Antibacterial glaze material

An antibacterial glaze and antibacterial agent technology, applied in the field of Jun porcelain manufacturing, can solve problems such as chronic poisoning, and achieve the effects of not decreasing antibacterial power, not easy to foam, and lasting bacteriostatic effect.

Inactive Publication Date: 2017-01-25
崔松伟
View PDF1 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The colored glaze on the ceramic surface in the market may become a health killer. The lead, mercury, radium, cadmium, etc. in the colored glaze are all harmful elements to the body. When the food enters the human body, over time, it will cause chronic poisoning

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] The preparation method of antibacterial glaze of the present invention is as follows:

[0023] (1) Pulverization: first take the above-mentioned parts by weight of zinc oxide, copper oxide, Hatoyama herbal medicine, quartz, talc, copper ore, and calcite and put them into a ball mill to pulverize them, mix them evenly and sieve to get the mixture powder;

[0024] (2) Smelting: Put the mixture powder in a crucible for smelting. The crucible is generally set on the flue between the kiln and the chimney. There is also a supplementary dye room on the furnace. When the heat of the flue gas is insufficient or the kiln stops burning, That is to say, it can be roasted in a supplementary combustion chamber. There is a small hole at the bottom of the crucible, which is blocked with a hard quartz ball. The melt splits into crisp and transparent pieces;

[0025] (3) Put the melt into small pieces together with nano-zirconium phosphate silver-loaded antibacterial agent and nano-tita...

Embodiment 1

[0027] An antibacterial glaze, which is composed of the following raw materials in parts by weight: 15 parts of nano zirconium phosphate silver-loaded antibacterial agent, 15 parts of nano titanium dioxide, 4 parts of zinc oxide, 4 parts of copper oxide, 65 parts of Hatoyama herb, 25 parts of quartz 15 parts of talc, 8 parts of copper ore, and 15 parts of calcite.

[0028] The preparation method of antibacterial glaze of the present invention is as follows:

[0029] (1) Pulverization: first take the above-mentioned parts by weight of zinc oxide, copper oxide, Hatoyama herbal medicine, quartz, talc, copper ore, and calcite and put them into a ball mill to pulverize them, mix them evenly and sieve to get the mixture powder;

[0030] (2) Smelting: Put the mixture powder in a crucible for smelting. The crucible is generally set on the flue between the kiln and the chimney. There is also a supplementary dye room on the furnace. When the heat of the flue gas is insufficient or the k...

Embodiment 2

[0033] An antibacterial glaze, which is composed of the following raw materials in parts by weight: 10 parts of nano-zirconium phosphate silver-loaded antibacterial agent, 10 parts of nano-titanium dioxide, 3 parts of zinc oxide, 3 parts of copper oxide, 60 parts of Hatoyama herb, 20 parts of quartz 10 parts of talc, 5 parts of copper ore, and 10 parts of calcite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

An antibacterial glaze material comprises a nano zirconium phosphate silver-loaded antibacterial agent, nano titanium dioxide, zinc oxide, copper oxide, Jiushan local glaze stone, quartz, talcum, copper ores and calcite. The antibacterial glaze material has the advantages that the nano zirconium phosphate silver-loaded antibacterial agent and the nano titanium dioxide are added into the glaze material, so that the glaze material has good antibacterial property, is non-toxic and pollution-free, and is suitable for the glaze formula of Jun porcelain kitchenware such as plates and bowls; the glaze material is good in fluidity, less prone to blistering and good in glossiness, and Jun porcelain glaze prepared by the glaze material is stable and uniform in color.

Description

technical field [0001] The invention belongs to the technical field of Jun porcelain manufacture, and in particular relates to an antibacterial glaze. Background technique [0002] Jun porcelain is based on the thickness of the glaze. Its color is either sunken under the glaze, suspended in the glaze, or floating on the surface of the glaze. The glaze is thick and lively, and the glaze layer is opalescent and moist. Jun porcelain is transformed into a god by the kiln, and the natural transformation of the kiln is the essence of Jun porcelain art, and it is also the rarity of Jun porcelain that is famous all over the world and famous in the porcelain forest. The same kind of glaze is applied during firing, and once fired, it will be colorful, that is, "one color when entering the kiln, and many colors when leaving the kiln". The ever-changing kiln transformation effect forms the magic of infinitely changing colors, purple in red, dark blue in purple, white in blue, red in wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20C03C8/04
CPCC03C8/04C03C8/20C03C2204/02
Inventor 崔松伟
Owner 崔松伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap