A kind of magnesium workpiece surface spray liquid and application thereof

A workpiece surface and spraying liquid technology, which is applied in the field of spraying liquid on the surface of magnesium workpieces to prepare durable superamphiphobic surfaces of magnesium workpieces, to achieve the effects of convenient operation, simple preparation process, and widening application fields

Active Publication Date: 2021-09-07
CHONGQING UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For the difficulties and problems existing in the prior art, the purpose of the present invention is to provide a kind of magnesium workpiece surface spraying liquid, and based on this spraying liquid is applied to the method for preparing the durable super-amphiphobic surface of magnesium workpiece

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of magnesium workpiece surface spray liquid and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The preparation of surface spraying liquid of pure magnesium workpiece (diameter 20mm, thick 5.0mm disc), concrete steps are as follows:

[0026] ① Take 500ml of concentrated phosphoric acid and dilute to 1L, then ultrasonically disperse 150g of aluminum hydroxide in it, and stir at 85°C for 4 hours to obtain solution A;

[0027] ② Add 10ml of nonanoic acid and 90ml of nonanol to 900ml of absolute ethanol, stir at room temperature for 2 hours to obtain solution B;

[0028] ③Take 400ml of solution A and 600ml of solution B, mix them, and stir at room temperature for 0.5 hours to obtain the surface spraying solution for magnesium workpieces.

[0029] Apply the above-mentioned spraying solution to prepare the durable super-amphiphobic surface of pure magnesium workpiece, the specific steps are as follows:

[0030] ① Spraying treatment: Spray the above-mentioned spraying liquid evenly on the surface of the clean pure magnesium workpiece, the ratio of the volume of the spra...

Embodiment 2

[0045] The preparation of surface spraying liquid on AZ31 magnesium alloy workpiece (1.0m×0.5m×3.0mm rectangular plate), the specific steps are as follows:

[0046] ① Take 750ml of concentrated phosphoric acid and dilute to 1L, then ultrasonically disperse 250g of aluminum hydroxide in it, and stir at 100°C for 5 hours to obtain solution A;

[0047] ② Add 30ml of nonanoic acid and 70ml of nonanol to 900ml of absolute ethanol, stir at room temperature for 1 hour to obtain solution B;

[0048] ③Take 400ml of solution A and 600ml of solution B, mix them, and stir at room temperature for 1.5 hours to obtain the surface spraying solution for magnesium workpieces.

[0049] Apply the above spraying solution to prepare the durable superamphiphobic surface of AZ31 magnesium alloy workpiece, the specific steps are as follows:

[0050] ① Spraying treatment: Spray the above-mentioned spraying liquid evenly on the surface of the clean AZ31 magnesium alloy workpiece. The ratio of the volum...

Embodiment 3

[0054] The preparation of surface spraying liquid of AZ61 magnesium alloy workpiece (square plate of 20cm * 20cm * 4.0mm), concrete steps are as follows:

[0055] ① Take 600ml of concentrated phosphoric acid and dilute to 1L, then ultrasonically disperse 200g of aluminum hydroxide in it, and stir at 90°C for 3 hours to obtain solution A;

[0056] ② Add 20ml of nonanoic acid and 80ml of nonanol to 900ml of absolute ethanol, stir at room temperature for 1.5 hours to obtain solution B;

[0057] ③Take 400ml of solution A and 600ml of solution B, mix them, and stir at room temperature for 1.0 hour to obtain the surface spraying solution for magnesium workpieces.

[0058] Apply the above spraying solution to prepare the durable superamphiphobic surface of AZ61 magnesium alloy workpiece, the specific steps are as follows:

[0059] ① Spraying treatment: Spray the above-mentioned spraying liquid evenly on the surface of the clean AZ61 magnesium alloy workpiece. The ratio of the volume...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a surface spraying liquid for a magnesium workpiece and a method for preparing a durable superamphiphobic surface of a magnesium workpiece by using the spraying liquid. The magnesium workpiece surface spraying liquid of the present invention does not contain fluorine, silicon, rubber, resin and various micro / nano fillers, and the components are environmentally friendly and do not cause compatibility problems; the spraying liquid is evenly sprayed onto the clean magnesium workpiece surface, and then The durable superamphiphobic surface of the magnesium workpiece can be obtained through proper curing treatment. The superamphiphobic surface of the magnesium workpiece prepared by the invention has good durability, and can withstand various severe tests such as friction and wear, ultraviolet radiation, high-pressure water column impact, strong acid and strong alkali, organic solvent immersion, strong corrosive medium immersion, etc., and is expected to greatly broaden the scope of magnesium materials. field of application. The method of the invention is applicable to the treatment of magnesium and its alloy workpieces of various sizes and shapes. The method of the invention has the characteristics of simple process, convenient operation, environmental protection, easy large-scale industrialized treatment and the like.

Description

technical field [0001] The invention belongs to the technical field of surface engineering, and in particular relates to a surface spraying liquid for magnesium workpieces and a method for preparing durable superamphiphobic surfaces of magnesium workpieces. Background technique [0002] Magnesium material has the advantages of high specific strength, specific stiffness, damping, machinability, thermal conductivity, strong electromagnetic shielding ability, etc., and is known as "the most promising green engineering material in the 21st century". with broadly application foreground. However, its chemical properties are very active, and the natural oxide film on its surface is loose and porous, and basically has no protective effect. Therefore, it is necessary to improve the durability of the magnesium alloy surface through appropriate surface treatment to promote its wide application. [0003] Due to its special wettability of both superhydrophobic and superoleophobic, compa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C22/20C23C22/76
CPCC23C22/20C23C22/76
Inventor 李凌杰雷惊雷李霞尹伟何建新潘复生
Owner CHONGQING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com