PE vacuum aluminized composite film and its preparation method

A technology of vacuum aluminum plating and composite film, applied in the field of packaging materials, to achieve the effects of simple preparation method, large-scale production and high comprehensive mechanical properties

Active Publication Date: 2021-08-31
ZHEJIANG BILI POLYMER TECH CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The polyethylene aluminized film provided by the invention application has the advantages of extremely high gloss, good metallic texture, and excellent physical and mechanical properties, but it still does not solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PE vacuum aluminized composite film and its preparation method
  • PE vacuum aluminized composite film and its preparation method
  • PE vacuum aluminized composite film and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] This embodiment provides a PE vacuum aluminized composite film, such as figure 1 As shown, it includes a PE composite base film 1 and an aluminum-coated film 2 connected to one side of the PE composite base film 1, and the PE composite base film 1 includes low-density polyethylene, 40 parts of low-density polyethylene, and 40 parts in mass parts respectively. Metallic polyethylene, 5 parts of surface adhesive resin, 15 parts of linear polyethylene, 3 parts of antioxidant, 3 parts of heat stabilizer, 3 parts of UV blocker and 3 parts of antiblocking agent.

[0038] Wherein, the surface adhesive resin comprises polyethylene adipate and a silane coupling agent, and the mass ratio of the polyethylene adipate to the silane coupling agent is 1:0.3; the low density polyethylene The melt flow rate is selected as 0.2g / 10min, and the density is 0.920g / cm 3 low-density polyethylene; the metallocene polyethylene is selected as a melt flow rate of 1.3g / 10min, a density of 0.940g / cm...

Embodiment 2

[0052] This embodiment provides a PE vacuum aluminized composite film, such as figure 1 As shown, it includes a PE composite base film 1 and an aluminized film 2 connected to one side of the PE composite base film 1, and the PE composite base film 1 includes low-density polyethylene, 30 parts of low-density polyethylene and 30 parts in mass parts respectively. Metallic polyethylene, 3 parts surface adhesive resin, 10 parts linear polyethylene, 1 part antioxidant, 1 part heat stabilizer, 1 part UV blocker and 1 part antiblocking agent.

[0053] Wherein, the surface adhesive resin comprises polyethylene adipate and a silane coupling agent, and the mass ratio of the polyethylene adipate to the silane coupling agent is 1:0.1; the low density polyethylene The melt flow rate is selected as 0.3g / 10min, and the density is 0.900g / cm 3 low-density polyethylene; the metallocene polyethylene is selected as a melt flow rate of 1.0g / 10min, a density of 0.920g / cm 3 The metallocene polyethy...

Embodiment 3

[0056] This embodiment provides a PE vacuum aluminized composite film, such as figure 1 As shown, including 35 parts by mass of low-density polyethylene, 35 parts of metallocene polyethylene, 4 parts of surface adhesive resin, 12 parts of linear polyethylene, 2 parts of antioxidant, 2 parts 2 parts of heat stabilizer, 2 parts of UV blocker and 2 parts of anti-blocking agent.

[0057] Wherein, the surface adhesive resin comprises polyethylene adipate and a silane coupling agent, and the mass ratio of the polyethylene adipate to the silane coupling agent is 1:0.2; the low density polyethylene The melt flow rate is selected to be 0.25g / 10min, and the density is 0.910g / cm 3 low-density polyethylene; the metallocene polyethylene is selected as a melt flow rate of 1.2g / 10min, a density of 0.930g / cm 3 The metallocene polyethylene; Antioxidant is PS-802 antioxidant; Thermal stabilizer can be selected commercially available products, such as organotin stabilizer; Ultraviolet blocking...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of packaging materials, and in particular relates to a PE vacuum aluminized composite film and a preparation method thereof. The present invention comprises a PE composite base film and an aluminized film connected to one side of the PE composite base film, and the PE composite base film includes low-density polyethylene, metallocene polyethylene, surface adhesive resin, linear polyethylene, anti- Oxygen, heat stabilizer, UV blocker and antiblocking agent. The PE composite base film provided by the present invention is added with surface adhesive resin, which greatly improves the adhesion of the PE composite base film to the aluminized film, and prevents the problem of the aluminized film from falling off, and the PE composite provided by the present invention An anti-blocking agent is added to the base film, so that the prepared packaging bag is not easy to block and has better opening property.

Description

technical field [0001] The invention belongs to the technical field of packaging materials, and in particular relates to a PE vacuum aluminized composite film and a preparation method thereof. Background technique [0002] With the continuous development of my country's economy, the demand for PE barrier composite films in the packaging industry is increasing day by day, and the scope of application is also expanding. Due to the poor oxygen and water vapor barrier ability of PE, and the excellent oxygen and water vapor barrier ability of aluminum foil, but the two Combination can only be combined, and the cutting performance of aluminum foil is poor, and the high cost is not conducive to promotion and application. PE vacuum aluminized composite film not only has very good oxygen and water vapor barrier ability, but also has good performance and low cost. It has good comprehensive performance in terms of mechanical properties and appearance novelty, and is easy to promote and u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/32B32B27/18B32B27/06B32B33/00B29C48/08B29C48/18B29C55/28B29C55/12B29C59/10C08J5/18C08L23/06C08L67/02C23C14/20
CPCB29C59/10B32B27/08B32B27/18B32B27/32B32B27/327B32B33/00B32B2250/242B29C48/0018B29C48/0022B29C48/08B29C48/18C08J5/18C08J2323/06C08J2423/06C08J2467/02C23C14/20
Inventor 李俊强
Owner ZHEJIANG BILI POLYMER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com