Formula of colored glaze with high brightness

A technology of brightness and glaze, applied in the field of glazed formulations, can solve problems such as affecting the aesthetics of glazed handicrafts, affecting the value of glazed crafts, etc., and achieve the effects of superior finish, improved use value, and improved brightness.

Inactive Publication Date: 2016-12-21
太仓市科教新城琉璃艺术策划中心
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process can only be completed through dozens of manual operations, and a little negligence can cause failure or flaws, so its value is high, and the brightness of colored glaze directly affects the aesthetics of colored glaze handicrafts, and also directly affects the color of colored glaze. The value of handicrafts, the brightness of traditional glass can no longer meet the needs of people now

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A glass formula with high brightness, comprising the following components in parts by mass:

[0014] 30 parts of quartz sand, 10 parts of yellow sand, 3 parts of cerium oxide, 6 parts of aluminum oxide, 2 parts of flux, 3 parts of brightening agent;

[0015] The brightening agent is composed of beeswax and turpentine mixed, calculated according to mass percentage, the content of the beeswax accounts for 55%, and the content of the turpentine accounts for 45%;

[0016] The flux is made by mixing potassium nitrate and sodium nitrate. Calculated by mass percentage, the content of sodium nitrate accounts for 62%, and the content of potassium nitrate accounts for 38%.

Embodiment 2

[0018] A glass formula with high brightness, comprising the following components in parts by mass:

[0019] 50 parts of quartz sand, 15 parts of yellow sand, 5 parts of cerium oxide, 10 parts of aluminum oxide, 6 parts of flux, 5 parts of brightening agent;

[0020] The brightener is composed of beeswax and turpentine mixed, calculated according to mass percentage, the content of the beeswax accounts for 65%, and the content of the turpentine accounts for 35%;

[0021] The flux is made by mixing potassium nitrate and sodium nitrate. Calculated by mass percentage, the content of sodium nitrate accounts for 68%, and the content of potassium nitrate accounts for 32%.

Embodiment 3

[0023] A glass formula with high brightness, comprising the following components in parts by mass:

[0024] 40 parts of quartz sand, 12 parts of yellow sand, 4 parts of cerium oxide, 8 parts of aluminum oxide, 4 parts of flux, 4 parts of brightening agent;

[0025] The brightening agent is composed of beeswax and turpentine mixed, calculated according to mass percentage, the content of the beeswax accounts for 60%, and the content of the turpentine accounts for 40%;

[0026] The flux is made by mixing potassium nitrate and sodium nitrate, and the content of the sodium nitrate accounts for 65% and the content of the potassium nitrate accounts for 35% according to the mass percentage.

[0027] Different from the prior art, the glaze formula with high brightness in the present invention can greatly improve the brightness of the product by adding a brightening agent composed of beeswax and turpentine, so that the product has superior smoothness and improves the use value .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a formula of colored glaze with high brightness. The formula comprises the following ingredients in parts by mass: 30-50 parts of quartz sand, 15-25 parts of yellow sand, 3-5 parts of ceria, 6-10 parts of aluminum oxide, 2-6 parts of fusing assistant and 3-5 parts of brightener, wherein the brightener is prepared through mixing talcum powder and montmorillonite, the content of the talcum powder in the brightener is 55% to 65% (by mass), and the content of the montmorillonite in the brightener is 35% to 45% (by mass). By the manner, the formula has the advantages that the brightness of products can be improved greatly, the products can have superior smoothness, and the use value is increased.

Description

technical field [0001] The invention relates to a kind of colored glaze, in particular to a kind of colored glaze formula with high brightness. Background technique [0002] Liuli refers to crystal works made of artificial crystals of various colors as raw materials and dewaxed at high temperature by the ancient bronze dewaxing casting method. Its color is flowing and beautiful, and its quality is crystal clear and dazzling. This process can only be completed through dozens of manual operations, and a little negligence can cause failure or flaws, so its value is high, and the brightness of colored glaze directly affects the aesthetics of colored glaze handicrafts, and also directly affects the color of colored glaze. The value of handicrafts and the brightness of traditional colored glaze can no longer meet the needs of people now. Contents of the invention [0003] The technical problem mainly solved by the present invention is to provide a glass formula with high brigh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C6/04
CPCC03C1/00
Inventor 孙武
Owner 太仓市科教新城琉璃艺术策划中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap