A kind of environment-friendly anti-UV flame-retardant polyethylene material and preparation method thereof

A flame-retardant polyethylene and environmental protection technology, applied in the field of environmentally friendly anti-UV flame-retardant polyethylene materials and their preparation, can solve the problems of polyethylene material aging, poor weather resistance, etc., achieve good weather resistance, improve anti-aging performance, The effect of improving weather resistance

Active Publication Date: 2020-10-30
GUANGDONG JUSHI CHEM CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because polyethylene molecules contain a small amount of double bonds and ether bonds, especially polyethylene materials added with flame retardants, their weather resistance is not good, and the sun and rain will cause polyethylene materials to age, so it is necessary to add antioxidants, Anti-UV agents and other additives for performance improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of environment-friendly anti-UV flame-retardant polyethylene material and preparation method thereof
  • A kind of environment-friendly anti-UV flame-retardant polyethylene material and preparation method thereof
  • A kind of environment-friendly anti-UV flame-retardant polyethylene material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] The preparation method of the above-mentioned environment-friendly anti-UV flame-retardant polyethylene material comprises the following steps:

[0043] 1) Add LDPE, decabromodiphenylethane, antimony trioxide, titanium dioxide and lubricant into a high-speed mixer and mix evenly, then add antioxidant and anti-UV agent, mix evenly;

[0044] 2) The material in step 1) is transferred to a co-rotating twin-screw extruder for mixing and extruding, and after cooling, it is drawn, pelletized, and screened to obtain an environmentally friendly anti-UV flame-retardant polyethylene material.

[0045] Preferably, the screw diameter of the co-rotating twin-screw extruder described in step 2) is 75-95mm, the length-to-diameter ratio of the screw is 44:1, and the temperature of each zone is: the first section is 100-115°C, the second section to the second section The fourth stage is 160-170°C, the fifth stage is 165-160°C, and the head is 160°C.

Embodiment 1

[0048] An environmentally friendly anti-UV flame-retardant polyethylene material, its raw material composition is shown in the following table:

[0049] Table 1 The raw material composition of an environmentally friendly anti-UV flame-retardant polyethylene material

[0050]

[0051]

Embodiment 2

[0053] An environmentally friendly anti-UV flame-retardant polyethylene material, its raw material composition is shown in the following table:

[0054] Table 2 The raw material composition of an environmentally friendly anti-UV flame-retardant polyethylene material

[0055]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural modulusaaaaaaaaaa
melt flow indexaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly anti-UV flame-retardant polyethylene material and a preparation method thereof. The environment-friendly anti-UV flame-retardant polyethylene material is composed of the following raw materials in parts by weight: 90-95 parts of LDPE, 2.5-4.5 parts of decabromodiphenylethane, 0.8-2.0 parts of antimony trioxide, 0.2-0.5 part of an antioxidant, 0.2-0.8part of an anti-UV agent, 0.5-2.0 parts of titanium dioxide and , 0.3-0.7 part of a lubricant; and the preparation method comprises the following steps: 1) adding LDPE, decabromodiphenylethane, antimony trioxide, titanium dioxide and the lubricant into a high-speed mixer for mixing uniformly, then adding the antioxidant and the anti-UV agent for mixing uniformly; and 2) transferring the materialsof the step 1) to a co-rotating twin-screw extruder for mixing and extruding, stripping, pelletizing and screening after cooling. The environment-friendly anti-UV flame-retardant polyethylene material provided by the invention has the advantages of excellent flame retardancy, excellent anti-UV and anti-aging performances, good weather resistance, difficult fading and discoloration, simple preparation method, low production cost and easy industrial large-scale production.

Description

technical field [0001] The invention relates to an environment-friendly anti-UV flame-retardant polyethylene material and a preparation method thereof, belonging to the technical field of flame-retardant composite materials. Background technique [0002] Polyethylene (PE) has the advantages of odorless, non-toxic, excellent low temperature resistance, good chemical stability, resistance to most acids and alkalis, low water absorption, and excellent electrical insulation. It is widely used in chemical industry, agriculture, construction and packaging and other fields. Among them, the demand for polyethylene in the simulated PE decoration industry is increasing, and the requirements are becoming stricter and stricter. Many products have been promoted from meeting the requirements of indoor use to meeting the requirements of outdoor use, with good weather resistance, no fading, and stable flame retardancy. High-quality weather-resistant polyethylene materials are the future de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08K13/02C08K5/098C08K3/22C08K5/03
CPCC08K3/22C08K3/2279C08K5/03C08K5/098C08K13/02C08K2003/2241C08L2201/02C08L2201/08C08L2207/066C08L23/06
Inventor 沈旭渠陈锐彬张翼翔刘华夏陈新泰龚文幸唐海兰田凯丽
Owner GUANGDONG JUSHI CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com