Platinum-carbon catalyst and preparation method and application thereof

A technology of platinum-carbon catalyst and carbon powder, which is applied in the direction of electrical components, battery electrodes, circuits, etc., can solve the problems of platinum falling off and not solving the problem of reverse pole, and achieve the problem of solving the problem of reverse pole, improving the carrier shedding rate, and consistent batches good sex effect

Active Publication Date: 2020-05-12
FAW JIEFANG AUTOMOTIVE CO
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the invention did not solve the reverse polarity problem
[0006] Based on the research of the above literature, how to develop a catalyst that can not only solve the problem of platinum falling off from the carrier, but also improve the water flooding resistance of the catalyst, and at the same time solve the problem of reverse pole, has become an urgent problem to be solved at present.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Platinum-carbon catalyst and preparation method and application thereof
  • Platinum-carbon catalyst and preparation method and application thereof
  • Platinum-carbon catalyst and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] The present embodiment provides a kind of preparation method of platinum carbon catalyst, comprises the following steps:

[0064] (1) 5g of graphene is placed in 100mL of nitric acid solution with a mass fraction of 40%, reflux at 60°C, magnetically stirred for 4h, the sample is suction filtered, washed until the pH is 4, and vacuum-dried at 80°C to obtain toner;

[0065] (2) Put the carbon powder in 100ml of 30% hydrogen peroxide solution by mass fraction, stir for 2 hours, perform suction filtration, wash until neutral, and dry in vacuum at 100°C to obtain the carbon carrier;

[0066] (3) Take 0.2 g of the carbon carrier obtained in step (2) and place it in 50 mL of chloroplatinic acid solution containing platinum at a concentration of 0.006 g / mL. After ultrasonication for 5 min, add 8 g of isopropanol for emulsification and shearing for 5 min, and add 1.23 g 50ml of 0.1mg / ml sodium formate solution of ascorbic acid, 20g of 0.05wt% graphene dispersion of 0.1wt% ammon...

Embodiment 2

[0074] The present embodiment provides a kind of preparation method of platinum carbon catalyst, comprises the following steps:

[0075] (1) Place 5 g of carbon nanospheres in 100 mL of nitric acid solution with a mass fraction of 56%, reflux at 80 ° C, and magnetically stir for 6 h, filter the sample, wash it to pH 6, and dry it at 60 ° C to obtain toner;

[0076] (2) Put the carbon powder in 134ml of 30% hydrogen peroxide solution and stir for 4h, perform suction filtration, wash to neutrality, and dry at 100°C to obtain the carbon carrier;

[0077](3) Take 0.2 g of the carbon carrier obtained in step (2) and place it in 25 mL of chloroplatinic acid solution containing platinum at a concentration of 0.006 g / mL. After ultrasonication for 10 min, add 14.8 g of n-butanol for emulsification and shearing for 10 min. Add 0.38 20ml of 0.1mg / ml sodium formate solution of g ascorbic acid, 20g of 0.01wt% graphene dispersion of 0.3%wt ammonium carbamate, under the protection of helium...

Embodiment 3

[0079] The present embodiment provides a kind of preparation method of platinum carbon catalyst, comprises the following steps:

[0080] (1) Put 5g of Vulcan XC-72 in 80mL of nitric acid solution with a mass fraction of 42%, reflux at 80°C and magnetically stir for 4h, filter the sample, wash to pH 6, and dry at 70°C. get toner;

[0081] (2) Put the carbon powder in 120ml of 30% hydrogen peroxide solution and stir for 4 hours, perform suction filtration, wash to neutrality, and dry at 100°C to obtain the carbon carrier;

[0082] (3) Take 0.2 g of the carbon support obtained in step (2) and place it in 25 mL of platinum nitrate solution with a platinum concentration of 0.006 g / mL. After ultrasonication for 10 min, add a mixture of 8 g of n-butanol and 6 g of isopropanol to carry out Emulsified and sheared for 8min, added 30ml of 0.1mg / ml sodium formate solution of 1.05g ascorbic acid, 20ml of 0.05wt% graphene dispersion of 0.2wt% ammonium carbamate, under argon protection, ref...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a platinum-carbon catalyst and a preparation method and application thereof. The preparation method provided by the invention comprises the following steps: (1) mixing a carbon material and a nitric acid solution, refluxing, separating and drying the mixed solution to obtain carbon powder; (2) mixing the carbon powder with a hydrogen peroxide solution, performing separating and drying to obtain a carbon carrier; and (3) mixing the carbon carrier, a platinum-containing solution and a reducing agent, performing refluxing under the protection of an inert atmosphere, adding an antipole inhibitor, performing emulsifying, carrying out microwave treatment, separating and drying to obtain the platinum-carbon catalyst. According to the method, nitric acid-hydrogen peroxidedouble oxidation is adopted, rich oxygen-containing functional groups are formed on the surface of the carbon carrier and combined with Pt through coordination bonds, and the problems that Pt is poorin dispersity, low in utilization rate, prone to falling off and the like are solved; the catalyst provided by the invention has the characteristics of high ORR activity, strong anti-reversion capability, reduced performance degradation and the like, and the battery prepared from the catalyst has excellent anti-reversion capability and the high open-circuit voltage.

Description

technical field [0001] The invention relates to the technical field of new energy fuel cells, in particular to a platinum-carbon catalyst and its preparation method and application. Background technique [0002] A fuel cell is a device that directly converts chemical energy stored in fuel and oxidant into electrical energy, because it has a wide range of fuel sources, is clean, environmentally friendly, is not limited by the Carnot cycle, has high energy conversion efficiency, and has strong modular structure flexibility. , Centralized power supply can also be decentralized power supply and other advantages, in line with the requirements of sustainable development of the environment and resources, so it is highly valued. Fuel cells have broad application prospects in the fields of power stations, electric vehicles, aerospace, submarines, and space power supplies. Among them, proton exchange membrane fuel cells (PEMFC) have become a key research object in the field of new ene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/88H01M4/92
CPCH01M4/8878H01M4/926Y02E60/50
Inventor 于力娜朱雅男裴国权张克金唐柳杨帅
Owner FAW JIEFANG AUTOMOTIVE CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap