A preparation method of ultra-wide and highly wear-resistant plastic-absorbing and coated environmentally friendly veneer

A high wear-resistant and veneer technology, which is applied in the jointing of wooden veneers, chemical instruments and methods, wood heating, etc., can solve the problems that cannot meet the needs of special-shaped parts, such as blistering, coating treatment, and rough and uneven surface appearance of decorative veneers. Satisfy processing and production problems, and achieve the effects of wide processing range, high barrier ability, aging resistance and strong ability

Active Publication Date: 2021-10-29
上海诚简环保科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing decorative coated veneers, such as furniture, doors, windows, walls, etc., are mostly spliced ​​with veneers within 60cm, forming large gaps in the veneer, and the surface texture is not beautiful, and the surface flatness is poor, which cannot meet the needs of special-shaped parts. Blistering and coating treatment, and most of the existing elastic coated veneers are made of toxic materials such as PVC, which will produce toxic gases such as chlorine after being burned at high temperature or fire source. In order to overcome many defects of this product, there will be The veneer with a thickness greater than 0.15mm-0.4mm is spliced ​​to overcome the defects of uneven surface and unsightly texture by increasing toughness and softening. Shrinkage makes the cracks at the splicing continue to increase, causing the surface of the decorative veneer to become rough and uneven, which seriously affects the service life of the veneer, and cannot meet the processing and production of customer blisters and large-scale special-shaped parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of ultra-wide and highly wear-resistant plastic-absorbing and coated environmentally friendly veneer
  • A preparation method of ultra-wide and highly wear-resistant plastic-absorbing and coated environmentally friendly veneer
  • A preparation method of ultra-wide and highly wear-resistant plastic-absorbing and coated environmentally friendly veneer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A method for preparing an ultra-wide, highly wear-resistant, plastic-absorbing, and environmentally-friendly veneer-coated method, comprising the following steps:

[0030] a. Composite: apply adhesive on the veneer, and then flatten the non-woven fabric on the veneer, the weight of the non-woven fabric is 4g / ㎡;

[0031] b. Toughening and constant humidity: put the composite veneer into the cooking equipment, the water temperature in the cooking equipment is raised from normal temperature to 45°C and then kept at the temperature, the duration of the heating is 1.5h, and then the temperature is raised from 45°C to 55°C, The heating duration is 2 hours, and the water in the cooking equipment is replaced once after cooking, and the temperature is slowly raised again. After repeating the above heating process twice, it is then dried by a belt dryer. Constant temperature and humidity in a closed environment until the moisture content of the veneer is 12%;

[0032] c. Piecing...

Embodiment 2

[0037] A method for preparing an ultra-wide, highly wear-resistant, plastic-absorbing, and environmentally-friendly veneer-coated method, comprising the following steps:

[0038] a. Composite: apply adhesive on the veneer, and then flatten the non-woven fabric on the veneer. The weight of the non-woven fabric is 15g / ㎡;

[0039] b. Toughening and constant humidity: put the composite veneer into the cooking equipment, the water temperature in the cooking equipment is raised from normal temperature to 45°C and then kept at the temperature. The duration is 3 hours, and the water in the cooking equipment is replaced once after cooking, and the temperature is slowly raised again. After repeating the above heating process 2 times, it is then dried by a belt dryer. Constant temperature and humidity in the environmental conditions until the moisture content of the veneer is 10%;

[0040]c. Piecing: The veneer is spliced ​​infinitely and seamlessly along the vertical direction to ensur...

Embodiment 3

[0045] A method for preparing an ultra-wide, highly wear-resistant, plastic-absorbing, and environmentally-friendly veneer-coated method, comprising the following steps:

[0046] a. Composite: apply adhesive on the veneer, and then flatten the non-woven fabric on the veneer, the weight of the non-woven fabric is 25g / ㎡;

[0047] b. Toughening and constant humidity: put the composite veneer into the cooking equipment, the water temperature in the cooking equipment is raised from normal temperature to 45°C and then kept at the temperature, the duration of the heating is 1h, and then the temperature is raised from 45°C to 55°C, and the temperature is raised The duration is 3 hours, and the water in the cooking equipment is replaced once after cooking, and the temperature is slowly raised again. After repeating the above heating process 2 times, it is then dried by a belt dryer. Constant temperature and humidity in the environmental conditions until the moisture content of the vene...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an ultra-wide, highly wear-resistant plastic-absorbing, coated and environmentally-friendly veneer and a preparation method thereof. The key points of the technical scheme include the following steps: compounding, coating an adhesive on a veneer blank, and then applying a non-woven fabric Flatly attached to the veneer blank; toughening and constant humidity; skinning; sanding and impurity removal; roller coating film; plastic forming. The invention provides a preparation method of an ultra-wide, highly wear-resistant plastic-absorbing, environmentally-friendly coated veneer. The process is environmentally friendly, and the sheet or coil can be industrially produced in batches, and the quality is easy to control.

Description

【Technical field】 [0001] The invention belongs to the technical field of fireproof materials, and in particular relates to an ultra-wide, highly wear-resistant plastic-absorbing, coated and environmentally friendly veneer and a preparation method thereof. 【Background technique】 [0002] Existing decorative coated veneers, such as furniture, doors, windows, walls, etc., are mostly spliced ​​with veneers within 60cm, forming large gaps in the veneer, and the surface texture is not beautiful, and the surface flatness is poor, which cannot meet the needs of special-shaped parts. Blistering and coating treatment, and most of the existing elastic coated veneers are made of toxic materials such as PVC, which will produce toxic gases such as chlorine after being burned at high temperature or fire source. In order to overcome many defects of this product, there will be The veneer with a thickness greater than 0.15mm-0.4mm is spliced ​​to overcome the defects of uneven surface and uns...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B27M1/08B27D1/10B27K5/00B32B37/10B32B37/12B32B38/00B32B38/18C09D175/04C09J11/04C09J175/06
CPCB27D1/10B27K5/001B32B37/10B32B37/1284B32B38/0012B32B38/164B32B38/1858B32B2307/40B32B2307/554B32B2307/558B32B2307/584C08K2003/2227C08L2201/02C09D175/04C09J11/04C09J175/06C08L67/04C08K3/34C08K3/22C08L63/00
Inventor 王黄志王灿义
Owner 上海诚简环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap