Double-phase stainless steel bar and preparation method thereof

A technology of duplex stainless steel and steel bar, applied in the field of high-strength stainless steel, can solve the problems of high price, no production data and literature reports of 2205 duplex stainless steel bar, increased production cost of stainless steel bar, etc., to improve yield strength and tensile strength Effect

Active Publication Date: 2017-11-24
CENT IRON & STEEL RES INST +1
View PDF17 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, duplex stainless steel is used to produce steel bars. During the rolling process, the cumulative deformation of the steel bars is large, and the yield strength of the steel bars is above 650 MPa. The excessively high strength exceeds the design requirements for the use of 500 MPa grade stainless steel bars.
[0004] Although, by increasing the content of Ni and Cr in stainless steel bars, it can meet the requirements of 500MPa stainless steel bars, but there are no production data and literature reports for 2205 duplex stainless steel bars. The content of Ni and Cr will increase the production cost of stainless steel bars, which is not conducive to the promotion and application of duplex stainless steel bars

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double-phase stainless steel bar and preparation method thereof
  • Double-phase stainless steel bar and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] Preferred embodiments of the present invention are specifically described below.

[0031] In the first aspect, the present invention provides a duplex stainless steel bar, which improves the yield strength and tensile strength of the duplex stainless steel bar by adding microalloying elements on the basis of the composition of 2205 stainless steel. The alloy composition of the duplex stainless steel bar consists of The mass percentages are: C≤0.03%, Si 0.20%~0.80%, Mn 0.80%~1.60%, Cr21.00%~23.00%, Ni 4.50%~5.50%, Mo 2.50%~3.50%, Nb 0~0.05 %, V 0-0.16%, Ti 0-0.02%, N 0.15%-0.20%, P≤0.020%, S≤0.010%, and the balance is Fe and unavoidable impurity elements.

[0032] Wherein, the so-called microalloying elements refer to one or more of Nb, V and Ti. It should be noted that since the design idea of ​​the present invention is to increase the yield strength and tensile strength of the solution-treated duplex stainless steel bar by adding microalloy elements, therefore, there ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a double-phase stainless steel bar and a preparation method thereof and belongs to the technical field of high-strength stainless steel. The alloy components of the double-phase stainless steel bar comprise C, Si, Mn, Cr, Ni, Mo, micro alloy elements, N, P, S and Fe. The micro alloy elements are one or more of Nb, V and Ti. Through smelting, continuous casting, hot rolling, cooling and solution treatment, the double-phase stainless steel bar is obtained. Under the premise that the production cost is basically unchanged, the yield strength of the double-phase stainless steel bar is improved, and thus the double-phase stainless steel bar can meet the 500 MPa-level stainless steel bar requirement; and meanwhile the corrosion resistance of the double-phase stainless steel bar is improved, and thus the double-phase stainless steel bar can meet the marine environment priority project requirement.

Description

technical field [0001] The invention relates to a high-strength stainless steel, in particular to a duplex stainless steel reinforcement and a preparation method thereof. Background technique [0002] In the marine environment, chloride ions have the most serious corrosion on concrete building structures, which makes conventional carbon steel and low alloy steel reinforcement unable to be used in harsh marine corrosion environments. [0003] Duplex stainless steel has excellent resistance to chloride ion corrosion, making it suitable for developing steel reinforcement materials of different strength grades. In the prior art, duplex stainless steel is used to produce steel bars. During the rolling process, the cumulative deformation of the steel bars is large, and the yield strength of the steel bars is above 650 MPa, which exceeds the design requirements for the use of 500 MPa grade stainless steel bars. [0004] Although, by increasing the content of Ni and Cr in stainless...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/58C22C38/04C22C38/50C22C38/48C22C38/46C22C38/44C22C33/04C21D8/08
CPCC21D8/065C21D8/08C22C33/04C22C38/001C22C38/04C22C38/44C22C38/46C22C38/48C22C38/50C22C38/58
Inventor 陈颖杨忠民王慧敏李昭东雍岐龙
Owner CENT IRON & STEEL RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka