C30 concrete and preparation method thereof
A concrete and bamboo fiber technology, applied in the field of concrete, can solve the problems of limited drainage capacity of impermeable concrete pavement, acceleration of urban heat island effect, and reduction of air humidity, so as to improve workability and flexural strength, and improve hydrophilicity And dispersibility, the effect of preventing drying shrinkage
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0033] Preparation Example 1: S1: Preparation of modified solution: take 30kg of sodium carbonate, 10kg of sodium silicate, 5kg of sodium oleate, 1kg of triethanolamine oleate, 1kg of laureth ether and 60kg of water at a speed of 100r / min Stir for 10 minutes to obtain the modified liquid;
[0034] S2: Modification treatment: take the bamboo fiber with a fineness of 100 mesh and place it at a temperature of 100°C and dry it for 6 hours; then put the dried bamboo fiber in the modification solution and soak it for 24 hours, the bamboo fiber and the modification solution The weight ratio of the bamboo fiber is 1:20; after taking out the bamboo fiber, clean it with deionized water to make its pH value 7-8, and then place it at a temperature of 100℃ for another 6-8h to obtain the modification bamboo fiber.
Example Embodiment
[0035] Preparation Example 2: S1: Preparation of Modified Liquid: Take 35kg of sodium carbonate, 15kg of sodium silicate, 7.5kg of sodium oleate, 1.5kg of triethanolamine oleate, 1.5kg of laureth ether and 65kg of water, with 150r / Stir for 15 minutes at a speed of 1 min to obtain the modified liquid;
[0036] S2: Modification treatment: take the bamboo fiber with a fineness of 150 mesh, place it at 105℃, and dry it for 7 hours; then put the dried bamboo fiber in the modification solution and soak for 30 hours, the bamboo fiber and the modification solution The weight ratio of the bamboo fiber is 1:20; after taking out the bamboo fiber, clean it with deionized water to make the pH value 7-8, and then place it at 105℃ for another 7h to obtain the modified bamboo fiber .
Example Embodiment
[0037] Preparation Example 3: S1: Preparation of Modified Solution: Take 40kg of sodium carbonate, 20kg of sodium silicate, 10kg of sodium oleate, 2kg of triethanolamine oleate, 2kg of laureth ether and 70kg of water at a speed of 200r / min Stir for 20 minutes to obtain the modified liquid;
[0038] S2: Modification treatment: take the bamboo fiber with a fineness of 150 mesh, place it at 110℃, and dry it for 8h; then put the dried bamboo fiber in the modification solution for 36h, the bamboo fiber and the modification solution The weight ratio of the bamboo fiber is 1:20; after taking out the bamboo fiber, clean it with deionized water to make its pH value 7-8, and then place it at a temperature of 110°C for another 8 hours to obtain the modified bamboo fiber .
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap