Hydrophobic polylactic acid and starch compound fully-degradable plastic film and manufacturing method thereof

A technology of plastic film and polylactic acid, which is applied in the field of plastic film, can solve the problems of poor compatibility with polylactic acid, etc., and achieve the effect of improving interface contact effect and compatibility, increasing strength and toughness, and improving hydrophobicity

Inactive Publication Date: 2016-09-28
ANHUI MENGNIU COLOR PRINTING&PACKAGING
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the present invention, the silane coupling agent kh-550 is used to pretreat the hemp fiber, thereby improving the interface contact effect and compatibility, and improving the mechanical properties of the material; then modifying the cornstarch through a series of processes and adding In the overall product, it solves the problem of poor compatibility with polylactic acid, improves the strength and toughness of the composite material, and can greatly reduce the overall cost of the product. Finally, the hydrophobicity of the components is modified by adding white petrolatum and glyoxal. properties, so that the overall hydrophobicity of the film is improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] specific implementation plan

[0018] The present invention will be described in detail below through specific examples.

[0019] A fully degradable plastic film composited with hydrophobic polylactic acid and starch, prepared from the following raw materials in parts by weight (kg): polylactic acid 70, polypropylene carbonate 10, corn starch 20, glycerin 12, epichlorohydrin 1.6 , an appropriate amount of 1mol / L sodium hydroxide solution, an appropriate amount of 1mol / L hydrochloric acid, an appropriate amount of distilled water, hemp fiber 25, silane coupling agent kh-550 0.8, antioxidant 1010 1.5, white petrolatum 6, glyoxal 1;

[0020] A kind of hydrophobic polylactic acid and starch composite fully degradable plastic film described in the present invention is made by the following specific steps:

[0021] (1) Put the hemp fiber into a double amount of 1mol / L sodium hydroxide solution, heat it to 100°C under normal pressure, cook for 2.5 hours, take it out after coo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hydrophobic polylactic acid and starch compound fully-degradable plastic film, which is characterized by being made from the following raw materials, by weight part, 70-75 of polylactic acid, 10-12 of propylene carbonate, 20-25 of corn starch, 12-14 of glycerin, 1.6-2 of epichlorohydrin, a proper amount of a sodium hydroxide solution with the concentration being 1 mol / L, a proper amount of hydrochloric acid with the concentration being 1 mol / L, a proper amount of distilled water, 25-30 of hemp fibers, 0.8-1 of a silane coupling agent kh-550, 1.5-2 of an antioxidant 1010, 6-7 of white petrolatum and 1-2 of glyoxal. Components including polylactic acid, propylene carbonate, and white petrolatum are pre-mixed and subjected to inner mixing molding, and hydrophobic components can be fully uniformly dispersed, and therefore, surface hydrophobicity of the plastic film is improved and vapor permeability is reduced. The plastic film is low in cost and convenient to manufacture, and can be used as preservative films, food storage bags or food package bags.

Description

technical field [0001] The invention relates to the technical field of plastic films, in particular to a fully degradable plastic film composited with hydrophobic polylactic acid and starch and a preparation method thereof. Background technique [0002] In order to reduce the use of petroleum-based plastic materials, protect the environment, and alleviate the increasingly severe shortage of petroleum resources, the development and utilization of bio-based degradable and environmentally friendly plastic materials has become the focus of research in the field of packaging materials. [0003] Polylactic acid material is one of the most widely used degradable plastic materials at present. As a packaging film material, PLA has good transparency, mechanical properties and biocompatibility, high strength, thermoplasticity, easy molding and processing, and can be completely degraded. The product is non-toxic and harmless to the human body, comes from renewable resources, and is easy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L67/04C08L3/02C08L97/02C08L69/00C08K5/053C08K5/544C08K5/1515C08K5/134C08J5/18
CPCC08J5/18C08J2367/04C08J2403/02C08J2469/00C08J2497/02C08L67/04C08L2201/06C08L2203/16C08L2205/035C08L3/02C08L97/02C08L69/00C08K5/053C08K5/544C08K5/1515C08K5/134
Inventor 李峰郑志龙
Owner ANHUI MENGNIU COLOR PRINTING&PACKAGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products