Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Filling method of gap between steel plates

A filling method and gap filling technology, applied in welding equipment, manufacturing tools, welding/cutting media/materials, etc., to achieve the effects of beautiful weld shape, improved filling quality, and increased strength

Active Publication Date: 2021-10-26
浙江高圣钢结构有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for gap filling between high-strength steel plates, the fatigue strength will not improve as long as the conventional gap filling technology between steel plates is used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Filling method of gap between steel plates
  • Filling method of gap between steel plates
  • Filling method of gap between steel plates

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A method for filling gaps between steel plates, comprising the following steps:

[0047] S1: Clean the gap between the steel plates to be filled. The steel plates are low-alloy high-strength steels. The composition is shown in Table 1, and the mechanical properties are shown in Table 2;

[0048] S2: Preheating the gap filling area at 70 °C;

[0049] S3: Use welding filler to weld and fill the gaps between the steel plates to form joints, and perform three-layer welding on the joints, each layer is welded three times, and the weld seam must be ground before the next layer is welded;

[0050] In this embodiment, the welding adopts semi-automatic mixed gas shielded welding, and the welding shielding gases are He, Ar and CO 2 Mixed gas shielding, He, Ar and CO 2 The volume ratio is 1:1.2:0.15, and the polarity of the power supply is reversed; the welding seam forming method is single-sided welding, double-sided forming, and the welding process parameters are shown in Tabl...

Embodiment 2

[0059] A method for filling gaps between steel plates, comprising the following steps:

[0060] S1: Clean the gap between the steel plates to be filled, the steel plate is the low-alloy high-strength steel used in Example 1;

[0061] S2: Preheating the gap filling area at 85 °C;

[0062] S3: Use welding filler to weld and fill the gap between the steel plates to form a joint, and perform 4-layer welding on the joint, with 4 welds for each layer, and the weld seam must be ground before the next welding;

[0063] In this embodiment, the welding adopts semi-automatic mixed gas shielded welding, and the welding shielding gases are He, Ar and CO 2 Mixed gas shielding, He, Ar and CO 2 The volume ratio is 1:1.2:0.15, and the polarity of the power supply is reversed; the welding seam forming method is single-sided welding, double-sided forming, and the welding process parameters are shown in Table 4.

[0064] The welding filler used in this embodiment includes 30% by weight of iron...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for filling gaps between steel plates, belonging to the technical field of metal materials, comprising the following steps: cleaning the gaps between steel plates to be filled; preheating the gap filling area at 150-250°C; using welding filler to weld and fill the gaps between steel plates to form joint; wherein, the joint strength matching is equal strength matching, and the welding filler includes 26-33% by weight of iron, 12-15% by weight of chromium, 0.15-0.18% by weight of carbon, 0.05-0.1% by weight of selenium, 2.1-2.7 % by weight of manganese, 0.8-1.2% by weight of silicon, 0.1-0.5% by weight of yttrium. The filling method of the present invention not only makes the strength of the obtained joint reach more than 98.3% of the strength of the steel plate, but also makes the structure of the weld seam of the joint mainly acicular ferrite with good strength and toughness, improves the toughness of the joint, and improves the filling quality of the gap between the steel plates .

Description

technical field [0001] The invention belongs to the technical field of metal materials, and in particular relates to a method for filling gaps between steel plates. Background technique [0002] With the continuous innovation of steel structure production technology and the rapid development of the construction industry, steel structures are widely used in housing construction, bridges and some large-span engineering projects due to their high strength, good toughness, and good seismic performance. And the use has played a significant effect, so it has won the strong support of the country, making my country a big country in the production and processing of steel structures, and the steel structure industry has also entered a stage of vigorous development. In the process of continuous research and development of steel structures, new steel materials and their production and processing technologies are constantly innovating. With the rapid development of urbanization, a large...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K9/16B23K35/30
CPCB23K9/16B23K35/308
Inventor 陈晓平盛长华
Owner 浙江高圣钢结构有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com