Artificial tooth polishing method

A technology for dentures and tongue tips, which is applied in the field of oral restoration, can solve the problems of cumbersome and complicated denture polishing operations, and achieve good polishing effects, convenient handling, and short polishing time

Inactive Publication Date: 2016-07-06
CHENGDU BESMILE BIOTECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Therefore, prior art is loaded down with trivial details and complicated to the polishing operation of denture

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1: a kind of polishing method of denture, it comprises the following steps:

[0016] S1. Grinding: Use a whetstone to smooth the metal on the tip of the tongue, and use a rubber wheel and a rubber strip to polish it until the edge of the tip of the tongue is free of burrs or missing edges;

[0017] S2. Polishing: put the polished denture into the solution for soaking and polishing, the soaking and polishing time is 15min. The solvent includes an active component and a carrier component, wherein the active component is a mixed solvent of ammonia water and toluene; the carrier The component is methanol solvent, and the content of the active component is 30%.

Embodiment 2

[0018] Embodiment 2: a kind of polishing method of denture, it comprises the following steps:

[0019] S1. Grinding: Use a whetstone to smooth the metal on the tip of the tongue, and use a rubber wheel and a rubber strip to polish it until the edge of the tip of the tongue is free of burrs or missing edges;

[0020] S2. Polishing: put the polished denture into the solution for soaking and polishing. The time for soaking and polishing is 24 minutes. The solvent includes an active component and a carrier component, wherein the active component is a mixed solvent of ammonia, toluene, and ethylbenzene; The carrier component is a mixed solution of cyclohexanone and acetol, and the content of the active component is 40%.

Embodiment 3

[0021] Embodiment 3: a kind of polishing method of denture, it comprises the following steps:

[0022] S1. Grinding: Use a whetstone to smooth the metal on the tip of the tongue, and use a rubber wheel and a rubber strip to polish it until the edge of the tip of the tongue is free of burrs or missing edges;

[0023] S2. Polishing: put the polished denture into the solution for soaking and polishing, the soaking and polishing time is 18min. The solvent includes active components and carrier components, wherein the active components are ammonia water, toluene, ethylbenzene, o-xylene The mixed solvent; the carrier component is a mixed solution of ethanol, n-propanol and amyl alcohol, and the content of the active component is 32%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an artificial tooth polishing method. The artificial tooth polishing method includes the steps of S1, grinding, namely grinding tongue tip metal smoothly by a grinding stone, and polishing the smooth tongue tip metal to enable tongue tip edge to be free of burrs or edge notches by a rubber wheel and a rubber strip; S2, polishing, namely subjecting a ground artificial tooth to soaking polishing in a solution. Due to the fact that the artificial tooth is subjected to primary grinding and chemical soaking polishing, the artificial tooth polishing method is short in polishing time but good in polishing effect. The artificial tooth polishing method combining a mechanical method with a chemical method has the advantages of simplicity in operation, convenience in treatment and low cost, thereby being applicable to industrialized mass production.

Description

technical field [0001] The invention belongs to the technical field of oral restoration, and in particular relates to a method for polishing dentures. Background technique [0002] With the continuous improvement of living standards and aesthetic requirements, implant denture restoration has become an important part of oral restoration. A complete or partial denture is pocketed to replace lost teeth in the mouth. Typically, dentures are manufactured using a cast or mold with a liquid or slurry cast material distributed therein. After the denture is fully manufactured, it must be removed from the cast or model. Currently, the denture is removed from the casting by cutting away the hardened casting material, at this point the denture contains a very rough surface and chips and chips of the casting material stick to many areas of the denture, the denture is sandblasted with walnut chips to All residual material is removed, a process that may take about 15-30 minutes. The de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B24B1/00A61C13/08C09G1/14
CPCB24B1/00A61C13/08C09G1/14
Inventor 潘许松
Owner CHENGDU BESMILE BIOTECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap