Preparation method of PP/SEBS suitable for rapid molding

A fast, composite material technology, applied in the direction of additive processing, etc., to achieve the effect of low hardness, improved weather resistance, and simple process

Inactive Publication Date: 2018-04-27
HEILONGJIANG XINDA ENTERPRISE GRP
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the consumables used in rapid prototyping are basically hard consumables, and many PP / SEBS composite materials are needed in industry and life, such as tire models, etc. Hard materials such as ABS and PLA cannot meet the requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Be applicable to the preparation method of the PP / SEBS composite material of rapid prototyping, adopt following steps:

[0028] (1) 27 parts (weight ratio, the same below) of polypropylene T30S, 35 parts of thermoplastic elastomer SEBS YH503, 35 parts of #70 white oil, 2 parts of antioxidant 1024, and 1 part of brominated styrene.

[0029] (2) Weigh each material according to the ratio in (1), and mix it in a high-speed kneader for 3-10 minutes to obtain a premix;

[0030] (3) Place the premix obtained in (2) in a twin-screw extruder for extrusion and drawing. The temperature of the twin-screw extruder is set as follows: 175°C, 178°C, 180°C, 185°C, 190°C, 200°C ℃, 205℃, die head temperature 210℃, screw aspect ratio greater than 32, screw rotation speed 150-180r / min, feeding speed 10-15r / min.

[0031] The obtained material has a Shore hardness (A) of 75, a tensile strength at break of 6.8 MPa, and an ultimate elongation of 300%, and has good rapid prototyping fluency an...

Embodiment 2

[0033] Be applicable to the preparation method of the modified polylactic acid composite material of rapid prototyping, adopt following steps:

[0034] (1) 30 parts (weight ratio, the same below) of polypropylene T30S, 25 parts of thermoplastic elastomer SEBS YH503, 40 parts of #100 white oil, 3 parts of antioxidant DSTP, 2 parts of decabromodiphenyl ether.

[0035] (2) Weigh each material according to the ratio in (1), and mix it in a high-speed kneader for 3-10 minutes to obtain a premix;

[0036] (3) Place the premix obtained in (2) in a twin-screw extruder for extrusion and drawing. The temperature of the twin-screw extruder is set as follows: 175°C, 178°C, 180°C, 185°C, 190°C, 200°C ℃, 205℃, die head temperature 210℃, screw aspect ratio greater than 32, screw rotation speed 150-180r / min, feeding speed 10-15r / min.

[0037] The obtained material has a Shore hardness (A) of 45, a tensile strength at break of 5.6 MPa, and an ultimate elongation of 300%, and has good rapid pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Shore hardnessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a PP/SEBS composite material suitable for rapid molding, and a preparation method thereof. The PP/SEBS composite material is prepared from, by mass, 25-40 parts of polypropylene, 10-30 parts of thermoplastic elastomer SEBS, 10-40 parts of mineral oil, 0-2 parts of an antioxidant and 0-2 parts of a fire retardant. Above raw materials are mixed by a high-speed mixer, and theobtained mixture undergoes extrusion wire-drawing by a twin-screw extruder. Compared with materials in the prior art, the material prepared in the invention has the characteristics of low hardness, improved resistance to weather and heat, excellent printing smoothness and excellent interlayer cohesiveness.

Description

technical field [0001] The invention belongs to the field of polymer materials and is suitable for rapid prototyping materials, in particular to a PP / SEBS composite material suitable for rapid prototyping and a preparation method thereof. Background technique [0002] Rapid prototyping technology, that is, a kind of rapid prototyping technology, is a technology based on digital model files, using bondable materials such as metal or plastic, and constructing objects by slicing and layer-by-layer printing. It has been widely developed in the fields of mold design, industrial machinery parts manufacturing, automobiles, aviation, medicine and medicine. Rapid prototyping technologies mainly include stereolithography, laser sintering, fusion lamination, etc. Among them, fusion lamination printing (FDM) is an extremely important one, and its application range is extremely wide. [0003] The main principle of Fused Deposition Printing Technology (FDM) is to heat the thermoplastic m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/02C08L91/06C08L91/00C08L23/12C08K5/03C08K5/06B33Y70/00B29C47/92B29C48/92
CPCC08L53/025B29C48/92B29C2948/9259B29C2948/92704B33Y70/00C08L91/06C08L2201/08C08L2205/03C08L2207/04C08L23/12C08K5/03C08K5/06
Inventor 周利波刘刚谢众
Owner HEILONGJIANG XINDA ENTERPRISE GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap