A kind of nanofiber reinforced polyimide airgel material and preparation method thereof

A polyimide and aerogel technology, applied in the field of aerogel materials and their preparation, can solve problems such as low strength and achieve the effects of enhancing mechanical strength, simple preparation process, and improving Young's modulus

Active Publication Date: 2022-03-04
DONGHUA UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a nanofiber-reinforced polyimide airgel material and its preparation method, which overcomes the weakness of low strength of the existing polyimide nanofiber airgel. Imide nanofibers into its gel, freeze-drying and thermal imidization techniques to prepare nanofiber-reinforced polyimide airgel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nanofiber reinforced polyimide airgel material and preparation method thereof
  • A kind of nanofiber reinforced polyimide airgel material and preparation method thereof
  • A kind of nanofiber reinforced polyimide airgel material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) Using N,N-dimethylacetamide as a solvent, the solid content is prepared by condensation polymerization of 4,4'-diaminodiphenyl ether and terephthalic anhydride in an ice-water bath in an equimolar ratio 15% polyamic acid. The specific process is as follows: Dissolve 8.0096g of 4,4'-diaminodiphenyl ether in 95.57g of N,N-dimethylacetamide, add 8.8556g of pyromellitic dianhydride, and react in an ice-water bath for 5h. Then, 4.0476 g of triethylamine was added, and the reaction was continued for 5 h to prepare a water-soluble polyamic acid solution with a solid content of 15%. The prepared water-soluble polyamic acid is precipitated with deionized water, and then washed and freeze-dried to obtain a water-soluble polyamic acid prepolymer for use.

[0032] (2) Using N,N-dimethylacetamide as a solvent, the solid content is prepared by condensation polymerization of 4,4'-diaminodiphenyl ether and terephthalic anhydride in an ice-water bath in an equimolar ratio It is 15...

Embodiment 2

[0035] The difference between this example and Example 1 is that the mass of the short polyimide nanofibers in Example 1 is changed to 0.25g. That is, take 50mL of deionized water, 2.5g of polyamic acid prepolymer, and 2.5g of triethylamine, mix them evenly, and obtain a polyamic acid hydrogel after 24 hours of sol-gel process. Then add 0.25g of short polyimide nanofibers to the hydrogel, mix well and then freeze-dry and thermally imidize the sample to obtain a fiber-reinforced polyimide airgel, which is named PI-10 .

Embodiment 3

[0037]The difference between this example and Example 1 is that the mass of the short polyimide nanofibers in Example 1 is changed to 0.5 g. That is, take 50mL of deionized water, 2.5g of polyamic acid prepolymer, and 2.5g of triethylamine, mix them evenly, and obtain a polyamic acid hydrogel after 24 hours of sol-gel process. Then add 0.5g of polyimide nano-short fibers to the hydrogel, mix well, freeze-dry and heat imidize the sample to obtain fiber-reinforced polyimide airgel, and name it PI-20 .

[0038] The stress-strain curves of nanofiber-reinforced polyimide airgel are as follows: figure 2 As shown, as the content of polyimide nano-short fibers increases, the maximum stress of the sample increases, and the curve does not shake significantly when the strain is 80%, indicating that it can still maintain structural integrity. The slope of the linear region in the curve also increases with the increase of the short fiber content, and the Young's modulus of the airgel in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a nanofiber-reinforced polyimide airgel material and a preparation method thereof. The raw materials include: water-soluble polyamic acid, polyimide nano-short fibers, triethylamine and water. The polyimide airgel prepared by the present invention has a low shrinkage rate, and its Young's modulus is improved under the condition that the density is basically unchanged, and its comprehensive performance is excellent. The scope of application of polyimide airgel.

Description

technical field [0001] The invention belongs to the field of airgel materials and preparation thereof, in particular to a nanofiber-reinforced polyimide airgel material and a preparation method thereof. Background technique [0002] Airgel refers to a gel material composed of microporous solids and the dispersed phase is gas. It has the characteristics of low density, high specific surface area, etc., and has broad application prospects in aerospace, petrochemical, automobile industry, building insulation and other fields. [0003] Due to the low density of the aerogel, it has a high porosity and a hierarchical porous structure, thus having an ultra-low density. Therefore, aerogels have great application prospects in many fields such as construction, automobiles, aerospace, household appliances, petrochemical plants, and outdoor sports. However, in practical applications, airgel should not only have low density, but also its strength should be further improved to expand it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J9/28C08L79/08
CPCC08J9/286C08J2205/026C08J2479/08C08J2201/0484C08J2379/08
Inventor 樊玮赵兴宇刘天西杨帆薛甜甜张翔
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com