Shining waterproof zipper

A technology of waterproof zipper and waterproof coating, applied in the field of zipper, can solve the problems of zipper not having durability, exposed flashing material, cracked coating, etc., and achieve the effects of high ornamental, improved crosslinking density, and uniform thickness

Active Publication Date: 2018-12-21
东莞市瑞翔新型材料科技有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the washing process, if the coating is not water-resistant, it will easily cause the coating to crack, and the glitter will be exposed or even detached, resulting in the zipper not being durable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Shining waterproof zipper
  • Shining waterproof zipper
  • Shining waterproof zipper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A flash waterproof zipper, comprising a cloth tape 1 and several fastener elements 3 arranged on the cloth tape 1, the cloth tape 1 is compounded with a flash waterproof coating 2, and the flash waterproof coating 2 is composed of a flash waterproof coating Prepared, the flash waterproof paint comprises the following raw materials in parts by weight:

[0036]

[0037] Wherein, the polyamide-glitter microbeads are composed of glitter microbeads and a polyacrylamide layer covering the glitter microbeads.

[0038] Wherein, the polyol is composed of polytetrahydrofuran ether diol and polycarbonate diol in a ratio of 1.5:2 by weight, the molecular weight of polytetrahydrofuran ether diol is 2500, and the hydroxyl value is 50KOH / g. The molecular weight of the alcohol is 1500, and the hydroxyl value is 45KOH / g.

[0039] Wherein, the isocyanate curing agent is composed of 4,4-diphenylmethane diisocyanate and isophorone diisocyanate in a ratio of 2:1 by weight, and the -NCO ...

Embodiment 2

[0051] A flash waterproof zipper, comprising a cloth tape 1 and several fastener elements 3 arranged on the cloth tape 1, the cloth tape 1 is compounded with a flash waterproof coating 2, and the flash waterproof coating 2 is composed of a flash waterproof coating Prepared, the flash waterproof paint comprises the following raw materials in parts by weight:

[0052]

[0053] Wherein, the polyamide-glitter microbeads are composed of glitter microbeads and a polyacrylamide layer covering the glitter microbeads.

[0054] Wherein, the polyol is composed of polytetrahydrofuran ether diol and polycarbonate diol in a ratio of 1:1 by weight, the molecular weight of polytetrahydrofuran ether diol is 2000, and the hydroxyl value is 40KOH / g. The molecular weight of the alcohol is 1000, and the hydroxyl value is 40KOH / g.

[0055] Wherein, the isocyanate curing agent is composed of 4,4-diphenylmethane diisocyanate and isophorone diisocyanate in a ratio of 1:1 by weight, and the -NCO of...

Embodiment 3

[0067] A flash waterproof zipper, comprising a cloth tape 1 and several fastener elements 3 arranged on the cloth tape 1, the cloth tape 1 is compounded with a flash waterproof coating 2, and the flash waterproof coating 2 is composed of a flash waterproof coating Prepared, the flash waterproof paint comprises the following raw materials in parts by weight:

[0068]

[0069]

[0070] Wherein, the polyamide-glitter microbeads are composed of glitter microbeads and a polyacrylamide layer covering the glitter microbeads.

[0071] Wherein, the polyol is composed of polytetrahydrofuran ether diol and polycarbonate diol in a ratio of 2:3 by weight, the molecular weight of polytetrahydrofuran ether diol is 3000, and the hydroxyl value is 60KOH / g. The molecular weight of the alcohol is 2000, and the hydroxyl value is 50KOH / g.

[0072] Wherein, the isocyanate curing agent is composed of 4,4-diphenylmethane diisocyanate and isophorone diisocyanate in a ratio of 3:1 by weight, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of zippers, in particular to a shining waterproof zipper. The shining waterproof zipper comprises a cloth strap and a plurality of zipper teeth arranged onthe cloth strap, wherein a shining waterproof coating is compounded on the cloth strap, the shining waterproof coating is prepared from shining waterproof paint, and the shining waterproof paint is prepared from the following raw materials: polyhydric alcohol, polyamide-shining microspheres, an isocyanate curing agent, a catalyst, a chain extender, a flatting agent, a wetting agent and deionizedwater, wherein the polyamide-shining microspheres are composed of shining microspheres and polyacrylamide layers covering the shining microspheres. According to the shining waterproof zipper, by adopting polyacrylamide for conducting covering treatment on the shining microspheres, the shining microspheres can be evenly dispersed in the deionized water, and can be subjected to cross-linking polymerization with isocyanate, so that the stability of the polyamide-shining microspheres in paint is improved, the coating has good mechanical performance and waterproofness, the durability of the zipperis high, and an ornamental value is high.

Description

technical field [0001] The invention relates to the technical field of zippers, in particular to a flash waterproof zipper. Background technique [0002] A zipper is a connecting piece that relies on continuously arranged chain elements to merge or separate items. It is now widely used in clothing, bags, tents, etc. As an important part of carrying chain teeth and other zipper components, the zipper bag will also have a great impact on the overall appearance of the garment. The existing zipper tapes have a single way of expression, generally only for simple color expression, and dyeing is also easy to cause problems such as fading and fading. [0003] In order to meet the needs of pursuing fashion and individuality, it is popular to add gold and silver onion powder to viscous fluids or liquid adhesives such as hairspray, personalized clothing spray glue, nail polish, etc., in order to achieve a shiny effect and earn the visual effect of other people's eyes. . Therefore, i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/14D06N3/00A44B19/34
CPCA44B19/34D06N3/0056D06N3/0061D06N3/146D06N3/148D06N2209/0838D06N2209/103D06N2209/142
Inventor 吴小锐
Owner 东莞市瑞翔新型材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap