Modified diatomaceous earth deodorant package and preparation method thereof

A diatomite and modified technology, applied in the field of modified diatomite deodorant packs and their preparation, can solve the problems of weakening and short lifespan, and achieve the effects of reducing harm, prolonging service life and slowing down the duration of weakness

Inactive Publication Date: 2018-03-23
佛山杰致信息科技有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a modified diatomite deodorant bag and its preparation method. The diatomite is modified by means of ultrasonic waves, and the diatomite is made softer by vibration, and the inside is easy to form a mesh, which is convenient for the mixture The advantages of mixing with other substances and diatomaceous earth solve the problem that the ability of the bamboo charcoal deodorant bag to absorb moisture and odors begins to weaken, and the service life is short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified diatomaceous earth deodorant package and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] This embodiment provides a modified diatomite deodorant bag, including the following components in parts by weight: 35 parts of diatomite, 10 parts of tea leaves, 10 parts of activated carbon, 5 parts of matrine, 10 parts of spearmint 3 parts of black poplar, 2 parts of black locust, 4 parts of neem flower, 8 parts of magnetite, 3 parts of tannic acid, 2 parts of flavonoids.

[0023] Diatomaceous earth, activated carbon, and magnets all have a particle size of 20 μm.

[0024] A kind of preparation method of modified diatomite deodorant bag, concrete method step is as follows:

[0025] S1: Weigh matrine, spearmint, black poplar, black locust, and neem flower in parts by weight, and rinse with deionized water for 10 minutes, and the washed matrine, spearmint, black poplar, black locust, and neem flower Then dry it in an oven at a drying temperature of 50°C, take it out and cool it to room temperature;

[0026] S2: respectively pulverize the cooled matrine, spearmint, bl...

Embodiment 2

[0032] This embodiment provides a modified diatomite deodorant bag, including the following components in parts by weight: 40 parts of diatomite, 11 parts of tea leaves, 11 parts of activated carbon, 6 parts of matrine, 10 parts of spearmint 4 parts of black poplar, 3 parts of black locust, 5 parts of neem flower, 9 parts of magnetite, 4 parts of tannic acid, 3 parts of flavonoids.

[0033] Diatomaceous earth, activated carbon, and magnets all have a particle size of 22 μm.

[0034] A kind of preparation method of modified diatomite deodorant bag, concrete method step is as follows:

[0035] S1: Weigh matrine, spearmint, black poplar, black locust, and neem flower in parts by weight, and rinse with deionized water for 12 minutes, and the washed matrine, spearmint, black poplar, black locust, and neem flower Then dry it in an oven at a drying temperature of 52°C, take it out and cool it to room temperature;

[0036] S2: respectively pulverize the cooled matrine, spearmint, bl...

Embodiment 3

[0042] This embodiment provides a modified diatomite deodorant bag, including the following components in parts by weight: 40 parts of diatomite, 13 parts of tea leaves, 13 parts of activated carbon, 10 parts of matrine, 10 parts of spearmint 3 parts of black poplar, 4 parts of black locust, 4 parts of neem flower, 10 parts of magnetite, 5 parts of tannic acid, 2 parts of flavonoids.

[0043] Diatomaceous earth, activated carbon, and magnets all have a particle size of 25 μm.

[0044] A kind of preparation method of modified diatomite deodorant bag, concrete method step is as follows:

[0045] S1: Weigh matrine, spearmint, black poplar, black locust, and neem flower in parts by weight, and rinse with deionized water for 15 minutes, and the washed matrine, spearmint, black poplar, black locust, and neem flower Then dry it in an oven at a drying temperature of 50°C, take it out and cool it to room temperature;

[0046] S2: respectively pulverize the cooled matrine, spearmint, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a modified diatomaceous earth deodorant package and a preparation method thereof. The modified diatomaceous earth deodorant package is prepared from the following components inparts by weight: 35 to 50 parts of diatomaceous earth, 10 to 15 parts of tea leaves, 10 to 15 parts of activated carbon, 5 to 10 parts of matrine, 10 to 12 parts of herba mentha spicata, and 3 to 5 parts of cortex populus nigra, 2 to 4 parts of cortex black locust and 4 to 6 parts of flos melia azedarach. The diatomaceous earth is modified by ultrasonic waves, the diatomaceous earth is made softer by vibration, and meshes are easily formed in the diatomaceous earth, which facilitates the mixing of a mixture, other substances and the diatomaceous earth; meanwhile, the meshes also facilitate the deodorization of the internal raw materials, thereby prolonging the service life of the deodorant package, and slowing down the debilitating time of the deodorant package; the activated carbon can adsorb undesirable odor, the tea leaves contain more phenol and alcohol organic matters, and the phenols can purify the air, thereby achieving the effect of deodorization; magnets can adsorb scrap ironand other impurities, thereby reducing the harm of magnetic substances on the human body.

Description

technical field [0001] The invention relates to the technical field of diatomite composite materials, in particular to a modified diatomite deodorizing bag and a preparation method thereof. Background technique [0002] Deodorant bag, suitable for absorbing odors in new homes, new cars, bathrooms, refrigerators, wardrobes and other places that are prone to odor. The existing deodorant bags are mainly deodorant bamboo charcoal bags. The deodorant bamboo charcoal bags are carbonized materials made of bamboo materials that are placed in a sealed carbonization furnace, isolated from the air and heated to 700°C-800°C to carbonize the bamboo materials. It is characterized by fine and porous, hard texture and large specific surface area. Bamboo charcoal deodorant bag has super adsorption function and the effects of generating negative ions, radiating far infrared rays, increasing alkalinity, etc. It can purify air and water quality, absorb moisture and adjust humidity, prevent mol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/20B01J20/30B01D53/02A61L9/013A61L9/014A61L101/04A61L101/12A61L101/44A61L101/56
CPCB01J20/20A61L9/013A61L9/014A61L2209/21A61L2209/22B01D53/02B01D2257/304B01D2257/406B01D2258/06B01J20/14
Inventor 王玉环
Owner 佛山杰致信息科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com