Emulsified asphalt, emulsified asphalt mixture and cold-mixed and cold-laid wearing layer prepared from mixture

A technology of emulsified asphalt and mixed materials, which can be used in building insulation materials, building components, buildings, etc., and can solve problems such as high driving noise

Active Publication Date: 2019-09-13
沈阳坛城道桥科技有限公司 +1
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Based on this, it is necessary to provide an emulsified asphalt, an emulsified asphalt mixture and a cold-mixed and cold-paved wear course prepared from the mixture in order to solve the problem of high maintenance road noise in the micro-surfacing technology.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Emulsified asphalt, emulsified asphalt mixture and cold-mixed and cold-laid wearing layer prepared from mixture
  • Emulsified asphalt, emulsified asphalt mixture and cold-mixed and cold-laid wearing layer prepared from mixture
  • Emulsified asphalt, emulsified asphalt mixture and cold-mixed and cold-laid wearing layer prepared from mixture

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The present invention also provides the preparation method of described emulsified asphalt, comprises the following steps:

[0033] S10, under the condition of 45° C. to 65° C., mix and stir the water, the organic amine emulsifier, and the organic polybasic acid in proportion to uniformly prepare soap liquid;

[0034] S20, pass the soap solution prepared in step S10 and the heated asphalt through a colloid mill in proportion to prepare emulsified asphalt.

[0035] The organic amine emulsifier can be selected from one or more of fatty amines, fatty amine epoxides, fatty imidazolines, fatty quaternary ammonium salts and fatty piperazine emulsifiers, so The organic polybasic acid can be selected from one or more of oxalic acid, terephthalic acid, maleic acid, tartaric acid, citric acid and trimesitic acid.

[0036]In the step S10, the soap liquid is prepared under the temperature condition of 45°C-65°C. In one embodiment, the temperature in step S10 may preferably be 55°...

Embodiment 1

[0060] S00, heat 1,000 parts of heavy-duty No. 70 asphalt to 180°C-190°C, add 50 parts of SBS to the asphalt, grind the mixture through a colloid mill and keep the temperature of the mixture at 180°C-190°C for 4-5 hours, then After reducing the temperature to 170°C-180°C, add 1 part of sulfur and keep it warm for 1-2 hours to obtain modified asphalt;

[0061] S10, heat 600 parts of water to 55 ℃ ~ 65 ℃, add 50 parts of organic amine emulsifier (oil diamine ethoxylate, CAS number: 68442-23-9) and 50 parts of citric acid into the water and stir Uniform preparation of soap liquid;

[0062] S20, pump the soap solution prepared in step S10 and the modified asphalt prepared in step S00 into the colloid mill, adjust the parameters of the colloid mill, and prepare emulsified asphalt.

[0063] The above-mentioned prepared emulsified asphalt was tested for performance, and the various indicators of the asphalt emulsion were measured according to the national standard determination meth...

Embodiment 2

[0069] S10, heat 600 parts of water to 45-55 °C, add 50 parts of organic amine emulsifier (oil diamine ethoxylate, CAS number: 68442-23-9) and 75 parts of oxalic acid into the water and stir evenly, Then add 100 parts of styrene-butadiene emulsion, and further stir to complete the soap solution preparation;

[0070] S20, pump the soap liquid prepared in step S10 and 1000 parts of heavy Jiao No. 70 asphalt heated to 140° C. into the colloid mill, adjust the parameters of the colloid mill, and prepare emulsified asphalt.

[0071] Performance tests were carried out on the emulsified asphalt prepared above: the emulsified asphalt is cationic, the storage stability of 1 day and 5 days is 0.1% and 2.0% respectively, the evaporation residue content is 60.3%, and the mixing time with the aggregate is 150s. The initial setting time is 8 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides emulsified asphalt, an emulsified asphalt mixture and a cold-mixed and cold-laid wearing layer prepared from the mixture. The emulsified asphalt comprises the following raw materials: asphalt, water, an organic amine emulsifying agent and an organic polybasic acid, wherein the organic amine emulsifying agent and the organic polybasic acid are combined with each other by electrostatic attraction.

Description

technical field [0001] The invention relates to the technical field of road maintenance, in particular to an emulsified asphalt, an emulsified asphalt mixture and a cold-mixed and cold-paved wearing layer prepared from the mixture. Background technique [0002] The maintenance of asphalt pavement is very important to prolong the service life of the pavement and reduce the national infrastructure investment. The maintenance technology based on hot mix asphalt mixture is restricted by many factors such as high energy consumption, high equipment investment cost, and short transportation distance of finished products. For example, the hot-mix ultra-thin wear layer technology, the hot-mix mixture used is restricted by the asphalt mixing plant, the transportation distance is limited, and there are problems such as large energy consumption, large VOC emissions, and high cost. Therefore, cold mixing and cold paving technology is expected to become the best means of asphalt pavement...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L95/00C08L53/02C08L9/06C08K5/092C08K5/17C08J3/03C04B26/26
CPCC08J3/03C04B26/26C08J2395/00C08J2453/02C08J2409/06C08K5/092C08K5/17C04B14/02C04B14/06
Inventor 王勇姚立峰
Owner 沈阳坛城道桥科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com