A kind of ultra-high performance concrete applied in the alpine region and its preparation method

An ultra-high-performance concrete technology, which is applied in the field of building materials, can solve the problems of losing strength, restricting the application of ultra-high concrete, and destroying the microstructure of concrete, and achieves excellent mechanical properties, excellent resistance to chloride ion penetration, and high density. Effect

Active Publication Date: 2021-12-24
ANHUI CONCH DESIGN & RES INST OF BUILDING MATERIALS CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The crystallized water inside the concrete freezes and expands under low temperature conditions, destroying the microstructure of the concrete, causing it to lose its strength, and seriously affecting the service life of the concrete
The low-temperature alpine region restricts the application of ultra-high concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultra-high performance concrete applied in the alpine region and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A method for preparing ultra-high performance concrete applied in alpine regions, comprising the following steps:

[0046] 1) Weigh 200g of early-strength polycarboxylate superplasticizer, 50g of water-reducing polycarboxylate high-performance water-reducer, 50g of melamine-type water-reducer, 0.15g of defoamer and 199.85g of water, stir and mix well , as a water reducing agent, spare.

[0047] 2), the concrete mixing volume is 15L. Weigh Portland cement P.Ⅰ52.5 grade 9.75kg, high aluminate cement 52.5 grade 3.45kg, silica fume 0.75kg, nano silicon dioxide 0.15kg, sand 18.75kg, steel fiber 0.525kg, step 1) preparation Water reducer 0.42kg, sodium nitrite 0.075kg, sodium silicate 0.03kg and water 2.775kg, spare.

[0048] 3), add the Portland cement, high aluminate cement, silica fume, nano-silica, sand, sodium nitrite, and sodium silicate weighed in step 2) into the stirring pot and stir for 60 seconds, then stir while stirring Add the weighed steel fiber, the steel f...

Embodiment 2

[0052] A method for preparing ultra-high performance concrete applied in alpine regions, comprising the following steps:

[0053] 1) Weigh 210g of early-strength polycarboxylate superplasticizer, 140g of water-reducing polycarboxylate high-performance water-reducer, 105g of melamine-type water-reducer, 0.35g of defoamer and 244.65g of water, stir and mix , as a water reducing agent, spare.

[0054] 2), the concrete mixing volume is 15L. Weigh Portland cement P.Ⅱ52.5 grade 8.25kg, high aluminate cement 52.5 grade 5.1kg, silica fume 1.05kg, nano silicon dioxide 0.675kg, sand 16.5kg, steel fiber 1.18kg, step 1) preparation 0.6kg of superplasticizer, 0.135kg of sodium nitrite, 0.015kg of sodium silicate, 0.0075kg of sodium thiocyanate, and 2.85kg of water for spare use.

[0055] 3) Add the Portland cement, peraluminate cement, silica fume, nano-silica, sand, sodium nitrite, sodium silicate and sodium thiocyanate weighed in step 2) into the stirring pot and stir for 60s , and th...

Embodiment 3

[0059] A method for preparing ultra-high performance concrete applied in alpine regions, comprising the following steps:

[0060] 1) Weigh 80g of early-strength polycarboxylate superplasticizer, 140g of water-reducing polycarboxylate high-performance water-reducer, 20g of melamine-type water-reducer, 0.32g of defoamer and 159.68g of water, stir and mix , as a water reducer, spare;

[0061] 2), the concrete mixing volume is 15L. Weigh Portland cement P.Ⅱ52.5 grade 6.975kg, high aluminate cement 62.5 grade 6.525kg, silica fume 1.0kg, nano silicon dioxide 0.3kg, sand 17.25kg, steel fiber 2.355kg, step 1) preparation 0.375kg of superplasticizer, 0.045kg of sodium nitrate, 0.03kg of sodium thiocyanate, and 2.7kg of water are used for standby.

[0062] 3) Add the Portland cement, high aluminate cement, silica fume, nano-silica, sand, sodium nitrate and sodium thiocyanate weighed in step 2) into the stirring pot and stir for 60 seconds, then add while stirring Step 2) The steel fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention provides an ultra-high-performance concrete used in alpine regions and a preparation method thereof, comprising the following raw materials in parts by weight: 450-650 parts of Portland cement, 200-450 parts of peraluminate cement, and 50-100 parts of silica fume , 5-50 parts of nano-silica, 1000-1300 parts of sand, 35-200 parts of steel fiber, 20-45 parts of water reducing agent, 2-10 parts of antifreeze, 0.2-2.0 parts of early strength agent and 180-210 parts of water share. Compared with the prior art, the ultra-high-performance concrete prepared in the invention can be constructed in a cold region of -20°C and can quickly gain strength. Moreover, it has high compactness, excellent resistance to chloride ion penetration and excellent mechanical properties.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to an ultra-high-performance concrete applied in an alpine region and a preparation method thereof. Background technique [0002] Ultra-high performance concrete, referred to as UHPC (Ultra-High Performance Concrete), as a new type of cement-based structural material, has excellent properties such as ultra-high strength, high durability, and high toughness. Ultra-high performance concrete has achieved a great leap forward in engineering materials, and it is also the most innovative cement-based engineering material in the past three decades. [0003] However, there is no report on the use of ultra-high performance concrete in the cold region of -20°C. This is mainly because the hydration rate of concrete decreases rapidly under low temperature conditions, and the strength increases very slowly, or even stops growing. Under low temperature conditions, the crystalline wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/06C04B111/76
CPCC04B28/06C04B2111/76C04B7/02C04B18/146C04B14/062C04B14/06C04B14/48C04B2103/302C04B22/002C04B2103/50C04B22/085C04B12/04C04B14/068C04B22/14
Inventor 肖慧丽沈江平徐文祥谢发权熊磊陈钦松王一健恽进进叶书峰
Owner ANHUI CONCH DESIGN & RES INST OF BUILDING MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap