epdm flame retardant sponge sealing strip for high-speed rail

A technology of sealing strip and sponge, applied in the field of rubber products, can solve the problem that there are not many flame retardant sponge products, and achieve the effects of good material performance, fast vulcanization speed, and meeting the requirements of flame retardant

Active Publication Date: 2018-04-03
TIANJIN XINZHONGHE RUBBER IND
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the demand for flame-retardant products in the market is increasing, but there are not many flame-retardant sponge products, and it is also a technical problem that many people are studying but cannot effectively solve.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • epdm flame retardant sponge sealing strip for high-speed rail
  • epdm flame retardant sponge sealing strip for high-speed rail
  • epdm flame retardant sponge sealing strip for high-speed rail

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] EPDM flame-retardant foam sealing strip for high-speed rail, the components and mass parts are as follows:

[0018]

[0019] After testing, the density and flame-retardant properties of the EPDM flame-retardant foam sealing strip for high-speed rail prepared in Example 1: The density is 0.65g / cm 3 , Self-extinguishing 6 seconds away from the fire, a lot of smoke is emitted.

Embodiment 2

[0021] EPDM flame-retardant foam sealing strip for high-speed rail, the components and mass parts are as follows:

[0022]

[0023] After testing, the density and flame-retardant performance of the EPDM flame-retardant foam sealing strip for high-speed rail prepared in Example 2: Density 0.5g / cm 3 , Self-extinguishing from the fire, a trace of smoke came out.

Embodiment 3

[0025] EPDM flame-retardant foam sealing strip for high-speed rail, the components and mass parts are as follows:

[0026]

[0027]

[0028] After testing, the density and flame-retardant performance of the EPDM flame-retardant foam sealing strip for high-speed rail prepared in Example 3: density 0.6g / cm 3 , 3 seconds away from the fire, self-extinguishing, a small amount of smoke comes out.

[0029] It should be noted that the components in Examples 1-3 are commercially available products, and the sources are as follows:

[0030]

[0031] Antimony trioxide, aluminum hydroxide, and chlorinated paraffin were purchased from Hunan Yiyang, Jinan Taixing, and Anming Hengxin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an EPDM flame-retardant sponge sealing strip for a high-speed rail. The EPDM flame-retardant sponge sealing strip comprises the following components in parts by mass: 100 parts of high-ENB-content EPDM (ethylene propylene diene monomer), 50 to 70 parts of fast extruding furnace black, 30 to 50 parts of inert filler, 140 to 160 parts of flame-retardant agent, 60 to 80 parts of high-flash-point paraffin oil, 1 to 2 parts of anti-aging agent TMQ, 6 to 8 parts of activated zinc oxide, 1 to 3 parts of stearic acid, 1 to 3 parts of polyethylene glycol, 1 to 3 parts of flow additive, 1 to 2 parts of vulcanizing agent, 4 to 6 parts of accelerant and 4 to 6 parts of foaming agent. By adopting the flame-retardant sponge formula, a better material performance can be obtained, the density is 0.5 to 0.6 g / cm<3>, the flame-retardant grade reaches a burning-resisting grade, and the requirement of the high-speed rail sponge sealing strip on light weight and flame retardant property can be met.

Description

Technical field [0001] The invention relates to the technical field of rubber products, in particular to an EPDM flame-retardant sponge sealing strip for high-speed rail. Background technique [0002] The EPDM flame-retardant foam sealing strip for high-speed rail mainly refers to the sealing strip used in the high-speed rail sealing system. The sealing strip is manufactured by an extrusion process and the material is high ENB content D EPDM (EPDM 547). The sealing strip works in high-speed trains. In addition to the conventional anti-aging and ozone performance, it also needs high flame retardant performance to prevent fire when encountering open flames. At present, there is an increasing demand for flame-retardant products in the market, but there are not many flame-retardant sponge products. It is also a technical problem that many people are studying but cannot effectively solve. Summary of the invention [0003] The purpose of the present invention is to provide an EPDM flam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C08L23/16C08L91/06C08L71/02C08K13/02C08K3/04C08K3/22C08K5/09C08K3/26C08K3/06C08J9/04
CPCC08J9/0061C08J9/04C08J2323/16C08L23/16C08L2201/02C08L2203/14C08L2205/025C08L2205/035C08L91/06C08L71/02C08K13/02C08K3/04C08K2003/2296C08K5/09C08K2003/265C08K3/2279C08K2003/2227C08K3/06
Inventor孙贵元
OwnerTIANJIN XINZHONGHE RUBBER IND