deionized water.

[0027] A method for preparing absorbable sutures includes the following steps:

[0028] (1) Dissolve sodium carbonate in deionized water to prepare the base solution, the mass concentration of sodium carbonate is 3%;

[0029] (2) Dissolve collagen, silk protein, silk fibroin and sericin in the base solution obtained in step (1), and stir until completely dissolved;

[0030] (3) Put glycolic acid, lactic acid, polyglycolide, polylactide, and polyglycolide lactide in a reaction kettle, and make a melt under the conditions of a temperature of 230°C and a pressure o...

Example Embodiment

[0033] Example 2:

[0034] An absorbable suture thread, which is mainly made of the following raw materials according to the mass ratio: 48 parts of collagen, 46 parts of silk protein, 21 parts of silk fibroin, 18 parts of sericin, 16 parts of glycolic acid, 22 parts of lactic acid, and poly 11 parts of glycolide, 17 parts of polylactide, 12 parts of polyglycolide lactide, 5 parts of sodium carbonate, 60 parts of deionized water.

[0035] A method for preparing absorbable sutures includes the following steps:

[0036] (1) Dissolve sodium carbonate in deionized water to prepare the base solution, the mass concentration of sodium carbonate is 6%;

[0037] (2) Dissolve collagen, silk protein, silk fibroin and sericin in the base solution obtained in step (1), and stir until completely dissolved;

[0038] (3) Put glycolic acid, lactic acid, polyglycolide, polylactide and polyglycolide lactide in a reaction kettle, and make a melt under the conditions of a temperature of 325℃ and a pressure...

Example Embodiment

[0041] Example 3:

[0042] An absorbable suture thread, which is mainly made of the following raw materials according to the mass ratio: 55 parts of collagen, 56 parts of silk protein, 27 parts of silk fibroin, 23 parts of sericin, 30 parts of glycolic acid, 28 parts of lactic acid, and poly 14 parts of glycolide, 20 parts of polylactide, 16 parts of polyglycolide lactide, 7 parts of sodium carbonate, 65 parts of deionized water.

[0043] A method for preparing absorbable sutures includes the following steps:

[0044] (1) Dissolve sodium carbonate in deionized water to prepare the base solution, the mass concentration of sodium carbonate is 8%;

[0045] (2) Dissolve collagen, silk protein, silk fibroin and sericin in the base solution obtained in step (1), and stir until completely dissolved;

[0046] (3) Put glycolic acid, lactic acid, polyglycolide, polylactide, and polyglycolide lactide in a reactor, and make a melt under the conditions of a temperature of 360°C and a pressure of 2....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an absorbable suture line and a method for preparing the same. The absorbable suture line is mainly prepared from, by mass parts, 24-55 parts of collagen, 23-56 parts of silk protein, 12-27 parts of fibroin, 13-23 parts of sericin, 12-30 parts of glycolic acid, 11-28 parts of lactic acid, 2-14 parts of polyglycolide, 6-20 parts of polylactide, 4-16 parts of poly glycolide-co-lactide, 1-7 parts of sodium carbonate and 40-65 parts of deionized water. The absorbable suture line has the advantages that the absorbable suture line prepared according to the scheme is high in degree of fusion with the human body, can be completely absorbed by the human body, is absorbed stably and reliably, causes no obvious individual difference and is free of toxic and side effects; the absorbable suture line prepared according to the scheme is high in tensile strength and good in biocompatibility and promotes cell growth; and the absorbable suture line prepared according to the scheme has convenience in material taking and is low in cost.

Description

technical field [0001] The invention relates to the field of medical biomaterials, in particular to an absorbable suture and a preparation method thereof. Background technique [0002] Surgical sutures refer to special threads used for suturing hemostasis and tissue suturing in surgical operations or in trauma treatment. Generally, it can be divided into two categories: absorbable sutures and non-absorbable sutures: absorbable sutures can be divided into catgut, chemically synthesized sutures, and pure natural collagen sutures according to the material and degree of absorption. [0003] Sheep catgut is made from healthy animal sheep intestines and contains collagen, so there is no need to remove the sutures after suturing. There are two types of medical gut: common gut and chrome gut, both of which can be absorbed. The length of time required for absorption depends on the thickness of the gut and the condition of the tissue. Generally, it can be absorbed within 6 to 20 day...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L17/12A61L17/10
Inventor 吕少波李卓才李苏杨
Owner SUZHOU JONATHAN NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap