Water-based matting finishing agent used for surface treatment of artificial leather and containing no inorganic matting powder, and preparation method thereof

A surface treatment and finishing agent technology, which is applied in the field of preparation of the matting finishing agent, can solve the problems of artificial leather white marks, inorganic matting powder dispersion, and no practical products, and achieve strong adhesion, good anti-blocking, The effect of improving quality

Active Publication Date: 2018-07-20
惠州长联新材料科技有限公司
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These treatment agents based on silica powder as the matting component have a good matting effect, but there is a problem of dispersion of inorganic matting powder, and artificial leather is prone to white marks after folding and rubbing
It has been reported in literature (Yang Xiping: "Preparation and Application of Environment-friendly PVC Artificial Leather Matting Treatment Agent", Shaanxi University of Science and Technology, 2014) that two polymer emulsions that are thermodynamically incompatible are blended, and the film-forming surface of the blended emulsion produces microscopic defects. Undulating, resulting in a matting effect, but no practical product seen

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The present embodiment does not contain inorganic matting powder and is used for artificial leather surface treatment water-based matting finishing agent, by mass parts, it is composed of: solid content is 45% environment-friendly acrylate resin emulsion MD55 (a kind of with core-shell structure and Self-crosslinkable acrylate resin emulsion at room temperature, MFT 22°C, Tg 45°C, viscosity (25°C) 95mPa·s (product of Dongguan Changlian New Material Technology Co., Ltd.) 100 parts, water 200 parts, PTF thickener 3 parts of C-1 (an acrylic acid copolymer thickener, a product of Guangdong Zhonglian), 0.9 part of defoamer, 1.5 parts of wetting agent OT-75 (trade name, such as Jiangsu Haian Petrochemical Factory), the content is 3.5 parts of 25% ammonia water.

[0038] In the dispersing pot equipped with a stirring and dispersing device, add the acrylate resin emulsion first, and then add water, thickener, defoamer, and wetting agent in sequence under slow (200rpm) stirring,...

Embodiment 2

[0042] The present embodiment does not contain inorganic matting powder and is used for artificial leather surface treatment water-based matting finishing agent, by mass parts, it is composed of: solid content is 45% environmental protection acrylate-styrene copolymer resin emulsion YD55 (a kind of having core- Water-based acrylic-styrene copolymer resin emulsion with shell structure and self-crosslinking at room temperature, MFT 22°C, Tg 45°C, viscosity (25°C) 105mPa·s. Product of Dongguan Changlian New Material Technology Co., Ltd.) 100 parts, 200 parts of water, 3 parts of PTF thickener C-1 (an acrylic acid copolymer thickener, Guangdong Zhonglian product), 0.9 part of defoamer, wetting agent OT-75 (commercial brand, Haian Petrochemical of Jiangsu Province) Plant) 1.5 parts, content is 3.5 parts of ammoniacal liquor of 25%.

[0043] Add the acrylate-styrene copolymer resin emulsion into the dispersing pot equipped with a stirring dispersing device, and then add water, thick...

Embodiment 3

[0047] The water-based matting finishing agent for artificial leather surface matting treatment that does not contain inorganic matting powder in this embodiment is composed of: a solid content of 45% environmentally friendly acrylic resin emulsion MD55 (a kind of acrylate resin emulsion with a core-shell structure Water-based acrylate resin that can be self-crosslinked at room temperature, MFT 22°C, Tg 45°C, viscosity (25°C) 95mPa s (product of Dongguan Changlian New Material Technology Co., Ltd.) and environmentally friendly acrylate with a solid content of 45% - Styrene copolymer resin emulsion YD55 (an acrylic ester-styrene copolymer resin emulsion with a core-shell structure and self-crosslinking at room temperature (product of Dongguan Changlian New Material Technology Co., Ltd., MFT 22°C, Tg 45°C , viscosity (25°C) 105mPa·s.) 50 parts each, 200 parts water, 3 parts PTF thickener C-1 (an acrylic copolymer thickener, a product of Guangdong Zhonglian), 0.9 parts defoamer, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention relates to a water-based matting finishing agent used for surface treatment of artificial leather and containing no inorganic matting powder, and a preparation method thereof, wherein the water-based matting finishing agent comprises the components in parts by mass: 100 parts of an environmentally friendly acrylate resin emulsion or acrylate-styrene polymerized resin emulsion or their mixed emulsion with the solid content of 45% by mass, 90-300 parts of water, 0-1.5 parts of a film forming auxiliary agent, 1.5-5.0 parts of an acrylic copolymer thickener, 0.9-1.2 parts of a defoamer, 1.2-4.5 parts of a wetting agent, 0-5 parts of a functional auxiliary agent, and 2-5 parts of ammonia water with the content of 25%. The preparation method comprises the steps: under dispersing mixing, successively adding the components into a dispersion pot, stirring and dispersing evenly, filtering, and thus obtaining the water-based matting finishing agent. The matting finishing agent is environmentally friendly, has the advantages of good surface affinity to the artificial leather, strong adhesion power, no folded marks, good water resistance and strong matting effect. With use of different functional auxiliary agents, different impressions and handfeeling effects can be obtained.

Description

technical field [0001] The invention relates to an environment-friendly water-based matting finishing agent which does not contain inorganic matting powder and is used for surface treatment of PVC and PU artificial leather. The invention also relates to a preparation method of the matting finishing agent. Background technique [0002] PVC and PU artificial leather are the two most produced artificial leathers. The production process of PVC artificial leather is mainly coating method and calendering method. PU artificial leather is mainly produced by coating process. With the change of production raw materials and production technology, artificial leather products with different properties and varieties can be obtained to meet different application requirements. [0003] Due to the manufacturing process, the surface of artificial leather without surface treatment has a strong plastic feeling, which is quite different from natural leather in appearance. By adding gloss and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D7/43
CPCC08L2205/025C08L2205/03C08L2205/035C08L2207/53C09D133/04C08L33/00C08L33/04C08L91/06C08L83/04
Inventor 卢如康廖凯荣张雅莲麦伟林麦友攀刘芳典
Owner 惠州长联新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap