Shoes and production method thereof

A raw material, stone powder technology, applied in the field of necessities of human life, can solve the problems of poor thermal insulation effect, poor antibacterial property, poor toughness, etc., and achieve the effects of friction-resistant processing and molding, good elasticity and good corrosion resistance

Inactive Publication Date: 2017-10-20
合肥梵清电子商务有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problems of existing shoes that are prone to breakage, heavy weight, poor antibacterial properties, poor toughness, and poor thermal insulation effect, the purpose of the present invention is to provide a shoe and a preparation method thereof. Lightweight, good antibacterial properties, good toughness and good heat preservation effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A shoe comprising the following raw materials in parts by weight: 265 parts of natural rubber, 650 parts of stone powder, 70 parts of zinc oxide, 4 parts of stearic acid, 5 parts of sulfur, 11 parts of ointment, 16 parts of silver-loaded zirconium phosphate powder, and 10 parts of glass wool 8 parts of airgel, 9 parts of waste polyethylene foam, 6 parts of ceramic fiber, 12 parts of aramid fiber, 7 parts of foaming agent, 4 parts of rubber accelerator, 2 parts of plasticizer, antioxidant 3 parts, heat stabilizer 4 parts, light stabilizer 4 parts and coupling agent 2 parts.

[0041] Zirconium phosphate silver-loaded powder is added to the raw material, and the zirconium phosphate silver-loaded powder has the characteristics of antibacterial, inhibiting the growth of harmful bacteria, and is safe and non-toxic.

[0042] Glass wool is added to the raw material, and there are many tiny pores inside the glass wool, which perform well in thermal insulation, sound absorption, ...

Embodiment 2

[0060]A shoe comprising the following raw materials in parts by weight: 250 parts of natural rubber, 600 parts of stone powder, 60 parts of zinc oxide, 3 parts of stearic acid, 4 parts of sulfur, 10 parts of ointment, 13 parts of silver-loaded zirconium phosphate powder, and 8 parts of glass wool 6 parts of airgel, 7 parts of waste polyethylene foam, 4 parts of ceramic fiber, 9 parts of aramid fiber, 5 parts of foaming agent, 3 parts of rubber accelerator, 1 part of plasticizer, antioxidant 2 parts, 3 parts of heat stabilizer, 2 parts of light stabilizer and 1 part of coupling agent.

[0061] Zirconium phosphate silver-loaded powder is added to the raw material, and the zirconium phosphate silver-loaded powder has the characteristics of antibacterial, inhibiting the growth of harmful bacteria, and is safe and non-toxic.

[0062] Glass wool is added to the raw material, and there are many tiny pores inside the glass wool, which perform well in thermal insulation, sound absorpti...

Embodiment 3

[0080] A shoe comprising the following raw materials in parts by weight: 280 parts of natural rubber, 700 parts of stone powder, 80 parts of zinc oxide, 5 parts of stearic acid, 6 parts of sulfur, 12 parts of ointment, 19 parts of silver-loaded zirconium phosphate powder, and 12 parts of glass wool 10 parts of airgel, 11 parts of waste polyethylene foam, 8 parts of ceramic fiber, 15 parts of aramid fiber, 9 parts of foaming agent, 5 parts of rubber accelerator, 3 parts of plasticizer, antioxidant 4 parts, heat stabilizer 5 parts, light stabilizer 6 parts and coupling agent 3 parts.

[0081] Zirconium phosphate silver-loaded powder is added to the raw material, and the zirconium phosphate silver-loaded powder has the characteristics of antibacterial, inhibiting the growth of harmful bacteria, and is safe and non-toxic.

[0082] Glass wool is added to the raw material, and there are many tiny pores inside the glass wool, which perform well in thermal insulation, sound absorption...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a shoe and a preparation method thereof, and relates to the field of necessities for human life. The shoe includes the following raw materials in parts by weight: 250-280 parts of natural rubber, 600-700 parts of stone powder, 60-80 parts of zinc oxide, and 3-3 parts of stearic acid 5 parts, 4-6 parts of sulfur, 10-12 parts of ointment, 13-19 parts of silver-loaded zirconium phosphate powder, 8-12 parts of glass wool, 6-10 parts of airgel, 7-11 parts of waste polyethylene foam, 4-8 parts of ceramic fiber, 9-15 parts of aramid fiber, 5-9 parts of foaming agent, 3-5 parts of rubber accelerator, 1-3 parts of plasticizer, 2-4 parts of antioxidant, heat 3-5 parts of stabilizer, 2-6 parts of light stabilizer and 1-3 parts of coupling agent. The preparation method includes the following steps: (1) weighing raw materials, (2) putting them into a rubber mixer, (3) preparing an upper mold, a lower mold and a last, (4) foaming and shaping, (5) taking out the last, putting Molds and bottom molds. The invention solves the problems of easy breakage, heavy weight, poor antibacterial property, poor toughness and poor thermal insulation effect of existing shoes.

Description

technical field [0001] The invention belongs to the field of necessities for human life, and in particular relates to shoes and a preparation method thereof. Background technique [0002] Shoes made by traditional shoemaking technology are prone to degumming between the upper and the sole after being used for a period of time. In low temperature weather, they are even prone to breakage. The quality is poor, the weight is heavy, and the wearing comfort Not enough, poor toughness, poor antibacterial properties, poor thermal insulation effect, can not meet people's needs. Contents of the invention [0003] In order to solve the problems of existing shoes that are prone to breakage, heavy weight, poor antibacterial properties, poor toughness, and poor thermal insulation effect, the purpose of the present invention is to provide a shoe and a preparation method thereof. It has the advantages of light weight, good antibacterial property, good toughness and good heat preservation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L91/00C08L23/06C08L77/10C08K13/06C08K9/12C08K3/08C08K3/32C08K7/04C08K3/22C08J9/04A43B13/04
CPCC08L7/00A43B13/04C08J9/04C08J2307/00C08J2423/06C08K2003/0806C08K2003/2296C08K2003/328C08L2201/08C08L2203/14C08L2205/035C08L2205/16
Inventor 不公告发明人
Owner 合肥梵清电子商务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com