Method for preparing waterproof emulsion of thermosetting composite polystyrene foam insulation board

A technology of polystyrene foam and waterproof emulsion, applied in the direction of adhesive types, adhesive additives, ester copolymer adhesives, etc., can solve the problems of poor thermal insulation and sound absorption effects, and the inability to improve the thermal insulation effect of board gaps, etc., to achieve The effect of improving the thermal insulation effect

Inactive Publication Date: 2019-01-11
江苏贝尔诺新能源科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] When the general waterproof emulsion is used, its own thermal insulation and sound absorption effect may be poor. When it is applied on the board or filled between the boards, it may not be able to improve the thermal insulation effect of the gap between the boards, and the heat loss in the gap may be relatively large. Big

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing waterproof emulsion of thermosetting composite polystyrene foam insulation board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A method for preparing a thermosetting composite polystyrene foam insulation board waterproof emulsion, said preparation method comprising the steps of:

[0022] (1) Weighing of raw materials, weighing of raw materials according to weight ratio, the weight ratio of each raw material when weighing is 35-37 parts of acrylic emulsion, 26 parts of polyvinyl alcohol, 25 parts of resin coating glue PBA, ethyl acetate 10-12 parts of grease, 13-16 parts of ethylene-vinyl acetate copolymer, 6-8 parts of light calcium powder, 5-8 parts of expanded perlite, 4-5 parts of calcium silicate;

[0023] (2) Mix some raw materials, put the acrylic emulsion, polyvinyl alcohol, resin coating glue PBA, ethyl acetate, ethylene-vinyl acetate copolymer and light calcium powder weighed in step (1) into the reaction kettle, The reaction kettle heats the input raw materials to keep the internal temperature of the reaction kettle at 60-75°C, then the reaction kettle mixes the raw materials, after s...

Embodiment 2

[0035] A method for preparing a thermosetting composite polystyrene foam insulation board waterproof emulsion, said preparation method comprising the steps of:

[0036] (1) Weighing of raw materials, weighing of raw materials according to weight ratio, the weight ratio of each raw material when weighing is 35-37 parts of acrylic emulsion, 20-26 parts of polyvinyl alcohol, 18-25 parts of resin coating glue PBA 10-12 parts of ethyl acetate, 16 parts of ethylene-vinyl acetate copolymer, 6-8 parts of light calcium powder, 5-8 parts of expanded perlite, 4-5 parts of calcium silicate;

[0037] (2) Mix some raw materials, put the acrylic emulsion, polyvinyl alcohol, resin coating glue PBA, ethyl acetate, ethylene-vinyl acetate copolymer and light calcium powder weighed in step (1) into the reaction kettle, The reaction kettle heats the input raw materials to keep the internal temperature of the reaction kettle at 60-75°C, then the reaction kettle mixes the raw materials, after stirri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing a waterproof emulsion of a thermosetting composite polystyrene foam insulation board. The method comprises: weighing raw materials according to a weightratio, mixing the raw materials, adding the weighed acrylic emulsion, polyvinyl alcohol, a resin coated adhesive PBA, ethyl acetate, an ethylene-vinyl acetate copolymer and light calcium powder into areactor, carrying out mixing, grinding expanded perlite and calcium silicate, adding the expanded perlite and calcium silicate powder into the mixture, and discharging the waterproof emulsion througha reactor. In preparation of the waterproof emulsion, expanded perlite and calcium silicate are used and are uniformly mixed in the waterproof emulsion in a form of powder particles so that the heatinsulation effects of the waterproof emulsion are improved.

Description

technical field [0001] The invention relates to a method for preparing a waterproof emulsion, in particular to a method for preparing a waterproof emulsion for a thermosetting composite polystyrene foam insulation board, and belongs to the technical field of preparation and application of waterproof emulsion. Background technique [0002] Thermosetting composite polystyrene foam insulation board is a kind of insulation board, which is generally used for wall insulation and heat insulation; when installed on the wall, it may be covered with waterproof emulsion to make it stick to the wall, and the waterproof emulsion Gaps between panels can be filled. [0003] When the general waterproof emulsion is used, its own thermal insulation and sound absorption effect may be poor. When it is applied on the board or filled between the boards, it may not be able to improve the thermal insulation effect of the gap between the boards, and the heat loss in the gap may be relatively large. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L33/04C08L29/04C08L23/08C08K3/26C08K7/26C08K3/34C09J133/04C09J129/04C09J123/08C09J11/04
CPCC08K2003/265C08L33/04C08L2201/52C08L2205/035C09J11/04C09J133/04C08L29/04C08L23/0853C08K3/26C08K7/26C08K3/34
Inventor 章友芳刘君
Owner 江苏贝尔诺新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap